Poly(methyl methacrylate) (PMMA) surfaces have been modified by dynamic plowing lithography. The resulting modified structures, presenting regions of different densities and stiffnesses, have been studied by forcedisplacement curves. The elasto-plastic response, the stiffness, and the adhesion of the modified samples have been characterized. Forcedisplacement curves are able to distinguish between unmodified PMMA and two different structures resulting from the lithography, i.e. compressed PMMA and low density PMMA. In particular, the low density regions are made up of cluster-like globular particles, whose elasto-plastic response and adhesion are measured and whose contribution to the total elasto-plastic response and to the adhesion has been studied in detail.
Stiffness variation in the interphase of amine-cured epoxy adjacent to copper microstructures
(2007)
In an effort to expand the understanding of the mechanical properties of the polymeric interphase on a metal surface, a composite consisting of epoxy and copper was prepared and analyzed. Scanning force microscopy-based force modulation microscopy (SFM-FMM) was employed along with dynamic mechanical analysis (DMA) and energy dispersive X-ray analysis (EDX). Diglycidyl ether of bisphenol A (DGEBA)-based epoxy resins were applied with amine curing agents. The samples were made taking advantage of electron beam lithography (EBL) in order to produce sharp edges of copper structures and a flat surface suitable for the SFM-FMM analysis, which was able to depict the stiffness within the interphase. It is considered significant information because the mechanical characteristic within the narrow interphase was revealed. Comparing with DMA and EDX, the stiffness information of SFM-FMM demonstrated a matching correlation and agreement in terms of preferential adsorption of the curing agent in the vicinity of the interface. The stiffness profiles of the two epoxy systems turned out to be different, and it shows the material dependence of the interphase characteristics.
Laser ablation of single-crystalline indium phosphide (InP) was performed in air by means of linearly polarized Ti:sapphire femtosecond-pulses (800 nm, 130 fs, 10 Hz). As a result of the first laser pulses, several morphological changes (crater formation, rim formation, ripple structures and cones) were observed. These effects were explored using force modulation microscopy (FMM), a technique based on scanning force microscopy (SFM), allowing the simultaneous imaging of both topography and local stiffness at a high lateral resolution. The first laser pulse induces the formation of a protruding rim (height <20 nm, width ~300 nm) bordering the ablated crater. A Fourier-analysis of the multi-pulse generated topographies reveals the formation of wavelength-sized periodic ripples (modulation depth <100 nm) with an orientation perpendicular to that of the electric field vector of the laser radiation. Besides these morphological alterations, also material modifications were observed in the irradiated regions by means of the FFM technique. Within the ablated craters, local stiffness variations were found revealing an inhomogeneous material composition/structure as a consequence of the femtosecond pulse laser treatment.