After a delamination process in a C-fiber reinforced polymer composite, the identification of the polymer residue of poly-(phenylene sulphide) on carbon fiber surfaces gives important information on the composite failure mechanism. Using scanning force microscopy (SFM) in its lateral force imaging mode or with the stiffness imaging mode, it is almost impossible to distinguish the two composite components owing to a very low material-based contrast of the local friction and compliance. The new technique using contrast based on a local AC current measurement allows a clear identification of the conducting carbon fiber and the non-conducting polymer coverage.
Two different approaches to investigate the local complex conductivity and the surface charge with Scanning Force Microscopy (SFM) techniques are presented. It is shown that the measurement of local electrical properties with SFM leads to interesting information about the composition of electrically heterogeneous surfaces
With an extended contact and non-contact mode scanning force microscope samples with different heterogeneous electrical properties can be characterized. The contact mode method allows the determination of local electric conductivities of heterogeneous systems at the sample surfaces. An interpretation of this behaviour can be obtained in combination with other SFM modes such as topography, friction and compliance used simultaneously. The non-contact mode SFM allows to get more information about the local surface charge of heterogeneous samples. In this paper two new SFM approaches will be discussed on examples of carbon-fibre reinforced, organic and ceramic materials
Scanning force microscopy (SFM) has been used to assess the local mechanical properties of fibre-reinforced polymers. Using a sinusoidal displacement modulation (DM) and lock-in technique the method allows to characterize local viscoelastic properties with a high lateral resolution. The simultaneous measurement of the local electrical conductivity is proposed which facilitates the interpretation of the mechanical data. The investigation of cross-sections perpendicular to the axis of carbon fibres embedded in PPS delivers some information about the change in local stiffness within the interfacial region. As a first approach, assuming a single-exponential decrease in local stiffness along a radial line from fibre to polymer we find characteristic decay lengths which are distributed in a range between 20 and 80nm. Further, a modified DM-mode is proposed which is expected to provide a contrast enhancement of the signal which is related to local stiffness. This can be achieved by installing an additional feedback loop which keeps constant the amplitude of dynamic indentation (CDI-mode).
Applying a high-frequency lateral vibration between tip and sample in a scanning force microscope (SFM), a harmonically modulated lateral (friction) force image can be obtained using lock-in techniques. Harmonically modulated lateral force microscopy (HM-LFM) offers several advantages compared with standard lateral force microscopy (LFM). After a brief investigation of the scan velocity dependence of LFM and HM-LFM, two samples were investigated. First, the surface of a poly(acrylonitrile-co-styrene)/polybutadiene blend (ABS) was used to demonstrate the ability of the new technique to decrease the stick effects of the SFM tip. Second, an interface between two chemically very similar polymers was prepared by melting polypropylene (PP) and poly(propene-block-ethene) (PP-block-PE) films on each other. After cutting, the surface roughness of this sample was very high. It is shown that only HM-LFM clearly resolves the local micromechanical properties without artefacts.
The physical properties as well as the thickness of the interphase between polymer and reinforcing phase are generally expected to show a strong influence on the macroscopic mechanical properties of composite materials. In this study the scanning force microscope (SFM) has been applied for detecting stiffness gradients near the interface between copper and epoxide. In displacement modulation mode the load exerted by the tip is modulated sinusoidally by vibrating the normal position of the cantilever or the sample. The corresponding amplitude of dynamic cantilever bending is related to local surface stiffness. Thus, using the SFM, the local mechanical properties of the surface under investigation can be probed. When scanning the tip across the reinforcement/polymer interface, the polymeric interphasial zone can be identified with the observed stiffness gradient. For a commercial epoxide based on diglycidyl ether of bisphenol A (DGEBA) cured with an amine-containing hardener, a stiffness gradient was detected that could be fitted by a Gaussian profile typical for diffusional processes. The width of the stiffness gradient was 280 nm. The observation is discussed in terms of interface-induced segregation processes between resin and hardener, as well as heat conduction mechanisms that can occur during the exothermic curing reaction. Both mechanisms are diffusional in nature and, via the local network structure, are expected to show some influence on the local stiffness of the cured epoxy. Copyright © 2000 John Wiley & Sons, Ltd.