Filtern
Dokumenttyp
- Zeitschriftenartikel (27)
- Vortrag (22)
- Beitrag zu einem Tagungsband (13)
- Posterpräsentation (4)
- Sonstiges (2)
- Beitrag zu einem Sammelband (1)
- Forschungsbericht (1)
Schlagworte
- Material moisture (17)
- Non-destructive testing (11)
- Air-coupled ultrasound (10)
- Building materials (9)
- Embedded sensors (8)
- Fluidics (6)
- Beton (5)
- Concrete (5)
- Moisture transport (5)
- Physisorption (5)
Organisationseinheit der BAM
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (70) (entfernen)
Eingeladener Vortrag
- nein (22)
Hydration is the exothermic reaction between anhydrous cement and water, which forms the solid cement matrix of concrete. Being able to evaluate the hydration is of high interest for the use of both conventional and more climate-friendly building materials. The experimental monitoring is based on temperature or moisture measurements. The first needs adiabatic conditions, which can only be achieved in laboratory. The latter is often measured comparing the weight of the material sample before and after oven drying, which is time-consuming. This study investigates the moisture content of two cement-based and two calcium sulphate based mixtures for the first 90 days by using the calcium carbide method and oven drying at 40 °C and 105 °C (Darr method). Thereby, the amount of chemically bound water is determined to derive the degree of hydration. The calcium carbide measurements highly coincide with oven drying at 40 °C. The calcium carbide method is therefore evaluated as a suitable alternative to the time-consuming Darr drying. The prompt results are seen as a remarkable advantage and can be obtained easily in laboratory as well as in the field.
Amorphous, porous materials represent by far the largest proportion of natural and men-made materials. Their pore networks consists of a wide range of pore sizes, including mesoand macropores. Within such a pore network, material moisture plays a crucial role in almost all transport processes. In the hygroscopic range, the pores are partially saturated and liquid water is only located at the pore fringe due to physisorption. Therefore, material parameters such as porosity or median pore diameter are inadequate to predict material moisture and moisture transport. To quantify the spatial distribution of material moisture, Hillerborg’s adsorption Theory is used to predict the water layer thickness for different pore geometries. This is done for all pore sizes, including those in the lower nanometre range. Based on this approach, it is shown that the material moisture is almost completely located in mesopores, although the pore network is highly dominated by macropores. Thus, mesopores are mainly responsible for the moisture storage capacity, while macropores determine the moisture transport capacity, of an amorphous material. Finally, an electrical analogical circuit is used as a model to predict the diffusion coefficient based on the pore-size distribution, including physisorption.
We present a preliminary investigation on distributed humidity monitoring during the drying process of concrete based on an embedded polymer optical fiber (POF). The water dissipated into the POF changes several properties of the fiber such as refractive index, scattering coefficient and attenuation factor, which eventually alters the Rayleigh backscattered light. The optical time Domain reflectometer (OTDR) technique is performed to acquire the backscattered signal at the wavelengths 650 nm and 500 nm, respectively. Experimental results show that the received signal increases at 650 nm while the fiber attenuation factor clearly increases at 500 nm, as the concrete dries out. In the hygroscopic range, the information retrieved from the signal change at 650 nm agrees well with the measurement result of the electrical humidity sensors also embedded in the concrete sample.
Air-coupled ultrasonic (ACU) testing has proven to be a valuable method for increasing the speed in non-destructive ultrasonic testing and the investigation of sensitive specimens. A major obstacle to implementing ACU methods is the significant signal power loss at the air–specimen and transducer–air interfaces. The loss between transducer and air can be eliminated by using recently developed fluidic transducers. These transducers use pressurized air and a natural flow instability to generate high sound power signals. Due to this self-excited flow instability, the individual pulses are dissimilar in length, amplitude, and phase. These amplitude and angle modulated pulses offer the great opportunity to further increase the signal-to-noise ratio with pulse compression methods.
In practice, multi-input multi-output (MIMO) setups reduce the time required to scan the specimen surface, but demand high pulse discriminability. By applying envelope removal techniques to the individual pulses, the pulse discriminability is increased allowing only the remaining phase information to be targeted for analysis. Finally, semi-synthetic experiments are presented to verify the applicability of the envelope removal method and highlight the suitability of the fluidic transducer for MIMO setups.
The development of prevention methods and the detection of moisture related damages in buildings and transport infrastructure at an early stage are current issues in the field of non-destructive testing in civil engineering.
Especially the subject of partial saturation requires further research since it is more likely to occur than full saturation of the material. In fact, partial saturation in porous media is even more complicated because both fully and partly saturated pores (i.e. pores in which the surfaces are covered with thin water layers) are present.
As the non-destructive method nuclear magnetic resonance (NMR) enables the measurement and quantification of relative low moisture contents, it is suitable for the investigation of partly saturated porous building materials. Nevertheless, the differentiation between partly and fully saturated pores is still a challenge. Therefore, in this study, we investigate two sandstones types (Bozanov and Schönbrunner sandstone) at various defined saturation states by using NMR. Furthermore, we measure the relative humidities within the samples and compute the water layer thicknesses (WLT) along the pore walls of all pore sizes to calculate the corresponding degree of pore saturation. To finally assign the NMR signals to pore sizes and to differentiate between partly and fully saturated pores, the water content distribution obtained from the WLT calculation is used for calibration of the relaxation-time distribution. In this extended abstract, selected results only for Schönbrunner sandstone are presented.
The effective gas diffusion coefficient describes the process of gas diffusion in porous materials. Several materials have a significant number of micropores in the lower nanometre range leading to a reduction of gas diffusion (Knudsen effect). In the case of partial pore saturation during adsorption, the available pore space is further reduced, as is the gas diffusion. In this study, the influence of partially saturated pores on the Knudsen effect and on the gas diffusion is quantified. Three different pore geometries are investigated (slit, cylindrical and spherical pores) and three different types of pore size distribution, including a broad equal distribution, three narrow normal distributions and two measured distributions of concrete.
Besides the intensive computation of the exact pore saturation, a simplified model with low computational requirements is suggested. This study shows that the influence of the water layer thickness on the effective diffusion becomes significant for pore radii below 50 nm and the assumed pore geometry is important. At the end, the overall effect is quantified for an amorphous material with most pore
radii below 30 nm. At a moisture level of 50% relative humidity, the effective diffusion is reduced by 35% due to partial saturation.
Several countries, which use or used nuclear power, started to destruct nuclear power plants. Thus, large amounts of radioactive waste have to be stored safely during the next decades. Large underground caverns will
be used a nuclear waste disposal. Once the cavern is full, a sealing construction is required. The sealing should avoid the contact to any fluids or substances of the storage barrels and reduce hazardous radiation.
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
High-Amplitude Surge of a Pitching Airfoil: Complementary Wind- and Water-Tunnel Measurements
(2018)
RECENT interest in gust response, rotorcraft forward flight and wind energy, among other applications, has focused on streamwise oscillations of nominally two-dimensional airfoils in attached and separated flows. The airfoil may be simultaneously held at constant incidence or execute some maneuver, such as pitch.
The relative freestream is spatially uniform but temporally unsteady, and this can be accomplished in a ground-test facility in two ways. The first method is to vary the output of the prime mover, such as the rotational speed of the impeller or the blower driving a wind tunnel, or (alternatively) to vary the pressure drop in the tunnel, thereby varying the flow speed in the test section, despite nominally constant primemover revolutions per minute. The second method is used to keep the tunnel’s operating speed constant, as well as to move the test article in the streamwise direction, fore and aft (for example, via an electric linear motor), such that the relative freestream speed felt by the test article varies according to some waveform. Typically, the latter approach is chosen in water tunnels, where there is too much tunnel-circuit inertia to vary the flow speed directly but where the usually low tunnel test section flow speeds enable large excursions in the relative freestream by oscillation of the test article. In fact, outright reverse flow is possible by moving the test article in the laboratory frame at a higher speed than the water-tunnel flow speed. In either case, a sinusoidal relative-speed waveform is the most intuitively realizable, and this can be combined with similar oscillations in the airfoil incidence angle or other kinematics. Although the two methods of realizing streamwise oscillations are mechanically distinct, experimental comparisons between an oscillating test article in a water tunnel and a stationary test article in a wind tunnel with a louvermechanismhave demonstrated agreement in themeasured lift and drag histories. Such experimentswere performed by Granlund et al. for a 10% freestream amplitude oscillation and fixed airfoil incidence, comparing a free-surface water tunnel and a closed-circuit wind tunnel. After buoyancy was subtracted from the wind-tunnel data (resulting from the louver pressure drop) and the model inertia subtracted from the water-tunnel data (resulting from acceleration of the test article), the remaining lift and drag histories matched well at the low freestream oscillation amplitude regime. The work of Granlund et al. was later extended to high-advance-ratio streamwise oscillations of 50% amplitude by Greenblatt et al., where the aerodynamic histories of the water-tunnel and wind-tunnel facilities were compared in combined pitch and freestreamoscillations (governed by relative pitch phase), pure pitch oscillations, and purely freestream oscillations. Agreement between the two facilities’ data for fixed-incidence streamwise oscillations was reasonably good, and in fact, better than agreement in just the static lift and drag, evidently owing to differences in blockage and model-support systems. Additionally, Greenblatt et al. determined there was no strong coupling between simultaneous freestream oscillations and pitch oscillations on resultant lift and moment coefficients.
Monitoring of the absolute water content in porous materials based on embedded humidity sensors
(2018)
Moisture transport monitoring may indicate the onset of deterioration in porous building materials Prior to damage occurring. Most moisture measurement systems provide only qualitative values, require extensive calibration, or are destructive. Thus, non-destructive and calibration-free monitoring Systems are required. Our approach of moisture monitoring is to embed sensors that measure the relative humidity.
In our experiment, screed samples are monitored during the Hydration and evaporation process. Every test sample is equipped with 10 embedded sensors which measure the relative humidity across the sample thickness. Based on Hillerborg’s approach, the relative humidity is converted into the corresponding pore saturation. In our study, the free water is computed without knowledge of the Sorption isotherm. The free water in the pore system is predicted and validated. The predicted weight decrease corresponds conclusively to gravimetrically measured weights. The embedded sensors yield the absolute liquid water content and enable an experimental, non-destructive monitoring of liquid water in porous materials.
Moisture testing and mapping
(2018)
Feuchtemessverfahren
(2018)
Experiments indicate that vortices trailing finite wings can be perturbed by periodic wing pitching, leading to rapid dissipation and bursting. To illustrate the perturbation mechanism, Betz vortex rollup relations are combined with the Theodorsen theory for unsteady lift response. A sinusoidal pitch motion on a rigid elliptic planform wing is computed in this study as one example. Pitching modifies the instantaneous lift due to the planform variations, via the reduced frequency, and the rollup relations are applied to low-frequency experimental conditions. The combined Betz–Theodorsen theory shows that relatively large spanwise perturbations of the vortex centers can be achieved and may accelerate the exponential growth associated with the Crow instability. In fact, 84.2% of the displacement of the
unsteady trailing vortices due to unsteady pitching is oriented in the direction of the Crow instability. Furthermore, the axial velocity in the vortex center, calculated based on the Batchelor method, varies on the order of the flight speed.
This forms two types of stagnation points produced by approaching and retreating axial core velocities; in the former case, conservation of mass leads to observations of “bursting.” This observation can be explained adequately on the basis of quasi-steady considerations.
Four cement-based and four calcium-sulphate-based screed types are investigated. The samples have a diameter of 300 mm and a height of 35 or 70 mm. Up to ten humidity sensors are embedded directly during the concreting of the screed samples. Thus, the humidity over the sample height is monitored during hardening, hydration, evaporation, and oven drying. Furthermore, the screed samples are weighted during every measurement to determine the total mass and the corresponding moisture loss.
To define the pore system precisely, mercury intrusion porosimetry as well as gas adsorption is performed. According to the data, the entire pore volume distribution is known. The measured pore diameters range from 0.8 nm to 100 μm and the total porosity of the examined screeds ranges between 11 % and 22 %.
Based on these measurement data, moisture transport, pore saturation as well as sorption isotherms and their hysteresis may be calculated quantitatively as described by Strangfeld et al.
Ultraschallmessverfahren werden seit Langem erfolgreich für Prüfaufgaben im Bauwesen eingesetzt. Die dauerhafte Überwachung und frühzeitige Erkennung von Schäden an komplexen Neubauten und alternder Infrastruktur kann mittels Ultraschall-Transmissionsmessungen und speziellen Auswertemethoden, wie z. B. Korrelationverfahren und Codawelleninterferometrie, realisiert werden. Für die Dauerüberwachung wurde ein kompaktes System entwickelt, das Ultraschall-Messdaten erfassen und ins Internet auf einen FTP-Server übertragen kann. Es können hierbei alle angeschlossenen Prüfköpfe für jede Messung wahlweise als Sender oder Empfänger geschaltet werden. Es wurden Vorverstärker entwickelt, bei denen die Versorgung mit Strom über die Messleitung erfolgt. Dadurch können die Verstärker nahe am Prüfkopf positioniert werden. Durch Änderungen in den Ultraschall-Signalen können Schädigungen des Bauteils, wie z.B. Risse, in Echtzeit erkannt werden.
The composition of concrete determines its resistance to various degradation mechanisms such as ingress of ions, carbonation or reinforcement corrosion. Knowledge of the composition of the hardened concrete is therefore helpful to assess the remaining service life of an existing structure or evaluate the damage observed during inspections. For example, for most existing concrete structures the type of cement originally used is not known and must therefore be determined afterwards. This paper presents a preliminary study on the application of laser-induced breakdown spectroscopy (LIBS) to identify the type of cement. For this purpose, ten different types of cement were investigated. For every type, three cement paste prisms were produced: (i) prisms dried, ground and pressed into tablets, (ii) prisms dried and (iii) prisms untreated. LIBS measurements were performed with a diode-pumped low energy laser (1064 nm, 3 mJ, 1.5 ns, 100 Hz) in combination with two compact spectrometers which cover the UV and NIR spectral range. A reduced subset of spectral features was used to build a classification model based on linear discriminant analysis. The results show that the classification of homogenized pressed cement powder samples provides a high accuracy, however, factors such as a different sample matrix and moisture content can affect the accuracy of the classification. The study demonstrates that LIBS is a promising tool to identify the type of cement.
Reinforced concrete and several other building materials deteriorate during their service life. Almost all deterioration processes are related to moisture. For understanding those processes, knowing the exact amount of the moisture content and the moisture transport characteristics is crucial. In fact, the moisture transport in porous materials is a two-phase flow; consisting of the vapour and the liquid phase. The two corresponding parameters are the diffusion coefficient and the hydraulic conductivity. By means of an inverse approach, these two coefficients are experimentally determined. The moisture transport of eight different screed types during hydration and evaporation is monitored based on embedded humidity sensors. The measured humidity profiles are converted into a pore saturation by adapting the approach of Hillerborg to the measured pore volume distribution. The summation of all pore saturations yields the total moisture content including the ink-bottle effect during desorption. The pore volume distribution was determined by mercury intrusion porosimetry as well as by gas adsorption. The measurement of the humidity and the pore saturation in the entire sample enables to invert the mass balance in order to extract the diffusion coefficient and the hydraulic conductivity. The determined diffusion coefficients of the eight investigated screeds are between m2s-1 and m2s-1.
Dynamic stall often occurs under conditions of simultaneous unsteady pitching and surging (e.g., rotorcraft and wind turbines), butmanymodels employ a dimensionless time base that implicitly assumes that surging is superimposed, in a quasi-steady manner, on dynamic pitching. An unsteady wind tunnel was used to examine this assumption, where a technique was developed to quantify the unsteady effects of surging on a pitching NACA 0018 airfoil. The technique involved performing multiple harmonic pitching experiments under nominally steady freestream conditions that bracketed a corresponding 50% surging amplitude (1.25 ⋅ 105 ≤ Re ≤ 3.75 ⋅ 105). By interpolating these data, unsteady-pitching/quasi-steady-surging data sets were constructed and compared with de facto synchronous pitch and surging experiments, thereby isolating the unsteady effects of surging on a pitching airfoil. Both large and small poststall maximum angles of attack (αs + 5° and αs + 15°) were considered at multiple pitch-surge phase differences. During deep dynamic stall (αs 15°), with large-scale separation, surging was seen to have a secondary effect on the unsteady aerodynamics. However, at small poststall maximum angles of attack (αs + 5°), either light or deep dynamic stall behavior was observed depending upon the pitch-surge phase difference. This was attributed to Reynolds number history effects, exemplified by boundary-layer transition, and thus it can be referred to as “transitional” dynamic stall.
The moisture content of the subfloor has to be determined before installation to avoid damages of the floor covering. Only if the readiness for layering is reached, an installation without damages can be expected in all cases. In general, three different approaches exist to measure the residual water content: determination of the moisture content, determination of the water release, or determination of the corresponding relative humidity. All three approaches are tested in laboratory at eight different screed types including two different samples thicknesses in each case. The moisture content and the water release are measured by sample weighing, the corresponding relative humidity is measured by embedded sensors. All three approaches are compared and correlated to each other. The evaluations show only weak correlation and, in several cases, contradicting results. Samples are considered as being ready for layering and not-being ready for layering at the same time, depending on the chosen approach. Due to these contradicting results, a general threshold for the risk of damage cannot be derived based on these measurements. Furthermore, the experiment demonstrates that the measurement of corresponding relative humidity is independent of the considered screed type or screed composition. This makes the humidity measurement to very promising approach for the installation of material moisture monitoring systems in the future.
Increasing traffic volume on the one hand and ageing infrastructure on the other hand have created many new challenges for maintenance and structural health monitoring of roads and bridges. In the past, many bridges and road structures have been neglected, often resulting in traffic congestion, road closure, and increased repair costs.
This research is concerned with the development of a system to improve the challenge of maintenance and early detection of damage, particularly moisture penetration and corrosion of steel reinforced concrete components. The objective is to develop a method that will also work after 30 years and longer. Many new IoT solutions are equipped with internal energy storage elements (accumulators or batteries) which are inappropriate here, since most relevant signs of concrete degradation occur after decades, where the functioning of such elements are more than questionable. The presented technology approach uses radio-frequency identification (RFID) and enables connectivity to sensors. It offers the advantage of an passive, completely independent energy supply without any energy storage components.
Since the system should be permanently embedded in concrete, it is crucial to develop a long-term stable device which is adapted to the environmental influences of the structure, e.g., long-term resistance in very alkaline environment of pH 13. In numerous experiments, the robustness of the system was tested and evaluated. Various tests with encapsulations to protect the electronics were performed, and for long-term validation different concrete specimens were instrumented with RFID-sensor-systems. Their operating time is now around two years and investigations for signs of fatigue and damage to the encapsulation and the electronics are ongoing.
The moisture content of screed samples is monitored by means of embedded sensors. Relative humidity sensors and multi-ring-electrodes are used to measure the spatial moisture distribution during desorption. Based on the humidity data and the pore volume distribution, the moisture and the water layer thickness within the pore space are predicted.
Slit shape as well as cylindrical pores are evaluated. Finally, the measured real part of the electrical impedance and the calculated water layer thickness are correlated. Based on the available data, a significant trend change of the impedance is documented at a water layer thickness of approximately 3 nm. This water layer thickness corresponds to a relative humidity of 88.3%.
In civil engineering, many structures are made of reinforced concrete. Most Degradation processes relevant to this material, e.g., corrosion, are related to an increased level of material moisture.
Therefore, moisture monitoring in reinforced concrete is regarded as a crucial method for structural health monitoring. In this study, passive radio frequency identification (RFID)-based sensors are embedded into the concrete. They are well suited for long-term operation over decades and are well protected against harsh environmental conditions. The energy supply and the data transfer of the humidity sensors are provided by RFID. The sensor casing materials are optimised to withstand the high alkaline environment in concrete, having pH values of more than 12. Membrane materials are also investigated to identify materials capable of enabling water vapour transport from the porous cement matrix to the embedded humidity sensor. By measuring the corresponding relative humidity with embedded passive RFID-based sensors, the cement hydration is monitored for 170 days.
Moreover, long-term moisture monitoring is performed for more than 1000 days. The Experiments show that embedded passive RFID-based sensors are highly suitable for long-term structural health monitoring in civil engineering.
In this communication a novel concept for pH sensing is introduced which is specifically adapted to monitor carbonation induced corrosion in concrete structures. The method is based on a ratiometric measurement principle, exploiting the pH sensitive colour switching of thymol blue in the basic pH regime and the emissive properties of two different (Zn)CdSe/ZnS core shell quantum dots. The transition point of thymol blue in a Hydrogel D4 matrix was determined to be at around pH 11.6, which fits ideally to the intended application. Next to the fundamental spectroscopic characterization of the ratiometric response, a new design for a sensor head, suitable for the incorporation into concrete matrices is presented. Toward this, a manufacturing process was developed which includes the preparation of a double layer of polymers containing either thymol blue or a quantum dot mixture inside a porous ceramic tube. Results of a proof-of-priciple performance test of the sensor head in solutions of different pH and in cement specimens are presented, with encouraging results paving the way for future field tests in concrete.
Increasing traffic volume on the one hand and ageing infrastructure on the other hand have created many new challenges for maintenance and structural health monitoring of roads and bridges. In the past, many bridges and road structures have been neglected, often resulting in traffic congestion, road closure, and increased repair costs.
This research is concerned with the development of a system to improve the challenge of maintenance and early detection of damage, particularly moisture penetration and corrosion of steel reinforced concrete components. The objective is to develop a method that will also work after 30 years and longer. Many new IoT solutions are equipped with internal energy storage elements (accumulators or batteries) which are inappropriate here, since most relevant signs of concrete degradation occur after decades, where the functioning of such elements are more than questionable. The presented technology approach uses radio-frequency identification (RFID) and enables connectivity to sensors. It offers the advantage of an passive, completely independent energy supply without any energy storage components.
Since the system should be permanently embedded in concrete, it is crucial to develop a long-term stable device which is adapted to the environmental influences of the structure, e.g., long-term resistance in very alkaline environment of pH 13. In numerous experiments, the robustness of the system was tested and evaluated. Various tests with encapsulations to protect the electronics were performed, and for long-term validation different concrete specimens were instrumented with RFID-sensor-systems. Their operating time is now around two years and investigations for signs of fatigue and damage to the encapsulation and the electronics are ongoing.
Subfloors are layered structures, consisting largely of porous building materials, such as screed. They are often suffering damage from tap water leakage, which is a typical problem in buildings, and which has largely contributed to repair costs of almost 3 billion Euro in 2018 alone in Germany. In this context, especially mould plays a role, which is both destroying the structure and posing severe health risks.
To determine the damaging effects of moisture, it is necessary to know the respective processes occurring in building materials, especially to quantify the amount of moisture and its progress in the material. In this study, humidity sensors are used to derive the material moisture experimentally.
Capacitive sensors recording the relative humidity are embedded into the screed and in the insulation materials such as expanded polystyrene, extruded polystyrene, perlite and glass wool. For the application in screed, the sensors need to be shielded against the aggressive alkaline materials. To ensure an appropriate exchange with the environment, a permeable membrane is requested. Different membrane materials have been investigated regarding their robustness and their permeability.
In the first experimental setup, two humidity sensor arrays with seven individual sensors are embedded in homogeneous screed samples. The measured corresponding relative humidity of the screed is converted to the material moisture based on the approach of Hillerborg. In a second experimental setup, a layered structure of a complete subfloor is built in a box of 0.8 m times 0.8 m. The humidity sensors are positioned in the different insulation materials of various thicknesses. By adding water, leakage damage is simulated and its progress and effect is investigated experimentally.
The investigations point at the question if the observed moisture is able to generate damage such as mould. The moisture and corresponding humidity values are discussed. It will be shown that this low-cost hygrometric approach can be used easily for moisture monitoring of screed and insulation materials as well
Since nuclear magnetic resonance with focus on 1H protons is highly sensitive to pore filling fluids, it is nowadays often applied for the investigation of porous media. Mainly in materials research and especially in the field of non-destructive testing in civil engineering it is increasingly used. Scientific questions about and based on NMR meanwhile cover a broad spectrum. To give an overview, we have reviewed various studies dealing with the determination of moisture contents and parameters such as the pore-size distribution, surface relaxivity, porosity, etc. In some papers, the monitoring of moisture transport in connection with degradation processes or admixtures was the main objective. In other papers, NMR was used for pore space analysis or even applied on site to assess the state of conservation of cultural heritage. Building materials that have been investigated in the presented studies are for example cement, concrete, woods, sandstones etc. In this paper, short descriptions and the significant results of the reviewed articles are summarized and their measurement problems and discrepancies are pointed out. A special feature of this review article is the concise tabular compilation of determined 𝑇1 and 𝑇2 relaxation times, as well as of surface relaxivity values for various materials and components. Finally, relevant aspects are summed up and conclusions about the increasing potential of NMR relaxometry for investigations of porous building materials are drawn, followed by an outlook about future applications and the need for technical development.
Structural Health Monitoring (SHM) has become very important in today's rapidly developing time. High buildings, large bridges and complex technical structures need to be monitored continuously and this over long periods.
Visual monitoring cannot evaluate the internal condition of building structures. Thus, material embedded sensors are needed. Cable connection of these sensors pose the disadvantage of weak spots and water intrusion. For concrete embedded sensors the use of batteries is not convenient, because of limited lifetime, difficult charging, and generation of electrical waste.. Hence, monitoring should be implemented preferentially with firmly embedded passive RFID sensor modules. However, since the concrete structure forms an electromagnetically reflective and absorbing barrier, only limited energy can be transmitted to the module. This project requires a highly energy-saving system, which can record different sensor parameters at critical points.
Four cement-based and four calcium-sulphate-based screed types are investigated. The samples have a diameter of 300 mm and a height of 35 or 70 mm. Up to ten humidity sensors are embedded directly during the concreting of the screed samples. Thus, the humidity over the sample height is monitored during hardening, hydration, evaporation, and oven drying. Furthermore, the screed samples are weighed during every measurement to determine the total mass and the corresponding moisture loss.
To define the pore system precisely, mercury intrusion porosimetry as well as gas adsorption is performed. According to the data, the entire pore volume distribution is known. The measured pore diameters range from 0.8 nm to 100 µm and the total porosity of the examined screeds ranges between 11% and 22%.
Based on these measurement data, moisture transport, pore saturation as well as sorption isotherms and their hysteresis may be calculated quantitatively as described in “Monitoring of the absolute water content in porous materials based on embedded humidity sensors” (Strangfeld and Kruschwitz, 1921).
Moisture testing and mapping
(2023)
In general, wind turbines transform the kinetic energy of the wind into electric power. Thereby, the wind turbine blades are facing unsteady loads which are transferred to the hub to generate a rotation of the turbine’s axis. This brief introduction focuses on the aerodynamics of the blades and the corresponding loads. Starting with the basic flow field and loads of an airfoil, terms like stagnation point, boundary layer, Reynolds number, transition, and separation are introduced. For different geometries, lift and drag coefficient curves are discussed. Then, full wings will be considered, including their three-dimensional flow field due to wing tip vortices and crossflows. As a main source of increased loads, unsteady effects are explained in more detail such as gusts, tower passing, earth boundary layer crossing, free stream turbulences, yaw misalignment, etc. At the end, extra loads due to an oscillating free stream are introduced.
The effect of high-amplitude harmonic surging on airfoil laminar separation bubbles, at small angles of attack, was investigated experimentally in a dedicated surging-flow wind tunnel. A generalized pressure coefficient was developed that accounts for local static pressure variations due to surging. This critical generalization facilitated direct comparisons between surging and quasisteady pressure coefficients, and thus unsteady effects could be distinguished from Reynolds number effects. A momentum-integral boundary layer analysis was implemented to determine movement of the bubble separation point, and movement of the transition point was extracted from experimental surface pressure coefficients. The most significant finding was that bubble bursting occurs, counterintuitively, during early imposition of the favorable temporal pressure gradient, because the favorable pressure gradient rapidly drives the bubble aft, rendering it unable to reattach. This surge-induced dynamic stall mechanism resulted in large lift and form-drag coefficient oscillations.
Furthermore, failure to implement the generalized pressure coefficient definition resulted in temporal form-drag coefficient errors of up to 400 counts.
Monitoring and maintenance of civil infrastructure are of great importance, as any undetected damage can cause high repair costs, unintended deadtime, or endanger structural integrity. The inspection of large concrete structures such as bridges and parking lots is particularly challenging and time-consuming. Traditional methods are mostly manual and involve mapping a grid of measurement lines to record the position of each measurement. Current semi-automated methods, on the other hand, use GPS or tachymeters for localization but still require trained personnel to operate. An entirely automated approach using mobile robots would be more cost- and time-efficient. While there have been developments in using GPS-enabled mobile robots for bridge inspection, the weak signal strength in indoor areas poses a challenge for the automated inspection of structures such as parking lots. This paper aims to develop a solution for the automated inspection of large indoor concrete structures by addressing the problem of robot localization in indoor spaces and the automated measurement of concrete cover and rebar detection.
Almost all building materials in civil engineering have an open porosity and interact with or are affected by the environmental conditions. Structures might suffer from effects such as moisture adsorption, carbonation, corrosion, penetration of salt ions and chemical substances, etc. In the hygroscopic range, these processes are mostly driven by diffusion. Due to the confinement of small pores (less than1 µm), the Knudsen effect reduces the molecular diffusion. This reduction can become more significant in case of temporal changing pore systems because of physisorption of water vapor, carbonation, or chemisorption.
In this study, unstabilised earth blocks and earth masonry are investigated. In a first step, the pore size distribution of the blocks is measured and sorption isotherms are recorded in experiments. Besides the ordinary physisorption, the involved clay minerals undergo swelling or shrinking due to chemisorption. The following two effects must be considered: first, the reduction of the available pore space by the adsorbed water layer. For this, the Hillerborg sorption theory is used, which is a combination of the well-known Brunauer-Emmett-Teller sorption theory and the Kelvin equation. This allows the computation of adsorbed water layers even in curved pore geometries. Second, the variation of the initial pore size distribution due to chemisorption needs to be modelled. Based on these two models, the effective diffusion coefficient can be predicted. For validation, arrays of relative humidity sensors were embedded into a free-standing earth masonry wall. This monitoring was carried out over more than a year to have a broad variety of environmental conditions and was located in Berlin, Germany.
The prediction of the effective diffusion coefficient can also be transferred to other processes and allows the investigation of materials having temporarily changing pore systems. Examples are the carbonation of cementitious materials, alkali silica reaction, calcium leaching of long-lasting structures, etc. These effects are prominent in the meso-pore range and might significantly alter the effective diffusion coefficient.
Almost all building materials in civil engineering have an open porosity and interact with or are affected by the environmental conditions. Structures might suffer from effects such as moisture adsorption, carbonation, corrosion, penetration of salt ions and chemical substances, etc. In the hygroscopic range, these processes are mostly driven by diffusion. Due to the confinement of small pores (< 1 µm), the Knudsen effect reduces the molecular diffusion. This reduction can become more significant in case of temporal changing pore systems because of physisorption of water vapor, carbonation, or chemisorption.
In this study, unstabilised earth blocks and earth masonry are investigated. In a first step, the pore size distribution of the blocks is measured and sorption isotherms are recorded in experiments. Besides the ordinary physisorption, the involved clay minerals undergo swelling or shrinking due to chemisorption. The following two effects must be considered: first, the reduction of the available pore space by the adsorbed water layer. For this, the Hillerborg sorption theory is used, which is a combination of the well-known Brunauer-Emmett-Teller sorption theory and the Kelvin equation. This allows the computation of adsorbed water layers even in curved pore geometries. Second, the variation of the initial pore size distribution due to chemisorption needs to be modelled. Based on these two models, the effective diffusion coefficient can be predicted. For validation, arrays of relative humidity sensors were embedded into a free-standing earth masonry wall. This monitoring was carried out over more than a year to have a broad variety of environmental conditions and was located in Berlin, Germany.
The prediction of the effective diffusion coefficient can also be transferred to other processes and allows the investigation of materials having temporarily changing pore systems. Examples are the carbonation of cementitious materials, alkali silica reaction, calcium leaching of long-lasting structures, etc. This effect becomes most prominent in the meso-pore range and might alter the effective diffusion coefficient by more than 100 %.
Almost all building materials in civil engineering have an open porosity and interact with or are affected by the environmental conditions. Structures might suffer from effects such as moisture adsorption, carbonation, corrosion, penetration of salt ions and chemical substances, etc. In the hygroscopic range, these processes are mostly driven by diffusion. Due to the confinement of small pores ( 1 m), the Knudsen effect reduces the molecular diffusion. This reduction can become more significant in case of temporal changing pore systems because of physisorption of water vapor, carbonation, or chemisorption.
In this study, unstabilised earth blocks and earth masonry are investigated. In a first step, the pore size distribution of the blocks is measured and sorption isotherms are recorded in experiments. Besides the ordinary physisorption, the involved clay minerals undergo swelling or shrinking due to chemisorption. The following two effects must be considered: first, the reduction of the available pore space by the adsorbed water layer. For this, the Hillerborg sorption theory is used, which is a combination of the well-known Brunauer-Emmett-Teller sorption theory and the Kelvin equation. This allows the computation of adsorbed water layers even in curved pore geometries. Second, the variation of the initial pore size distribution due to chemisorption needs to be modelled. Based on these two models, the effective diffusion coefficient can be predicted. For validation, arrays of relative humidity sensors were embedded into a free-standing earth masonry wall. This monitoring was carried out over more than a year to have a broad variety of environmental conditions and was located in Berlin, Germany.
The prediction of the effective diffusion coefficient can also be transferred to other processes and allows the investigation of materials having temporarily changing pore systems. Examples are the carbonation of cementitious materials, alkali silica reaction, calcium leaching of long-lasting structures, etc. This effect becomes most prominent in the meso-pore range and might alter the effective diffusion coefficient by more than 100 %.
Zur Versiegelung von Endlagern für radioaktive oder chemische Abfälle in ehemaligen Salzbergwerken werden Verschlussbauwerke aus Salzbeton auf ihre Eignung geprüft. Seit einigen Jahren werden durch die Bundesgesellschaft Endlagerung (BGE) und der Bundesanstalt für Materialforschung und -prüfung (BAM) an Versuchsbauwerken Erfahrungen mit der Ultraschalltechnik zur Qualitätssicherung unter Tage gesammelt. Hierbei kommen sowohl kommerzielle und experimentelle Geräte zur Echoprüfung als auch eigens entwickelte Bohrlochsonden zum Einsatz. Alle Geräte basieren auf niederfrequenten s-Wellen-Punktkontaktprüfköpfen (25 kHz– 50 kHz), die in unterschiedlichen Arrays kombiniert werden. In mehreren Versuchsreihen gelang es, unverfüllte und teilverfüllte Risse über mehrere Meter zu verfolgen und in ihrer Lage abzubilden. Technische Einbauten konnten bis in ca. 8 m Tiefe im Bauwerk detektiert werden. Mit Hilfe aus der Geophysik adaptierte Abbildungsverfahren gelang es, einige bisher nicht detektierbare Features sichtbar zu machen.
Die Ergebnisse dienen sowohl der Analyse des Versuchsbauwerks als auch der Entwicklung eines Qualitätssicherungssystems für zukünftige reale Verschlussbauwerke.
Entwicklung eines luftgekoppelten Ultraschall-Echo-Prüfverfahrens mittels fluidischer Anregung
(2019)
In vielen technischen Bereichen werden Ultraschallverfahren zur zer-störungsfreien Werkstoffprüfung eingesetzt. Dabei wird ein Schallpuls von einem Prüfkopf in ein Prüfobjekt eingebracht. Der Puls kann unter anderem durch Membra-nen oder Piezoelemente erzeugt werden und wird in der Regel durch direkten Kontakt oder über ein Koppelmittel an das Objekt übertragen. Luftgekoppelter Ultraschall spielt in kommerziellen Anwendungen bisher eine untergeordnete Rolle, da die Dif-ferenz der akustischen Impedanzen von Luft und Festkörpern immense Verluste beim Übergang des Schallsignals hervorruft.
In diesem Beitrag soll ein neuartiges Anregungsprinzip vorgestellt werden, mit dem ein Großteil dieser Verluste vermieden wird. Anstelle eines Festkörpers soll mit Hilfe einer fluidischen Düse Druckluft zur Signalerzeugung eingesetzt werden. In die-ser Düse wird eine selbsterhaltende Strömungsinstabilität erzeugt, die einen Schall-puls von bis zu 100 kHz hervorruft, sodass der Impedanzverlust in die Umgebungsluft entfällt. Da die charakteristische Frequenz eines fluidisch generierten Pulses maßgeb-lich von der Bauform der Düse und dem anliegenden Druck abhängt, lässt sich mittels einer geeigneten Strömungsregelung ein breiter Frequenzbereich zur Abtastung nut-zen. Die so emittierten Pulse werden auf das Prüfobjekt gerichtet und die reflektierten Signale mit einem Laservibrometer an der Oberfläche des Objekts im Echo-Verfahren abgetastet. Von drei signalmindernden Materialübergängen bei gewöhnlichem luftge-koppeltem Ultraschall bleibt in dem hier vorgeschlagenen Messystem lediglich die Grenzfläche von Luft zu Prüfkörper, sodass eine höhere Signalausbeute als bisher er-wartet werden kann.
Development of an Accurate and Robust Air-Coupled Ultrasonic Time-of-Flight Measurement Technique
(2022)
Ultrasonic time-of-flight (ToF) measurements enable the non-destructive characterization of material parameters as well as the reconstruction of scatterers inside a specimen. The time-consuming and potentially damaging procedure of applying a liquid couplant between specimen and transducer can be avoided by using air-coupled ultrasound. However, to obtain accurate ToF results, the waveform and travel time of the acoustic signal through the air, which are influenced by the ambient conditions, need to be considered. The placement of microphones as signal receivers is restricted to locations where they do not affect the sound field. This study presents a novel method for in-air ranging and ToF determination that is non-invasive and robust to changing ambient conditions or waveform variations. The in-air travel time was determined by utilizing the azimuthal directivity of a laser Doppler vibrometer operated in refracto-vibrometry (RV) mode. The time of entry of the acoustic signal was determined using the autocorrelation of the RV signal. The same signal was further used as a reference for determining the ToF through the specimen in transmission mode via cross-correlation. The derived signal processing procedure was verified in experiments on a polyamide specimen. Here, a ranging accuracy of <0.1 mm and a transmission ToF accuracy of 0.3μs were achieved. Thus, the proposed method enables fast and accurate non-invasive ToF measurements that do not require knowledge about transducer characteristics or ambient conditions.
Ultrasonic methods are used in concrete investigations since decades. While being limited to transmission testing in the laboratory for a while, in-situ echo measurements for structural investigations and condition assessment have made their way into practical application in the past 20 years. However, several challenges remain. On one side, there are technical issues as limitations in depth of penetration, resolution and imaging capabilities. On the other side there are still gaps in validation, standardization and certification, which are limiting the applicability in condition/load capacity assessment.
This review reports a couple of developments which will help to overcome these issues. This includes technical developments as new devices which are easier to handle on site or giving a much deeper penetration depth (e.g. the LAUS device at BAM) as well as improvements in imaging by hardware update (e. g. air coupled ultrasound or coded signals) or new software (e. g. RTM imaging). To foster the application in real world projects we are as well working on standardization by developing new reference specimen with international partners which will ensure world-wide comparability of ultrasonic and other methods and quality assurance codes. Further, non-destructive methods are being used to update probabilistic models used for the reassessment of existing structures to support the structural engineer’s decisions.
The majority of ultrasonic devices used for non-destructive testing in civil engineering require contact with the surface of the concrete (specimen), which significantly increases the time required for the measurement. This makes it impractical for extensive investigation of large-scale structures such as bridge decks, foundations, or tunnels.
In a pioneering approach, fluidic oscillators are used as contact free ultrasonic sources to overcome the aforementioned limitations. These robust and cost-effective actuators require only pressurised air and are ideally suited for harsh environments. At a constant supply pressure, they generate a continuous mono-frequent actuation signal. Further, varying the supply pressure via a fast pressure regulator was found to generate a frequency modulated signal which enabled time-of-flight measurement with an added advantage of increased signal to noise ratio. To demonstrate the feasibility of this novel idea of non-contact ultrasound, the results of the initial tests are presented.
The majority of ultrasonic devices used for non-destructive testing in civil engineering require contact with the surface of the concrete (specimen), which significantly increases the time required for the measurement. This makes it impractical for extensive investigation of large-scale structures such as bridge decks, foundations, or tunnels.
In a pioneering approach, fluidic oscillators are used as contact
free ultrasonic sources to overcome the aforementioned limitations. These robust and cost-effective actuators require only pressurised air and are ideally suited for harsh environments. At a constant supply pressure, they generate a continuous monofrequent actuation signal. Further, varying the supply pressure via a fast pressure regulator was found to generate a frequency modulated signal which enabled time-of-flight measurement with an added advantage of increased signal to noise ratio. To demonstrate the feasibility of this novel idea of non-contact ultrasound, the results of the initial tests are presented.