Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
Chemischer Angriff auf Betonbauwerke - Bewertung des Angriffsgrads und geeignete Schutzprinzipien
(2014)
In verschiedenen Bereichen des Betonbaus ist Beton einem chemischen Angriff von außen ausgesetzt, der die Dauerhaftigkeit des betreffenden Bauteils bzw. des gesamten Bauwerks beeinträchtigen kann. Für einen chemischen Angriff in natürlichen Böden und Grundwässern bestehen normative Vorgaben in DIN 4030-1 [R10] bzw. DIN 1045-2 [R19], um den Angriffsgrad anhand der Art und Konzentration der angreifenden Stoffe in Expositionsklassen XA1 (schwach angreifend) bis XA3 (stark angreifend) einzustufen. Hinsichtlich weiterer maßgeblicher Einflussfaktoren wird an dieser Stelle nicht näher differenziert, ob und inwieweit die Regelungen für Böden und Grundwässer auch auf andere Bereiche mit chemischem Angriff auf Beton zu übertragen sind, ist stets im Einzelfall zu überprüfen. Ebenfalls sind die zu treffenden Maßnahmen über die Vorgaben der DIN EN 206-1/DIN 1045-2 [R19] hinaus anwendungsspezifisch festzulegen. Der Hauptausschuss Baustofftechnik (HABT) des DBV hat daher den Arbeitskreis "Chemischer Angriff auf Beton" beauftragt, dieses Merkblatt zu erarbeiten, das Hilfestellung bei der Bewertung einer projektspezifischen chemischen Angriffssituation auf Beton sowie bei der Planung und Ausführung von Schutzprinzipien leisten soll.
ln den letzten Jahren wurden diverse Prüfverfahren und Methoden entwickelt, um die Leistungsfähigkeit von Beton bzw. Bindemittel hinsichtlich des Widerstands gegenüber betonaggressiven Einwirkungen beurteilen zu können. Ein wesentliches Ziel von Prüfverfahren zur Beurteilung der Dauerhaftigkeit von Baustoffen ist, die im Laufe der Nutzungsdauer zu erwartenden Einwirkungen auf den Baustoff realitätsnah abzubilden. Dazu sind die Prüfparameter auf die im jeweiligen Anwendungsbereich vorherrschenden Umgebungs- und Randbedingungen anzupassen. Daneben sind auch die Bewertungskriterien individuell unter Berücksichtigung der im Einzelfall geforderten Nutzungsdauer eines Bauwerks festzulegen. Eine systematische Zuordnung von adäquaten Prüfverfahren bzw. Prüfparametem und Bewertungskriterien für die verschiedenen Anwendungsbereiche im Betonbau, in denen betonaggressive Einwirkungen auftreten, ist mit Ausnahme von Einzelfällen bislang nicht vorhanden. Daneben stellt sich in der Praxis immer wieder das Problem, das Angriffspotenzial der Umgebung eines Bauwerks (prüftechnisch) zu erfassen und zu bewerten.
Der Hauptausschuss Baustofftechnik des DBV hat daher den Arbeitskreis „Chemischer Angriff auf Beton“ beauftragt, dieses Merkblatt zu erarbeiten, das auf Basis von einschlägigen Erfahrungen der Baupraxis und wissenschaftlichen Erkenntnissen Grundsätze und bewährte Methoden zur Beurteilung der Einwirkungs- und Widerstandsseite beim chemischen Angriff auf Beton aufzeigt und diesbezüglich Hinweise für verschiedene Anwendungsbereiche im Betonbau liefert.
Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained.
Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors.
Composition and microstructure stability of cement compound under cyclic hydrothermal condition
(2020)
There have been many researches focused on the performance improvement of ultra-high performance concrete (UHPC) by autoclaving treatment. The goal of autoclaving is to increase the pozzolanic reaction, and to densify the cement stone and the transition zone which originates from the incorporation of supplementary cementitious materials (SCMs), such as silica fume, fly ash and blast furnace slag. Due to the superior properties, UHPC can also be utilized under high mechanical load and aggressive condition, for example, the fabrication of water tanks for thermal storage which is of great significance for saving energy and reducing CO2 emission. It is known that mineral stability of the hydration products of an inorganic binder is highly related to the temperature and pressure of the environment. A certain stable composition at room temperature, however, may undergo a phase transformation at high temperature and the performance decrease under this severe condition will generally be more severe. In this way, the rationale behind this deterioration under long-term hydrothermal condition involving many cycles and long duration has to be clarified, and then appropriate optimizing methods will be performed in order to obtain a kind of construction with high durability under aggressive environment. For this purpose, different types and amounts of SCMs are introduced into the standard mixture of UHPC and the phase compositions after autoclaving at 200 °C and 15.5 bar are determined by combined X-ray diffraction and scanning electron microscope. Mercury intrusion porosimeter is used to characterise the microstructure of the samples. In order to establish the relationship between microstructure and macroscopic properties, compressive and flexural strength are also investigated.
Die Klinkerphasenbildung durch Sinterung in Drehrohröfen bei der Herstellung von Portlandzementklinker (PZK) ist gründlich erforscht und optimiert. Im Hinblick auf mögliche ökonomische und ökologische Vorteile befassen sich aktuelle Forschungsvorhaben darüber hinaus mit der Herstellung von Klinkermineralen aus Stahlwerksschlacken, die eine vergleichbare chemische Zusammensetzung aufweisen.
Neuste Untersuchungen zeigen, dass nach der reduzierenden Behandlung schmelzflüssiger Linz-Donawitz-(LD)-Schlacken und Abscheidung des gebildeten metallischen Eisens eine mineralische Schlacke entsteht, die unabhängig von ihren Abkühlbedingungen ca. 50–60 Gew.% des wichtigsten Klinkerminerals Alit (C3S) enthält und eine hohe hydraulische Reaktivität aufweist.
Die Stabilität des Alits auch nach langsamer Abkühlung deutet auf eine Stabilisierung des Minerals durch Nebenelemente aus den LD-Schlacken hin. Ein sinkender Anteil an LD-Schlacke durch Zusatz synthetischer Schlackemischung, die sich hinsichtlich ihrer Hauptkomponenten wie eine ausreduzierte LD-Schlacke zusammensetzt, führt zu einem Rückgang des Alitgehaltes und dem Zerfall der Schlacke beim Erstarren.