Impulse and lock-in thermography have been applied to detect delaminations of prototype solder joints, similar to those to be produced between Cu shunts and Cu busbar stabilisers at the Large Hadron Collider (LHC) at CERN. Two infrared cameras with different detector materials and with different spectral ranges and two excitation techniques have been tested and compared for their ability to detect delaminations behind 2 and 3 mm thick Cu shunts. We have analyzed the signal to noise ratio (SNR) for each detected defect and are able to detect defects down to a nominal edge length of 4 mm behind 2 mm thick Cu shunts by using fast impulse thermography and a camera with a microbolometer array. For the 3 mm thick Cu shunt, on the other hand, the nominal 4 mm defect is only visible in the lock-in thermography phase images and the highest SNR has been achieved with a cooled InSb-based camera. In addition, numerical simulations show the influence of the minimum detectable defect size on the shunt thickness and that the developed on-site testing technique is sufficient to find all defects that are detectable theoretically.
Carbon fiber reinforced polymer (CFRP) specimens with artificial delaminations and with impact damage have been characterized using active thermography with flash excitation. Systematic investigations have been performed in four different experimental configurations of flash lamps and infrared (IR) camera in transmission as well as in reflection alignment. It is shown here that the diffusivities determined for the sound and for the damaged areas give a good measure for damage characterization. Although reflection measurements also give information about defect depth, reflection measurements from only one side are not sufficient for assessing the whole cross section of the specimens. Thus, depending on sample thickness the lateral size of damage could only be determined from reflections measurements from both sides or from transmission measurements. In this paper, measurement accuracy and limits of flash thermography for the investigation of CFRP specimens are presented in detail together with quantitative data concerning the defects.
Active thermography is well suited for the detection of delaminations and cracks in façade elements like plaster and tiles. Not only artificial heating but also solar heating can be used if the adjustment of the façade and the weather conditions are suitable. Optical methods like laser scanners, photogrammetric methods and crack tracking sensors are providing geometrical 3D data which can be used for a 3D mapping of thermograms and for providing data with higher geometrical resolution. Thus, by the combination and fusion of these data, a comprehensive mapping and monitoring of damages of façade systems is possible.
Lockin thermography as well as flash thermography are very well suited for non-destructive testing and characterisation of inhomogeneities and damage in CFRP structures. Both methods are applied more and more in research and industry, but until know it is not clear which are the advantages of one method against the other. In
this paper, results of two research projects concerning the validation and standardisation of both methods are presented. Three different types of CFRP test specimens consisting of well-defined flat bottom holes, of artificial delaminations made of PTFE plates embedded in CFRP and of real impact damage have been investigated systematically with flash and lockin excitation. Here, the phase images of both methods are compared qualitatively as well as quantitatively.
In this contribution, the development and application of optical and thermographic methods for the nondestructive evaluation of delaminations, cracks and further substructures in Connection with bulging is presented.
Since delaminated fagade elements show geometric as well as thermal anomalies, surface geometry and defects beneath the surface were investigated. As methods, Stereo photogrammetry, a tracking based method for tactile recording of geometric 3D data and active thermography were used. Two case studies were assessed with a combination of these methods: the plaster scratches at the Magdeburg Cathedral and a mural painting in Cobbelsdorf, both located in Germany. While the plaster scratches have been investigated by artificial heating with an infrared radiator, the rural painting was tested by analysing the temperature increase due to solar heating.
Lockin thermography is a well-suited method for the characterization of structures made of both metal and fiber reinforced plastic. In most cases, only phase images are analyzed, although the amplitude images might contain useful information as well. Thus, systematic studies of lockin thermography are presented, assessing amplitude and phase images for the detection and quantification of defects in isotropic (steel) and anisotropic (carbon fiber reinforced plastic) materials. Characterized defects are flat bottom holes with different diameters and various remaining wall thicknesses as well as crossed notches at different depths. The excitation frequency was varied while keeping the number of analyzed excitation periods nearly constant for each material. The data analysis was focused on the detectability of the defects both in the amplitude and phase images, including the determination of the signal-to-noise ratio and of the spatial resolution. As a result, the limits of defect detectability and spatial resolution are given for each material
Standards for the application of flash thermography as well as of lock-in thermography are urgently required.
Both methods are applied more and more often in research and industry, but still extensive validation procedures are required for each individual application. In this paper, the results of two research projects concerning the validation and standardisation of both methods are presented. This includes results of a detailed study of the influence of measurements parameters on flash thermography, of the comparison of the lateral resolution obtained with flash and lock-in thermography and the description of a draft standard for flash thermography.