- Dispergierung (3)
- Nanopulver (3)
- Folie (2)
- Friction (2)
- Alcaline earth fluorides (1)
- Bending strenght (1)
- Bending strength (1)
- Ca-Ba fluoride (1)
- Ceramic wear (1)
- Ceramics (1)
The tribological behavior of different low infrared (IR) emission ceramic materials from the titanate group has been investigated at room temperature under gross slip fretting conditions against 100Cr6 ball bearing steel and α-alumina as the counterface materials. For all material pairs, friction and wear depended largely on the relative humidity of the environment. When paired with steel the low IR-emission ceramic disks showed higher wear resistance. Under dry conditions, almost no wear was found on the low IR-emission ceramic specimen. The high wear on the steel counter body is caused not only by tribo-oxidation, which is the main wear mechanism, but also by abrasion. In dry conditions a COF of 0.6 and in humid conditions a COF of 0.2 have been measured. When paired with α-alumina the results on wear are just opposite to those with steel counterbody and the low IR-emission ceramic materials show much lower wear resistance under all conditions. This is explained by the predominance of abrasion and the relatively large difference in hardness between the low IR-emission ceramic and α-alumina. In high humidity environments the results point to the formation of stable reaction layers causing lower friction and wear.
It has been successfully demonstrated that ceramic materials can be joined in the green
state without a second phase by using low pressure injection molded parts. The investigation of the
joining interface revealed that a high quality interface can be achieved by carefully adjusting the
different manufacturing steps. The use of monomodal particle size distribution in the used powder
CT3000SG is inferior to a broader particle size distribution obtained by replacing 33% of the finer
alumina powder by coarser CT1200SG. In this way the dewaxing process is significantly improved
when the wall thickness of the part exceeds 3 mm. The investigation of the mechanical properties of
the joined and sintered parts revealed, that the bending strength of the joined specimens achieved
about 80 % of the unjoined, monolithic specimens.