Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (8)
- Zeitschriftenartikel (6)
- Vortrag (6)
- Posterpräsentation (6)
Schlagworte
- GMR (10)
- Neutron diffraction (5)
- Residual stress (5)
- Metal magnetic memory (4)
- Baustahl (3)
- GMR-Sensorik (3)
- Magnetic stray fields (3)
- Plastic deformation (3)
- Eigenspannungen (2)
- Low carbon steel (2)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (4)
- 8.4 Akustische und elektromagnetische Verfahren (4)
- 5 Werkstofftechnik (3)
- 5.2 Metallische Hochtemperaturwerkstoffe (3)
- 9 Komponentensicherheit (2)
- 5.1 Mikrostruktur Design und Degradation (1)
- 7 Bauwerkssicherheit (1)
- 7.1 Baustoffe (1)
- 8.5 Röntgenbildgebung (1)
- 9.2 Versuchsanlagen und Prüftechnik (1)
Eingeladener Vortrag
- nein (6)
The metal magnetic memory (MMM) technique relies on the measurement of stress-induced self-magnetic leakage fields (SMLFs) at the stress concentration zones (SCZs) of ferromagnetic materials during mechanical loading. However, there is an associated change in geometry of the specimen along with the stress due to plastic deformation. This paper presents a three-dimensional finite element (3D-FE) analysis of the stress-induced geometry effect on SMLFs in notched specimens during tensile deformation. The tangential (Hx) and normal (Hy) components of the SMLF signals have been predicted from the deformed specimens caused by different levels of tensile stress. Key parameters from the SMLF signals are determined for the possible estimation of damage in the specimen under tension. Studies reveal that the stress-induced geometry effect has a great influence (about 20%) on the SMLF signals, especially in the plastic deformation stage. The results show that the peak amplitude could be used for the estimation of different deformation stages under tension. The study also reveals that the SMLF signal is influenced by the thickness of the tensile specimen. The model-predicted thickness profile has also been experimentally validated.
Die Messung spontaner magnetischer Streufelder ferromagnetischer Materialien wird als neue, Metal Magnetic Memory (MMM) genannte, Methode der zerstörungsfreien Prüfung (ZfP) angesehen, Schädigungen frühzeitig vorherzusagen. Die MMM Methode versucht, die sich gleichzeitig mit der Schadensentwicklung ausbildende lokale magnetische Struktur für die ZfP zu nutzen und zwar schon vor der eigentlichen Rissinitiierung. Das zugehörige Regelwerk ISO 24497 verspricht neben der Detektion von Mikrorissen und Inhomogenitäten des Werkstoffgefüges auch die Bestimmung des (Eigen-) Spannungszustandes. Neue, an der Bundesanstalt für Materialforschung und -prüfung für die ZfP angepasste GMR (Giant Magneto Resistance)-Sensorik erlaubt Magnetfeldmessungen mit einer Ortsauflösung im Mikrometerbereich. Mit höherer Ortsauflösung zeigen sich Unterschiede, jedoch keine Widersprüche zu bisher publizierten Daten. Ihnen wesentlich ist, dass es einige verwertbare Hinweise auf einen Zusammenhang von Restfeldmagnetisierung und Materialeigenschaften gibt.
Measurement of spontaneous magnetic stray field signals has been reported to be a promising tool for capturing macro-scale information of deformation states, defects and stress concentration zones in a material structure. This paper offers a new method for self-magnetic leakage field detection using a magneto-optical (MO) hand-held microscope. Its sensor has a dynamic field range between ±0.05 and ±2 kA/m and a lateral optical resolution of approx. 10 µm. We examined flat tensile test specimens of metastable austenitic steel AISI 304. Static tensile tests were repeatedly interrupted at various predetermined states of strain and the magnetic information was measured by the MO system. Comparative measurements using a high-precision magnetic field GMR-sensor, verify the outstanding capability of the MO microscope regarding spatial resolution of magnetic fields.
Evaluation of high spatial resolution imaging of magnetic stray fields for early damage detection
(2017)
The paper discusses the evaluation of elastic and plastic strain states in two low-carbon steels of the same steel group with high spatial resolution GMR (giant magneto resistance) sensors. The residual stress distributions of tungsten inert gas welded plates were determined by means of neutron diffraction as a reference. The normal component of local residual magnetic stray fields arise in the vicinity of the positions of maximum stress. The experiments performed on flat tensile specimen indicate that the boundaries of plastic deformations are a source of stray fields. The spatial variations of magnetic stray fields for both the weld and the tensile samples are in the order of the earths magnetic field.
This study examines the relationship between the magnetic mesostructure with the microstructure of low carbon steel tungsten inert gas welds. Optical microscopy revealed variation in the microstructure of the parent material, in the heat affected and fusion zones, correlating with distinctive changes in the local magnetic stray fields measured with high spatial resolution giant magneto resistance sensors. In the vicinity of the heat affected zone high residual stresses were found using neutron diffraction.
Notably, the gradients of von Mises stress and triaxial magnetic stray field modulus follow the same tendency transverse to the weld. In contrast, micro-X-ray fluorescence characterization indicated that local changes in element composition had no independent effect on magnetic stray fields.
The residual stress distribution of tungsten inert gas welded S235JRC+C plates was determined by means of neutron diffraction(ND). Large longitudinal residual stresses with maxima around 600 MPa were found. With these results as reference, the evaluation of residual stress with high spatial resolution GMR (giant magneto resistance) sensors was discussed. The experiments performed indicate a correlation between changes in residual stresses (ND) and the normal component of local residual magnetic stray fields (GMR). Spatial variations in the magnetic field strength perpendicular to the welds are in the order of the magnetic field of the earth.
The measurement of spontaneous magnetic stray fields of ferromagnetic materials is considered as a new method of non-destructive testing, the Metal Magnetic Memory method. Usually fluxgate sensors with spatial resolution in the order of a few millimeters are used as receivers. This contribution discusses the application of GMR (Giant Magneto Resistance) sensors with a spatial resolution in the micrometer range. Studies reveal that GMR sensors can detect clear demarcated plastic deformations in S235JR steel. Furthermore we present high spatial resolution magnetic measurements of deformation induced martensite formation of AISI 304 metastable austenitic steel for different deformation states.