The measurement of spontaneous magnetic stray fields of ferromagnetic materials is considered as a new method of non-destructive testing, the Metal Magnetic Memory method. Usually fluxgate sensors with spatial resolution in the order of a few millimeters are used as receivers. This contribution discusses the application of GMR (Giant Magneto Resistance) sensors with a spatial resolution in the micrometer range. Studies reveal that GMR sensors can detect clear demarcated plastic deformations in S235JR steel. Furthermore we present high spatial resolution magnetic measurements of deformation induced martensite formation of AISI 304 metastable austenitic steel for different deformation states.
Magnetic testing methods are frequently applied in non-destructive evaluation of ferromagnetic materials. In the past decade, metal magnetic memory (MMM) technique according to ISO 24497 is gaining considerable interest in the magnetic NDT community. In contrast to traditional Magnetic Flux Leakage (MFL) testing, the inspection objects are not intentionally magnetized by an external magnetic field. Due to physical coupling between mechanical stress and magnetization in ferromagnetic materials, it is assumed that the distribution of the “natural” MFL (self-magnetic-leakage field, SMLF) indicate zones of different remanent magnetization, which in turn, correspond to the internal stress of specimen or in the most general sense to material degradation.
Usually, MMM measurements are performed by relatively bulky magnetic inspection sensors providing a spatial resolution in millimetre range. High precision GMR (Giant Magneto Resistance) measurements in the micrometer regime along with image based representation and evaluation can provide a higher degree of information. We present a concise summary of a broader research project aimed at studying the correlation of magnetic structure and microstructure of steels. Particularly, we compare residual stress measurements in S235JR steel by means of neutron diffraction with high resolution magnetic field measurements. In addition, we discuss the influence of deformation-induced magnetization in plastically deformed specimens with and without notches due to various quasi-static and cyclic load levels. Furthermore, comparative measurements with common non-destructive testing methods are presented.
Despite of a quantitative evaluation of material degradation, the in the field inspection by MMM remains problematic due to substantial influences on such as external magnetization, anisotropy of internal magnetization and material degradation, as well as geometry and surface effects of the inspection objects on SMFL signals. The prospects and restrictions of the MMM technique are discussed in this contribution.
Die mechanische Spannung ist ein maßgeblicher Parameter ferromagnetischer Materialien. Wird ein solches Material unter die Curie Temperatur abgekühlt, zerfällt es spontan in nahezu selbstgesättigte magnetische Domänen. Diese Magnetisierung führt gleichzeitig zu einer Verformung der mit ihr gekoppelten Kristallgitter. Ein Effekt der auch reziprok gilt: wird die Gitterverformung durch eine Spannung behindert ändert sich zwangsweise der magnetische Zustand.
Man kann annehmen, dass zwischen unterschiedlichen, für sich aber homogen verspannten Werkstoffbereichen, lokale magnetische Streufelder auftreten, weil magneto-mechanische Effekte eine Inkompatibilität der Domänenstruktur induzieren. Bekanntlich bilden sich Spannungsgradienten nach Schweißprozessen durch ungleichmäßigen Wärmeeintrag, thermischer Dehnung, und unterschiedlichen Abkühlraten aus.
Unter dieser Prämisse untersuchen wir Wolfram-Inertgas geschweißte Blindnahtproben (250x100x4,8 mm^3) aus einem hypereutektoiden Baustahl.
Der Spannungszustand der Proben wurde anhand von Neutronendiffraktometrie (ND) am Instrument E3 am Reaktor BERII (Helmholzzentrum Berlin, HZB) charakterisiert. ND ist ein Referenzverfahren für die quantitative Bestimmung von elastischen Dehnungen in kristallinen Materialien, deren Gitter selbst der Messmaßstab ist. Die Auswertung zeigt hohe Längsspannungen mit lokalen Maxima in Größenordnung von 600 MPa, die von umgebenen Druckspannungszonen kompensiert werden.
Zur Detektion der magnetischen Kleinststreufelder verwenden wir speziell designte GMR-Sensorik (GMR - Giant Magneto Resistance), die aufgrund der geringen Größe ihrer aktiven Sensorelemente hohe Ortsauflösung mit Sensitivität vereint. Die Visualisierung der Messergebnisse lässt eine klare magnetische Mikrostruktur der Schweißnähte erkennen, in der die Streufelder lateral in Größenordnung des Erdmagnetfeldes variieren (~50 µT).
Wir zeigen durch einen Vergleich beider Messverfahren, dass lokale magnetische Streufeldmaxima in hohem Maße mit den Spannungsgradienten übereinstimmen.