We show how historical gypsum plaster preparation methods affect the microstructure and the wettability properties of the final stucco materials. We reproduced a traditional Persian recipe (Gach-e Koshteh, ~14th century AD), which involves a continuous mechanical treatment during plaster hydration. These samples were compared with a laboratory-replicated historical recipe from Renaissance Italy (Gesso Sottile, ~15th century AD) and contemporary low-strength plaster. The Koshteh recipe induces the formation of gypsum platelets, which exhibit preferential orientation in the plaster bulk. In contrast,
the Italian and low-strength plasters comprise a typical needle-like morphology of gypsum crystals. The platelets in Koshteh expose the more hydrophilic {010} face of gypsum in a much more pronounced manner than needles. Consequently, the Iranian plaster displays enhanced wettability, enabling its direct use for water-based decoration purposes, or as a fine finishing thin layer, without the need of mixing it with a binder material.
Contrary, in Sottile, gypsum crystals are left to equilibrate in large excess of water, which promotes the growth of long needles at the expense of smaller crystals. Typically, such needles are several times longer than those found in a control regular plaster. For this
crystal habit, the total surface of hydrophilic faces is minimized. Consequently, such plaster layers tend to repel water, which can then be used, e.g., as a substrate for oilbased panel paintings. These findings highlight the development of advanced functional materials, by tuning their microtexture, already during the premodern era.
Here, we show that calcium sulfate dihydrate (gypsum) can be directly, rapidly and reversibly converted to calcium sulfate hemihydrate (bassanite) in high salinity solutions (brines). The optimum conditions for the efficient production of bassanite in a short time (<5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the better-known behaviour of the bassanite phase in low-salt environments. In low-salinity aqueous solutions, bassanite is considered to be metastable with respect to gypsum and anhydrite, and therefore gypsum-to-bassanite conversion does not occur in pure water. Interestingly, the high-salinity transformation of gypsum-to-bassanite has been reported by many authors and used in practice for several decades, although its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures was inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline phase for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.