The control of friction and wear is a major concern in many industrial applications. A promising method for a tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in deterministic pattern where needed on highly stressed surfaces, i.e. on forming or cutting tools. However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free Metal Matrix Composite with a high share of homogeneously distributed particles and especially a high implant hardness.
In this study TiN, TiC and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of the pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel was investigated. Although all powder materials had grain sizes smaller than 10 µm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (~64 %) was observed for TiB2. By scanning electron microscopy and energy dispersive X-ray spectroscopy, it was also shown that a significant share of the pre-placed particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in-situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 HV1 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By X-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in-situ formation of TiC particles, which was proven by electron backscatter diffraction. In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown the most promising results.
The control of friction and wear is a major concern in many industrial applications. A promising method for a tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in deterministic pattern where needed on highly stressed surfaces, i.e. on forming or cutting tools. However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free Metal Matrix Composite with a high share of homogeneously distributed particles and especially a high implant hardness.
In this study TiN, TiC and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of the pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel was investigated. Although all powder materials had grain sizes smaller than 10 µm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (~64 %) was observed for TiB2. By scanning electron microscopy and energy dispersive X-ray spectroscopy, it was also shown that a significant share of the pre-placed particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in-situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 HV1 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By X-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in-situ formation of TiC particles, which was proven by electron backscatter diffraction. In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown the most promising results.
Die Laserimplantation erlaubt die Herstellung verschleißbeständiger, erhabener Mikrostrukturen (Implants) auf Stahloberflächen durch ein diskontinuierliches Dispergieren von keramischen Partikeln mittels gepulster Laserstrahlung. Durch die flexible Anordnung separierter Implants zu komplexen Mustern erlaubt das Verfahren eine gezielte Oberflächenstrukturierung zur Beeinflussung des Reibungs- und Verschleißverhaltens. Insbesondere erwies sich Titandiborid (TiB2) als Implantationsmaterial für geeig-net, da eine Manipulation der Implantgeometrie in einem breiten Bereich vorgenommen werden konnte, ohne dass Materialdefekte wie Risse oder Poren auftraten.
Ziel der Untersuchungen war es, den Einfluss implantierter TiB2-Partikel auf die Materialeigenschaften von X153CrMoV12 zu ermitteln. Hierfür wurden im Rahmen der Arbeit die Laserparameter (Pulsleistung und -dauer) in einem breiten Parameterfeld variiert und vergleichende Untersuchungen an TiB2 implan-tierten Zonen sowie an punktuell umschmelzstrukturierten Zonen durchgeführt. Die Ergebnisse zeigen, dass eine reine Umschmelzstrukturierung zu einer deutlichen Reduktion der Oberflächenhärte aufgrund erhöhter Restaustenitgehalte (γR) führt. Im Gegensatz dazu führt das Laserimplantieren von TiB2-Partikeln zu einer deutlichen Härtesteigerung in den kuppel- oder ringförmigen Implants. Härtewerte von bis zu 1800 HV1 resultieren aus dispergierten TiB2-Primärpartikeln sowie in-situ ausgeschiedenen Se-kundärphasen, durch die der Restaustenitanteil zudem deutlich reduziert wird.
The laser implantation technique bases on a localized dispersing of ceramic particles in metallic surface layers for changing their micro geometry as well as their material properties. Using TiB2 and NbC hard particles, tailored microtextures consisting of elevated dome-, ring-, or line-shaped Features can be manufactured. Especially TiB2 implants feature high hardness values up to 1800 HV1 and ceramic particle contents up to 55 %, indicating superior wear resistant properties.