In the automotive industry, hot stamping has been established as a key technology for manufacturing safety-relevant car body components with high strength-to-weight ratio. However, hot stamping tools are stressed by cyclic thermo-mechanical loads, which leads to severe wear and high friction during the forming operation. Consequently, the quality of the parts, the durability of the tools and the efficiency of the process are negatively affected. Within the scope of this work, a promising approach named laser implantation process has been investigated for improving the tribological behavior of hot stamping tools. This technique enables the fabrication of highly wear resistant, separated and elevated micro-features by embedding hard ceramic particles into the tool via pulsed laser radiation. Hence, highly stressed tool areas can be modified, which influences the thermal and tribological interactions at the blank-die interface. To clarify these cause-effect relations, numerical simulations, quenching tests as well as tribological investigations have been conducted. In this context, laser-implanted tools reveal a significantly improved tribological performance while offering the possibility to adjust the thermal properties within hot stamping. Based on these results, a tailored tool modification can be pursued in future research work, in order to enhance the effectiveness of hot stamping tooling systems.
Laser metal deposition (LMD) has been applied as a coating technology for many years. Today, the technologies capacity to produce 3D depositions leads to a new field of application as additive manufacturing method. In this paper, 3D laser metal deposition of titanium alloy Ti-6Al-4V is studied with special regard to the demands of additive manufacturing. Therefore, only the coaxial LMD powder nozzle is used to create the shielding gas atmosphere, which ensures high geometric flexibility. Furthermore, specimen with high aspect ratio and hundreds of layers are manufactured, which represent typical features in additive manufacturing. The presented study contains the following steps: First, cylindrical specimens are manufactured with a standard shell-core build-up strategy and mechanical properties as well as fracture mechanisms are determined. Based on the results, experiments are conducted to improve the build-up strategy and new tensile test specimens are built with the improved strategy. The improved strategy incorporates variable track overlap ratios to achieve a constant growth in the shell and core area. As blanks, lean cylinders comprising more than 240 layers and a height of more than 120mm are manufactured. The specimens are analyzed by X-ray inspection for material defects. Fractured surfaces are observed via scanning electron microscopy and the composition of the surfaces is determined using energy dispersive X-ray spectroscopy. The tensile test results prove mechanical properties close to ASTM F1108 specification for wrought material.
The control of friction and wear is a major concern in many industrial applications. A promising method for tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in a deterministic pattern where needed on highly stressed surfaces, i.e., on forming or cutting tools.
However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free metal matrix composite with a high share of homogeneously distributed particles and, especially, high implant hardness. In this study, TiN, TiC, and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel were investigated.
Although all powder materials had grain sizes smaller than 10 μm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (∼64%) was observed for TiB2. By scanning electron microscopy and energy dispersive x-ray spectroscopy, it was also shown that a significant share of the preplaced particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By x-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in situ formation of TiC particles, which was proven by electron backscatter diffraction.
In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown
the most promising results.
The laser implantation–named technique aims to address the tribological problems frequently seen on tool surfaces during hot stamping. It is based on the creation of elevated dome- or ring-shaped hard structures on the surface of tool steels by a localized dispersing of hard particles. Therefore, a combination of the two distinct approaches that are normally used in surface Technology for optimizing friction and wear, i.e., surface texturing and surface material optimization, are realized in one processing step. In experimental studies, a localized dispersing of TiB2 particles in the surface layer of the hot work tool steel X38CrMoV5-3 was considered and compared with punctual laser–remelted textures. The structures (micro-) hardness was measured at top- and cross-sections. With the aid of a scanning electron microscope, energy dispersive X-ray spectroscopy and X-ray diffraction the interaction between the hard particles and the substrate material were studied. From the results, an optimal parameter range was identified for laser implantation. To the investigation’s end, the implant geometry was measured by optical microscopy and White light microscopy. Furthermore, a mathematic model was introduced, which allows a prediction of the implant geometry as a response to the laser parameters. It was shown that the implantation of TiB2 particles leads to a significant hardness increase up to 1600 HV1 due to the dispersion of initial particles and an in situ precipitation of new titanium-rich phases. It was possible to create defect-free dome- and ring-shaped microstructures on the surfaces. It was also shown that the implants geometry highly depends on the applied laser parameters. The applied central composite design shows a good agreement with the experimental results.
AISI D2 is one of the most applied cold-working tool steel for deep drawing operations, due to the materials good toughness and high wear resistance. However, since the lubricant-free deep drawing as well as the processing of high strength and ultra-high strength steel sheets remaining ongoing trends in the automotive industry, the tool surfaces need to be improved regarding their friction and wear behavior. For this purpose elevated micro textures can be applied. Since protruded micro features are predominantly affected by wear, a structuring process enabling the formation of suitable textures with high wear resistance is needed.
In this paper surface texturing at microscale was conducted by laser implantation. This technique allows the fabrication of highly wear resistant, separated and elevated features (implants) on steel surfaces via a discontinuous dispersing of ceramic particles by pulsed laser radiation. The aim of this study was to investigate the techniques potential for the creation of wear resistant elevated micro features on AISI D2 tool steel surfaces by the application of TiB2 particles. The laser parameters (pulse power and length) were varied and a comparative material analysis on AISI D2 laser remelted spots and TiB2 localized dispersed zones was examined. High-speed camera recordings allowed the description of the particle insertion mechanism from pre-coatings during laser processing. Mechanical properties were analyzed by (micro-) hardness measurements at top and cross sections. The microstructure was investigated by optical microscopy, scanning electron microscopy (SEM), energy dispersive Xray
spectroscopy (EDX) and X-ray diffraction (XRD). The implants geometrical properties (diameter, height, depth) were investigated by white light interferometry and optical microscopy. The experiments reveal that a pulsed laser remelting of AISI D2 leads to a significant hardness drop due to high retained austenite (γR) contents. Contrary, a localized dispersing of TiB2 particles leads to defect free dome- or ring-shaped elevated features with hardness values up to 1800 HV1. The high hardness values result from the dispersed TiB2 particles and an in-situ precipitation of new hard particle phases, which lead to a reduction of the γR content within the matrix.