Filtern
Dokumenttyp
Schlagworte
- 3D printing (1)
- 3D-printing process (1)
- Bending strength (1)
- Bone substitute material (1)
- Calcium alkali phosphate (1)
- Drywood termite (1)
- Flowability (1)
- Powder bed additive manufacturing (1)
- Powder flow (1)
- Powder rheology (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (2)
- 5.4 Multimateriale Fertigungsprozesse (2)
- 4 Material und Umwelt (1)
- 4.0 Abteilungsleitung und andere (1)
- 4.1 Biologische Materialschädigung und Referenzorganismen (1)
- 6 Materialchemie (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.0 Abteilungsleitung und andere (1)
Glass-ceramics containing Ca2KNa(PO4)2 as the main crystalline phase have a solubility which is 8 times higher than that of alpha-tricalcium phosphate ceramics. When using these compositions in drug delivery systems, especially in bone, it is necessary to create a material with a high open porosity. A Ca2KNa(PO4)2-based glass-ceramic was prepared from a borosilicate glass melt. The processed material includes minor amounts of boron which are low enough for medical application. Tissue response was studied using an animal model. Particles were implanted in rabbit femurs. Bone and soft tissue development occurred at the particle interfaces. In general, most particles were enclosed in the network of trabecular bone. The advantages of using a biomaterial with high porosity (pore size of 1-3 micron), together with rapid biodegradation, bioactivity and biocompatibility, despite traces of boron, were shown. 4 refs.
In vivo test of a high porous rapidly resorbable dicalcium potassium sodium phosphate glass-ceramics
(2002)
Frass (fine powdery refuse or fragile perforated wood produced by the activity of boring insects) of larvae of the European house borer (EHB) and of drywood termites was tested as a natural and novel feedstock for 3D-printing of wood-based materials. Small particles produced by the drywood termite Incisitermes marginipennis and the EHB Hylotrupes bajulus during feeding in construction timber, were used. Frass is a powdery material of particularly consistent quality that is essentially biologically processed wood mixed with debris of wood and faeces. The filigree-like particles flow easily permitting the build-up of woodbased structures in a layer wise fashion using the Binder Jetting printing process. The Quality of powders produced by different insect species was compared along with the processing steps and properties of the printed parts. Drywood termite frass with a Hausner Ratio HR = 1.1 with ρBulk = 0.67 g/cm3 and ρTap = 0.74 g/cm3 was perfectly suited to deposition of uniformly packed layers in 3D printing. We suggest that a variety of naturally available feedstocks could be used in environmentally responsible approaches to scientific material sciences/additive manufacturing.
The flow behavior of powders has an essential role in many industrial processes, including powder bed additive manufacturing. The characterization of the flow behavior is challenging, as different methods are available, and their suitability for an application in additive manufacturing is still controversial. In this study, six standardized methods (measurement of bulk density by ISO 60 and by ASTM B329, angle of repose by ISO 4324, discharge time by ISO 6186 and by ASTM B964-16, and Hausner Ratio by ASTM 7481 – 18), the rotating drum method (by GranuDrum) and powder rheometry (Anton Paar powder cell), were applied to five size fractions of a crushed quartz sand powder and compared. A statistical approach is proposed and discussed to correlate the obtained flowability indexes with the packing density of powder beds deposited layer-by-layer, and these correlations are compared between methods. Overall, the measurement of bulk density by ASTM B329 that showed the best correlation with the powder bed density. Advanced methods such as the rotating drum method and powder rheometry did not demonstrate particularly good correlations, however they provided complementary information which can be useful to assess the dynamic behavior of powders.