Laser-induced periodic surface structures (LIPSS, ripples) were processed on steel (X30CrMoN15-1) and titanium (Ti) surfaces by irradiation in air with linear polarized femtosecond laser pulses with a pulse duration of 30 fs at 790 nm wavelength. For the processing of large LIPSS covered surface areas (5 mm × 5 mm), the laser fluence and the spatial spot overlap were optimized in a sample-scanning geometry. The laser-processed surfaces were characterized by optical microscopy (OM), white light interference microscopy (WLIM) and scanning electron microscopy (SEM). Spatial LIPSS periods between 450 and 600 nm were determined. The nanostructured surface regions were tribologically tested under reciprocal sliding conditions against a 10-mm diameter ball of hardened 100Cr6 steel. Paraffin oil and engine oil were used as lubricants for 1000 sliding cycles at 1 Hz with a normal load of 1.0 N. The corresponding wear tracks were analyzed by OM and SEM. In particular cases, the laser-generated nanostructures endured the tribological treatment. Simultaneously, a significant reduction of the friction coefficient and the wear was observed in the laser-irradiated (LIPSS-covered) areas when compared to the non-irradiated surface. The experiments reveal the potential benefit of laser surface structuring for tribological applications.
This paper shows how Angle-Resolved Scattering can reveal wear on engineered surfaces. The samples studied, three discs made of steel 100Cr6H used in gear wheels in the automotive industry, were assessed after they had undergone ball-on-disc tests. Scattering maps recorded for spatial frequencies from 0.1 µm-1 to 2.7 µm-1 show a contrast inversion around 0.36 µm-1 revealing the wear trace. Besides measurements of rms roughness, where mean values are 20 nm and 24 nm depending on the locations considered, stationarity and isotropy, we demonstrate the ability of the technique to reveal localized wear on this type of surface in a rapid, robust and convenient way. We show that the tool trace is influenced by the load magnitude rather than by the number of oscillation cycles and highlight the key role played by surface roughness in how the sample responds to wear tests.