Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (26) (entfernen)
Referierte Publikation
- ja (26) (entfernen)
Schlagworte
- Friction (8)
- Wear (8)
- Roughness (5)
- Slip-rolling (5)
- Tribology (5)
- DLC (4)
- Laser-induced periodic surface structures (LIPSS) (4)
- Femtosecond laser ablation (3)
- Femtosecond laser processing (3)
- AFM (2)
Organisationseinheit der BAM
Downsizing (power-to-weight ratio) and higher speeds lead to a rise in Hertzian contact pressures in combination with an increase in surface or oil temperatures. Under such conditions, commonly used bearing steels, such as 100Cr6, reach their limits, creating a demand for alternative slip-rolling resistant steel alloys. The present work therefore compares the slip-rolling performance of various steel types with Maraging- and PM-type steel alloys such as e.g. CSS-42L™, ASP2012, BIMAX42+, in the Hertzian contact pressure range up to P0max of 4 GPa. Through-hardened 100Cr6H (AISI 52100), case-hardened 20MnCr5 (AISI 5120H) and nitrogen alloyed Croni-dur30 (AMS 5898) still compete in terms of slip-rolling and wear resistance and load carrying capacity, whereas Maraging- and PM-type steel alloys offer superior strength and toughness properties.
Paraffinöl geschmierte Wälztests wurden an extrem harten Diamantschichten auf hartem SSiC Substrat, unterschiedlichen, harten DLC-Schichten auf 100Cr6 Substraten (HRC60) sowie ausgewählten DLC-Schichten auf ungehärtetem Stahl (HRC 20) durchgeführt. Die Wälztests wurden in einem Zweischeibentribometer vom Typ Amsler bei einer anfänglichen, maximalen Flächenpressung nach Hertz von P0=2,3 GPa ausgeführt. Als Abbruchkriterium für die Tests wurde das Erreichen von n=1.000.000 Überrollungen (Langzeittests n=10.000.000 Überrollungen) oder das Auftreten einer Schädigung mit einer zusammenhängenden Fläche von A>1 mm2 festgelegt. Die Wälztests zeigten, dass das harte SSiC Substrat zwar eine stützende Wirkung auf die Diamantschicht hat, diese aber aufgrund von Rissen im Substrat versagte. Ferner gibt es wenigstens zwei DLC-Schichten, die, aufgebracht auf 100Cr6 Scheiben (HRC60), den Wälztests bis n=10.000.000 Überrollungen ohne nennenswerte Schäden widerstanden. Diese Schichten passten sich auch den Verformungen des weichen, stickstofflegierten Stahls (HRC20) an, ohne das es zu größeren Abplatzungen kam (A>1 mm2).
High-power piezo-electric motors with power densities of 1.4 kW/kg display a potential for substituting hydraulic actuators. For this application, two novel tribometers of the same type have been designed using commercially available components for sliding motion at 40 kHz with amplitudes between 2.5 µm and 5 µm. The tribometers are equipped with means to measure amplitude, frequency, power required to keep the samples in motion and load applied. The effective motion between the two contacting bodies is monitored in each of the tribometers. These data are used to evaluate the coefficient of friction. The wear rate was determined after the tests. The set-ups were tested using well-known 100Cr6H (AISI 52100) samples before investigating novel, non-commercial substrates such as AlFeCrTi-alloys and tungsten carbide-based coatings as well as Magnéli-type coatings (Tin-2Cr2O2n-1 and TinO2n-1). This paper presents the principle of the ultra-high frequency tribometers and first tribological quantities of materials and coatings tested up to and above 1011 cycles. Very low wear rates in the range 10-8 mm³/Nm down to 10-10 mm³/Nm were determined under dry oscillation in air.
Diamond-like carbon (DLC) coatings are perceived as part of a strategy for low frictional tribosystems. Especially the automotive industry anticipates a benefit in applying such coatings in association with the lightweight construction of mechanical parts, for instance in gear and engine components. Therefore, in previous investigations amorphous carbon (a-C) and tetragonal amorphous carbon (ta-C) coatings were inspected. For up to ten million cycles at Hertzian contact pressures P0max of 2.9 GPa it was shown that these coatings are slip-rolling resistant not only at room temperature in the presence of unaddivated paraffin oil, but also up to 120 °C oil temperature. The steel substrates in this investigation were made of the hardened and tempered steels 100Cr6H and Cronidur 30. The aim of the current work is manifold. The Hertzian contact pressures should be increased up to P0max of 4.2 GPa by using new steel metallurgies as substrates for thin film coatings. These steel metallurgies are also assessed, if they can compete as uncoated couples. Two high toughness spring steels and an ultra-high toughness aerospace steel were tested in a twin disc tribometer of the Amsler type as well as in an Optimol 2Disk test rig under mixed/boundary conditions in a factory fill SAE 0W-30 engine oil. Different factors such as influences of the lubrication, surface chemistry and wear behaviour were investigated.
Contact formation and development are the basis of friction and wear modelling and understanding. Unanimously topography formation and development in friction contacts are regarded of highest importance for understanding and modelling friction processes. The frequently found running in behaviour of sliding contacts is—aside from the build up of reaction and transfer layers-at least partly caused by the topography development due to friction processes until a stable equilibrium state is reached.
Experimental results of friction and topography measurements are presented which demonstrate the mutual modification of friction and contact topography.
A special experimental set up with an AFM allowed to correlate the measured friction forces with the contact position and the topography at this point. In this way, friction force transitions and changes can be assigned to topography changes due to abrasion, adhesion and wear particle agglomeration.
Contact surfaces with artificial regular structures have been prepared to avoid problems with topography and friction correlation due to the statistical nature of roughness on technical contact surfaces. The friction effects of roughness were simulated by etched ditches of defined width, depth and distance on silicon or metal surfaces. This allowed to explain the mutual influences of topography and friction. The effect of a single asperity and of the 'roughness structures' could be demonstrated.
Topography measurements with an AFM correlated with the friction force could help to understand friction changes without changing any parameter.
We review contact mechanics with emphasis on the rheological (time dependent) properties of polymers and their relations to surface roughness, material properties, and friction as well as wear behavior of rubbing polymer surfaces. The main concept of polymer mechanics related to tribology consists of three basic elements involved in friction: deformation resulting in the real area of contact of rough surfaces, contact adhesion, and shear and rupture of materials in the contact during the sliding friction. The results of classical work are included, which addresses the real contact area calculation and the description of adhesion interaction between rough surfaces. A brief review of experimental investigations concerning the surface characterization by means of bearing curves, the intermolecular force interaction using the adhesion parameter, the effect of temperature on the real contact area, the formation of transferred polymer film during friction, and tribological behavior of ultrathin polymer layers are presented and their implications discussed.
Adhesion measurements are presented which were carried out with an atomic force microscope between polymer balls attached to a cantilever and a silicon wafer under ultra high vacuum conditions. In using a silicon surface with a defined structure a correlation between adhesion force and contact area was found. This correlation could partly be explained by the Johnson-Kendall-Roberts model, if a change of the surface energy is assumed as a result of the structuring. For a constant geometric contact area an additional structuring leads to a decrease of the adhesion force.
A correlation of adhesion force and electrical conductivity is established for a vanadium oxide and highly oriented pyrolytic graphite (HOPG). Adhesion forces were determined by analysis of pull-off forces obtained from force–distance curves with atomic force microscopy in ultrahigh vacuum, on clean surfaces and with defined contact conditions. The investigated samples include (i) different stoichiometries of Magnéli-type vanadium oxides (V3O5, V4O7, V6O11, and V7O13), which undergo metal-insulator-transitions as a function of temperature, (ii) the (0001) basal plane and the (10–10) prism plane of highly oriented pyrolytic graphite (HOPG), which differ in their respective perpendicular-plane electrical conductivities by several orders of magnitude, and (iii) the (100) surfaces of pure metal single crystals, i.e., silver (Ag), copper (Cu), iron (Fe) and gold (Au). It is shown, that the vanadium oxides as well as the graphite exhibit significantly lower adhesion forces in their electrical conductive state than in their non-electrical conductive state. The values obtained for the electrical conductive states are quantitatively confirmed by the measurements on the single crystal metals.