In situ Acoustic Emission for wear life detection of DLC coatings during slip-rolling friction
(2006)
Different diamond-like carbon (DLC) coatings on a steel substrate (100Cr6) were tested under slip-rolling friction conditions against uncoated counter bodies of the same steel. The initial maximum Hertzian pressure was varied in a range of P0 = 1.52.3 GPa. The friction tests were carried out under dry conditions and with an unadditivated paraffin oil as lubricant. It could be shown that the thickness of the coatings affects the respective wear life. Further, a very important factor for the wear life of a coating under lubricated slip-rolling conditions is the roughness of the surface of the respective counterbody. The wear life tests were monitored by recording in situ the Acoustic Emission (AE) signals. Some causes for a high AE activity could be identified.
Paraffinöl geschmierte Wälztests wurden an extrem harten Diamantschichten auf hartem SSiC Substrat, unterschiedlichen, harten DLC-Schichten auf 100Cr6 Substraten (HRC60) sowie ausgewählten DLC-Schichten auf ungehärtetem Stahl (HRC 20) durchgeführt. Die Wälztests wurden in einem Zweischeibentribometer vom Typ Amsler bei einer anfänglichen, maximalen Flächenpressung nach Hertz von P0=2,3 GPa ausgeführt. Als Abbruchkriterium für die Tests wurde das Erreichen von n=1.000.000 Überrollungen (Langzeittests n=10.000.000 Überrollungen) oder das Auftreten einer Schädigung mit einer zusammenhängenden Fläche von A>1 mm2 festgelegt. Die Wälztests zeigten, dass das harte SSiC Substrat zwar eine stützende Wirkung auf die Diamantschicht hat, diese aber aufgrund von Rissen im Substrat versagte. Ferner gibt es wenigstens zwei DLC-Schichten, die, aufgebracht auf 100Cr6 Scheiben (HRC60), den Wälztests bis n=10.000.000 Überrollungen ohne nennenswerte Schäden widerstanden. Diese Schichten passten sich auch den Verformungen des weichen, stickstofflegierten Stahls (HRC20) an, ohne das es zu größeren Abplatzungen kam (A>1 mm2).
Diamond like carbon (DLC)-coatings are applied very successfully on computer discs. Sliding friction tests confirm their high performance as dry lubricants with friction coefficients (COFs) below 0.1. In contrast to sliding tests, until very recently most of the DLC-coatings failed in slip-rolling test after fewer cycles than uncoated samples. However, present tests with DLC-coatings of seven different suppliers show a more promising tribological behaviour under slip-rolling conditions. The DLC-coatings were deposited onto steel 100Cr6, HRC 60, with a thickness of 23 ?m. The counter bodies were uncoated, grinded or polished 100Cr6 discs with 30 mm radius of curvature. The tests were performed on a twin disc testing rig (Amsler type) with paraffin oil under boundary/mixed lubrication and rolling with 10% slip. The initial, average Hertzian contact pressure was adjusted to Pm = 1.0, 1.25, and 1.5 GPa. The failure criterion was defined as the occurrence of a single damaged area larger than 1 mm2, which was controlled by optical microscopy (OM). An acoustic emission (AE) measurement system was installed as an additional online control for coating failure. The stressed coatings and the chipping areas were analyzed by OM, SEM, EDX, AFM and Raman spectroscopy.
Until now, the results reveal that a large scatter in lifetime of coatings occurs not only between samples of different coaters but also between the samples of one single batch. The highest lifetime reached by a DLC-coating under these testing conditions is 10 × 106 cycles. That is the highest life time for a coating tested under the testing conditions above in our laboratory so far. The following factors were identified to influence the life time of the coatings: coating thickness, interlayer type, topography of the coatings, counter body roughness and mechanical properties. But the most important factor determining the life time of the coatings is that the coating process does produce homogenous layers free of faults.
Costs reduction is one of the major objectives in mechanical applications with a parallel increase of the power output. Another driver represents new environmental standards and their increasing restrictions in the automotive industry leading to the question, if materials based concepts may substitute harmful EP/AW additives in lubricants. This paper presents the slip-rolling resistance of different DLC/THC coatings on steel substrates with a definite slip rate of 10%. Industrial DLC coatings of ta-C and a-C:H types from various manufacturers were deposited on steels SAE 52100 and AMS 5898 to compile the slip-rolling resistance under initial average Hertzian contact pressures between 1.5 GPa and 2 GPa. The tests were carried out on Amsler-type twin disc tribometer under the regime of mixed/boundary lubrication in unadditivated paraffinic oil (ISO VG 46) and a factory fill engine oil. The spherical steel sample was uncoated and the cylindrical coated with DLC. Some coatings achieved 10 million cycles without any damage under a maximal Hertzian contact pressure Pmax well over 2.25 GPa, thus exceeding FZG 12.
High-power piezo-electric motors with power densities of 1.4 kW/kg display a potential for substituting hydraulic actuators. For this application, two novel tribometers of the same type have been designed using commercially available components for sliding motion at 40 kHz with amplitudes between 2.5 µm and 5 µm. The tribometers are equipped with means to measure amplitude, frequency, power required to keep the samples in motion and load applied. The effective motion between the two contacting bodies is monitored in each of the tribometers. These data are used to evaluate the coefficient of friction. The wear rate was determined after the tests. The set-ups were tested using well-known 100Cr6H (AISI 52100) samples before investigating novel, non-commercial substrates such as AlFeCrTi-alloys and tungsten carbide-based coatings as well as Magnéli-type coatings (Tin-2Cr2O2n-1 and TinO2n-1). This paper presents the principle of the ultra-high frequency tribometers and first tribological quantities of materials and coatings tested up to and above 1011 cycles. Very low wear rates in the range 10-8 mm³/Nm down to 10-10 mm³/Nm were determined under dry oscillation in air.
The light-weight approach and fuel economy targets in today's automotive engineering require tribosystems, which can withstand higher contact pressures associated with low coefficients of friction. The application of high-performance coatings represents one approach among others. This paper presents some recently developed DLC coatings (a-C:H and ta-C) as well as a novel coating-substrate system (Zr(C,N)) in a benchmark test procedure under slip-rolling conditions in the presence of liquid lubricants. Various coatings with different thickness, interlayer and substrates were evaluated for their slip-rolling resistance in different lubricants at ambient temperature and at 120 °C. Results indicate that some of these coating systems can withstand at least 10 million cycles under initial Hertzian contact pressures of up to Pmax = 3.500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions. Surface of the coatings and the counter bodies were analysed and compared with untreated substrates.
Downsizing (power-to-weight ratio) and higher speeds lead to a rise in Hertzian contact pressures in combination with an increase in surface or oil temperatures. Under such conditions, commonly used bearing steels, such as 100Cr6, reach their limits, creating a demand for alternative slip-rolling resistant steel alloys. The present work therefore compares the slip-rolling performance of various steel types with Maraging- and PM-type steel alloys such as e.g. CSS-42L™, ASP2012, BIMAX42+, in the Hertzian contact pressure range up to P0max of 4 GPa. Through-hardened 100Cr6H (AISI 52100), case-hardened 20MnCr5 (AISI 5120H) and nitrogen alloyed Croni-dur30 (AMS 5898) still compete in terms of slip-rolling and wear resistance and load carrying capacity, whereas Maraging- and PM-type steel alloys offer superior strength and toughness properties.
We review contact mechanics with emphasis on the rheological (time dependent) properties of polymers and their relations to surface roughness, material properties, and friction as well as wear behavior of rubbing polymer surfaces. The main concept of polymer mechanics related to tribology consists of three basic elements involved in friction: deformation resulting in the real area of contact of rough surfaces, contact adhesion, and shear and rupture of materials in the contact during the sliding friction. The results of classical work are included, which addresses the real contact area calculation and the description of adhesion interaction between rough surfaces. A brief review of experimental investigations concerning the surface characterization by means of bearing curves, the intermolecular force interaction using the adhesion parameter, the effect of temperature on the real contact area, the formation of transferred polymer film during friction, and tribological behavior of ultrathin polymer layers are presented and their implications discussed.
Diamond-like carbon (DLC) coatings are perceived as part of a strategy for low frictional tribosystems. Especially the automotive industry anticipates a benefit in applying such coatings in association with the lightweight construction of mechanical parts, for instance in gear and engine components. Therefore, in previous investigations amorphous carbon (a-C) and tetragonal amorphous carbon (ta-C) coatings were inspected. For up to ten million cycles at Hertzian contact pressures P0max of 2.9 GPa it was shown that these coatings are slip-rolling resistant not only at room temperature in the presence of unaddivated paraffin oil, but also up to 120 °C oil temperature. The steel substrates in this investigation were made of the hardened and tempered steels 100Cr6H and Cronidur 30. The aim of the current work is manifold. The Hertzian contact pressures should be increased up to P0max of 4.2 GPa by using new steel metallurgies as substrates for thin film coatings. These steel metallurgies are also assessed, if they can compete as uncoated couples. Two high toughness spring steels and an ultra-high toughness aerospace steel were tested in a twin disc tribometer of the Amsler type as well as in an Optimol 2Disk test rig under mixed/boundary conditions in a factory fill SAE 0W-30 engine oil. Different factors such as influences of the lubrication, surface chemistry and wear behaviour were investigated.
A correlation of adhesion force and electrical conductivity is established for a vanadium oxide and highly oriented pyrolytic graphite (HOPG). Adhesion forces were determined by analysis of pull-off forces obtained from force–distance curves with atomic force microscopy in ultrahigh vacuum, on clean surfaces and with defined contact conditions. The investigated samples include (i) different stoichiometries of Magnéli-type vanadium oxides (V3O5, V4O7, V6O11, and V7O13), which undergo metal-insulator-transitions as a function of temperature, (ii) the (0001) basal plane and the (10–10) prism plane of highly oriented pyrolytic graphite (HOPG), which differ in their respective perpendicular-plane electrical conductivities by several orders of magnitude, and (iii) the (100) surfaces of pure metal single crystals, i.e., silver (Ag), copper (Cu), iron (Fe) and gold (Au). It is shown, that the vanadium oxides as well as the graphite exhibit significantly lower adhesion forces in their electrical conductive state than in their non-electrical conductive state. The values obtained for the electrical conductive states are quantitatively confirmed by the measurements on the single crystal metals.