Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (4)
- Zeitschriftenartikel (2)
- Posterpräsentation (2)
- Buchkapitel (1)
- Beitrag zu einem Sammelband (1)
- Vortrag (1)
Sprache
- Englisch (11) (entfernen)
Referierte Publikation
- nein (11) (entfernen)
Schlagworte
- Corrosion (3)
- Alumina (2)
- Coating (2)
- Martensitic steel (2)
- Al2O3 (1)
- AlPO4 (1)
- Alpha-cordierite (1)
- Back-filling specimen mount technique (1)
- Boehmite (1)
- Cement (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating.
The suitability of an Al2O3 coating for corrosion protection on X20Cr13 was evaluated in various artificial geothermal brines, focusing on the influence of different pH (4, 6 and 8) and their chemical compositions on the coating properties. All experiments were performed in the laboratory using autoclaves at 150 ◦C and 1 MPa in deaerated condition for 1 and 7 days. Results showed that the pH of geothermal waters is the most detrimental factor in the transformation of ɣ-Al2O3 and its protective abilities. Delaminations were found in the Coating exposed to geothermal brines with pH 4. FTIR spectra indicated a transformation of ɣ-Al2O3 to boehmite AlOOH after exposure to pH 4 and 6, and bayerite Al(OH)3 was formed after exposure to pH 8. Different Crystal structures of the hydrated Al2O3 also contribute to the stability of the coatings, observed by the SEM- EDX of the surface and cross-section of coatings. This study indicated that ɣ-Al2O3 sol-gel coating presents a promising aspect of corrosion protection in geothermal environment with a neutral pH.
In order to reduce CO2 emissions fossil fuelled power stations with high combustion efficiency are being developed. The increase of the operating temperature, a common way to improve combustion efficiency, leads to enhanced corrosion of heat exchange steel tubes in the power plants. Within the framework of the European project “Production of Coatings for New Efficient and Clean Coal Power Plant Materials” (POEMA)", high temperature corrosion protection coatings are now under investigation.
Thin porous sol-gel alumina films are promising candidate coating materials. Coatings were prepared by applying boehmite sols on grinded steel P92 and subsequent heat treatments at temperatures up to 650 °C. Thus a porous layer of worm-like particles was formed consisting of nano-crystallites and amorphous alumina. A dense interface with satisfying adhesion resulted from diffusion of chromium and iron ions out of the steel into the porous coating. However, the film locally exhibited some cracks caused by steep edges in the grinded steel surface. An appropriate substrate pretreatment should avoid this problem.
The protection of the steel relies on the barrier function of the alumina coating and the formation of a dense chromia layer at the steel surface.
In order to observe the effect of the aggregate phases between 2 mm and 16 mm without overlap with rheological effects induced by the cement hy-dration and without interactions with a threshold fine sand particle size that affects both, paste and aggregates, rheological experiments were conducted on a limestone filler based paste mixed with aggregates up to 16 mm. Vari-ous aggregate fractions were blended and mixed with the replacement paste in different volumetric ratios.
The dry aggregates’ flow coefficients were determined and compared to yield stress and plastic viscosity values at different aggregate volume fractions. The results indicated that the flow coefficient is not a suitable parameter to predict the performance of the aggregates in the paste. It was shown that the yield stress of pastes is largely determined by the blend of different aggregate fractions, while the plastic viscosity to large extend depends upon the coars-est aggregate fraction.
Based on the results, ideal aggregate composition ranges for minimised yield stress are presented. For the plastic viscosity no such grading curves to achieve minimum values could be found, but high viscosity curves are identified.