Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (50)
- Beitrag zu einem Tagungsband (47)
- Vortrag (43)
- Forschungsdatensatz (17)
- Beitrag zu einem Sammelband (9)
- Forschungsbericht (6)
- Buchkapitel (5)
- Monografie (3)
- Posterpräsentation (3)
Sprache
- Englisch (111)
- Deutsch (68)
- Mehrsprachig (3)
- Portugiesisch (1)
Schlagworte
- Microstructure (16)
- Creep (14)
- Ontology (11)
- TMF (10)
- Aging (9)
- Coarsening (9)
- Fatigue (8)
- LCF (8)
- Transmission electron microscopy (7)
- Aluminium (6)
Organisationseinheit der BAM
- 5 Werkstofftechnik (92)
- 5.2 Metallische Hochtemperaturwerkstoffe (91)
- 5.5 Materialmodellierung (13)
- 9 Komponentensicherheit (12)
- 5.1 Mikrostruktur Design und Degradation (10)
- 8 Zerstörungsfreie Prüfung (10)
- 9.6 Additive Fertigung metallischer Komponenten (7)
- 8.5 Röntgenbildgebung (6)
- 9.4 Integrität von Schweißverbindungen (4)
- 8.0 Abteilungsleitung und andere (3)
Eingeladener Vortrag
- nein (43)
A material family to replace the current superalloys in aeronautical gas turbine engines is
considered to be that of gamma Titanium Aluminide (γ-TiAl) alloys. Structural components in
aeronautical gas turbine engines typically experience large variations in temperatures and multiaxial
states of stress under non-isothermal conditions. The uniaxial, torsional and bi-axial thermomechanical
fatigue (TMF) behaviour of this γ-TiAl alloy have been examined at 400 800°C with
strain amplitudes from 0.15% to 0.7%. The tests were conducted at both in-phase (IP) and out-ofphase
(OP). The effects of TMF on the microstructure were also investigated. For the same
equivalent mechanical strain amplitude uniaxial IP tests showed significantly longer lifetimes than
pure torsional TMF tests. The non-proportional multiaxial OP test showed the lowest lifetimes at
the same equivalent mechanical strain amplitude compared to the other types of tests.
In the present work, the titanium alloy Ti-6.8Mo-4.5Fe-1.5Al (Timetal LCB) was investigated with respect to the microstructural evolution during strain controlled fatigue loading. The alloy was developed to reduce the generally high material costs of β-alloys by substituting expensive beta stabilizers by using a standard Fe-Mo master alloy. One possible application seen in the automotive industry is the substitution os suspension structural parts currently made of steel, suc as suspension springs. These components require a high strength and fatigue resistance.
Mechanical properties of superheater materials after ageing and corrosion in CO2 rich flue gases
(2010)
The present work covers the mechanical behaviour of Timetal LCB under fatigue loading and utilizes transmission electron microscopy (TEM) to study the associated microstructural evolution. Fatigue specimens were taken out of LCB wire made for automotive suspension spring manufacturing in a solution treated as well as an additionally aged state. Uniaxial fatigue tests were carried out in total strain control with R = 0.1. Solution treated specimens tested at 3% and 4% maximum total strain showed a saturating force response, which differed from all other total strain controlled tests, and a distinct fracture behaviour. In addition, an increase of the dynamic Young's modulus is observed under these test conditions and in this material state. These findings are interpreted as a deformation induced precipitation of nanosize α- or ω-phase.
In the aged state, the α-phase carries the major part of deformation work, noticeable by distinct α-substructures in fatigued specimen states.
Aluminiumlegierungen mit besonders hoher Festigkeit werden vor allem in der Luft- und Raumfahrt sowie der Automobilindustrie eingesetzt. Ein Anwendungsbeispiel im Fahrzeugbereich sind Radialverdichterräder von Abgasturboladern. Der hierfür untersuchte Werkstoff ist die Legierung 2618A. Die hohe Festigkeit wird durch Ausscheidungshärtung erreicht. Es scheiden sich hierbei durch eine entsprechende Wärmebehandlung Al-Cu-Mg-Teilchen in die Aluminium-Matrix aus. Diese Teilchen stellen Hindernisse für die Bewegung von Versetzungen dar und haben im Fall der Legierung 2618A stabförmige Geometrie. Durch Einsatz bei Betriebstemperatur von etwa 160 °C bis 190 °C vergröbern die Teilchen im Verlauf der Einsatzzeit (Ostwaldreifung) und die Festigkeit nimmt ab.
Der Zwischenbericht soll einen Überblick über die bisherigen experimentellen und theoretischen Ergebnisse geben. Es konnten Brinell-Härteverläufe nach Auslagerung bei 160 °C, 180 °C und 190 °C bis 8.760 h Auslagerungszeit gemessen werden. Erste TEM (Transmissionselektronenmikroskopie )-Untersuchungen der Mikrostruktur liegen vor. Anhand dieser Untersuchungen wurden erste Simulationen und Berechnungen der AI-Cu-Mg-Teilchengrößenentwicklung (Vergröberung) durchgeführt. Auswirkungen dieser Vergröberung der AlCu-Mg-Teilchen auf die Fließgrenze bei Raumtemperatur wurden berechnet. Weitere Ergebnisse sind Kriechversuche an Proben im Ausgangszustand T61 der Legierung 2618A bei den Temperaturen 160 °C, 180 °C und 190 °C. Um das zyklische visko-plastische Verhalten des Werkstoffes und den Einfluss der Alterung zu untersuchen, wurden LCF-Ermüdungsversuche an verschiedenen Auslagerungszuständen durchgeführt.
The aluminium alloy 2618A is an Al-Cu-Mg alloy which is part of the 2xxx series of age-hardenable alloys. These materials are designed for long-term Operation in transportation and aerospace industries. The desired properties, e.g. creep behavior, hardness, and damage tolerance, are controlled by the distribution of fine precipitates formed within the matrix. However, the strength of the material declines du ring exposition to elevated temperatures due to the overageing of the S-phase precipitates (AI2CuMg) and the conversion of the S-phase into the stable equilibrium S-phase. A quantitative model of the overageing process at application relevant temperatures would be desirable for accurate predictions of component lifetime made from the 2618A alloy.
Charakterisierung des Kriechverhaltens hochwarmfester Stähle durch Versuche an Miniaturproben
(2014)
Die Einsatzbedingungen der Bauteile von fossil befeuerten Kraftwerken unterliegen derzeit durch aktuelle Entwicklungen des Energiesektors (Stichwort „Energiewende“) erheblichen Veränderungen. Während das Interesse an einer weiteren Steigerung der Wirkungsgrade und den damit verbundenen Erhöhung der Prozessdrücke und -temperaturen prinzipiell anhält, werden parallel neue Verbrennungsprozesse wie z. B. die Oxyfuelverbrennung diskutiert und die Einsatzmöglichkeiten von Ersatzbrennstoffen wie Biomasse und hochkalorischen Müllfraktionen werden untersucht.
Während diese Maßnahmen über veränderte Rauchgaszusammensetzungen ggf. zu einem generell verstärkten Hochtemperaturkorrosions-Angriff der Bauteile führen, zwingt der Ausbau der Stromerzeugung auf Basis von Wind- und Sonnenenergie die Anlagenbetreiber gleichzeitig zu einer lastflexiblen Anlagenfahrweise mit häufigen Warm- und Kaltstarts bei möglichst hohen Lastgradienten.
Diese veränderten Betriebsbedingungen stellen eine Herausforderung für die Überwachung und Instandhaltung bestehender Kraftwerke sowie für die Konstruktion neuer Anlagen und Komponenten dar.
In Germany spent nuclear fuel and high level radioactive waste is stored in interim storage containers with double lid systems. Those lids are equipped with metal seals (e.g. Helicoflex®) that ensure the safe enclosure of the inventory. The used metal seals consist of three components as can be seen in the cross-sectional view in Figure 1. The innermost part is a helical spring that is surrounded by an inner jacket made of stainless steel. The outer jacket that is made of a softer material which in case of assembly in the aforementioned storage containers is silver or aluminum (i.e. Al 99.5). During application the seal is compressed and due to the restoring force of the helical spring, the outer jacket is plastically deformed and adapts to the sealing surface. Hence, leakage paths are closed and the sealing function is generated. In Germany the above-mentioned containers are licensed for up to 40 years of interim storage, which in case extended storage becomes necessary before a final repository is available will have to be extended to even longer periods. Therefore, the evaluation of the long-term behavior of the seals is necessary, taking into account storage conditions, decay heat and possible mechanical loads as well.
At Bundesanstalt für Materialforschung und –prüfung (BAM) long-term investigations are being conducted in which seals are assembled in test flanges and aged at temperatures ranging from room temperature to 150°C for accelerated aging. The aged seals are tested semi-annually (after the first 6 months in which the seals are tested more frequently) regarding the sealing performance, the remaining seal force, and the useable resilience upon decompression. Results of these investigations have been published over the past years (e.g. Grelle, Wolff, Probst, Jaunich, & Völzke, 2017; Völzke, Wolff, Probst, Nagelschmidt, & Schulz, 2014). It was found that the seal force and the useable resilience decrease with time and temperature, which is in agreement with the result of other studies (Sassoulas et al., 2006; Wataru et al., 2016) as well. Geometry change of the outer jacket has been identified as the main reason for this seal behavior. At the prevailing operating temperatures and stresses the aluminum is subjected to creep deformation leading to a thinning of the outer jacket. Since the seal groove depth remains unchanged the helical spring expands, which in turn leads to a decrease of the generated spring and seal force.
Although the main reason for the change of seal parameters over time and temperature is known, a detailed characterization of the seal behavior and a reliable prediction of the parameter development for aging times that exceed the experimental time frame have not been possible, yet.
For deeper understanding of the aging processes, an Investigation program, which is covered in this contribution, is conducted at Bundesanstalt für Materialforschung und –prüfung (BAM) that focusses on the behavior of the aluminum jacket and its influence on the long-term sealing performance. The program investigates properties of material samples as well as the behavior of the seal as a component.
Original sheet material of the same aluminum that is used for manufacturing of the seals is investigated in compression creep tests. For this, a DMA (dynamic mechanical analysis) machine is employed (here used for static tests) that allows for a measurement of the specimens deformation under forces of up to 500 N. The advantage of this method is that the original material can be tested in the same shape as used for the seals which is 0.5 mm thick sheet material. For investigation of tensile creep standard specimens are used, that were machined from surrogate material of the same composition and annealing condition.
Furthermore, aluminum seals that are cut into smaller segments are assembled in flanges and placed in heating chambers at temperatures ranging from 23°C to 150°C. After different periods of time from 3 days to 300 days the segments are taken out of the flanges and are investigated, thus giving information on different states of aging. Measurements of the development of the seal contact width and the aluminum jacket thickness are done with an optical microscope. Further investigations on the segments will include metallography and hardness measurements.
From the detailed material and component behavior including the results of the long-term seal force and useable resilience investigations a better understanding of the overall seal behavior can be gained. The aim is to contribute to the development of material models and analytical approaches for the prediction of the sealing behavior in dependence of time and temperature.
The use of miniaturized specimen geometries in mechanical testing allows extracting the sample material directly from critical components of power plants like e.g. headers and pipes. In this way, both the impacts of the manufacture of the component (including all shaping and tempering influences) and of the complex aging/loading/oxidation conditions during Service can be analyzed and representative mechanical properties are obtained. In the present study, example results of a comparative creep and creep rupture study on P91 tempered martensite ferritic Steel, involving Standard and miniature specimens that were all taken from one batch of material, are presented. Cylindrical creep specimens with a minimum gauge length diameter of 3 mm were used, representing the smallest recommended test geometry of ISO 204. The test results of miniature specimens exhibit all characteristic creep features of tempered martensite ferritic steels, and analysis of the stress and temperature dependence of creep results in values that correspond well to literature data for P91. However, direct comparison with large scale specimen data reveals small but systematic variations in minimum creep rates, elongations at fracture and times to rupture. In our contribution, these differences are discussed in the light of literature findings on specimen size influences in other heat resistant alloys. Size effects need to be considered for a correct interpretation of results from miniature specimen creep tests.
It is widely known that the magnetic domain structure of stress-sensitive ferromagnetic materials may be altered by external or internal mechanical stresses due to magnetoelastic effects. In this contribution, localized magnetic domain changes arising from inhomogeneous deformation and multiaxial loading conditions are imaged by the Bitter method for the first time. It is demonstrated that these domain changes provide deformation-related information and thus, allow for the visualization of macroscopic strain gradients in fine-grained polycrystalline steels, while keeping a sufficient spatial resolution.
This approach has been developed within the framework of BAM-MI-project “MICRONET”.
Components in the Aerospace, Power and Automotive engineering sectors are frequently subjected to cyclic stresses induced by thermal fluctuations and mechanical loads. For the design of such components, reliable material property data are required which need to be acquired using well accepted and reproducible test procedures for thermo-mechanical fatigue (TMF) loading. There is limited availability of proven TMF data indicating there is need for further research and testing. The TMF behaviour of materials is often desired to be simulated in models which describe the cyclic stress-strain behaviour, the fatigue life and the cyclic crack growth behaviour. There is a continuous need for the development and amendment of such models. Models can be validated by using materials in industrial applications which are subjected to TMF loading.
The 3rd Workshop on Thermo-Mechanical Fatigue was held on 27–29 April 2016 at BAM, Berlin, Germany. The workshop was attended by 90 attendees coming from 17 countries in the world. 38 presentations including five poster presentations were held.
The following topics were covered by the workshop:
– TMF of materials coated with Thermal Barrier Coatings.
– Thermal Gradient Mechanical Fatigue.
– TMF crack growth.
– TMF + High Cycle Fatigue.
– TMF Modelling and Lifetime Prediction.
– TMF Properties of steels, cast iron, Al-, Mg- and Ni-alloys
– Advanced TMF Testing Techniques.
– Industrial Applications.
A panel discussion was held regarding the present state of TMF testing standards (ISO and ASTM) and their potential for improvement. The discussion and contributions were summarized and forwarded to the standard committees. The 3rd TMF-Workshop ensured the continuation of international exchange of knowledge providing a forum to present and discuss all recent developments in the field of thermo-mechanical fatigue.
The current special issue publishes eleven selected papers of the 3rd TMF-Workshop 2016. The papers were peer reviewed by a number of experts in the Thermo-Mechanical Fatigue sector. I hope you will enjoy reading papers of this special issue.
Werkstoffe im Hochtemperatureinsatz verändern mit der Zeit ihre Mikrostruktur. Mit diesem Alterungsprozess einher geht eine Veränderung der mechanischen Eigenschaften ebenso wie eine Veränderung des Schädigungsverhaltens. Im Rahmen des FVV Vorhabens „Alterung und Lebensdauer“ haben das Fraunhofer IWM in Freiburg und die BAM in Berlin die weit verbreitete warmfeste Aluminiumlegierung EN AW-2618A in verschiedenen Alterungszuständen experimentell charakterisiert und darauf aufbauend Modelle für die Lebensdauerbewertung mit der Finite-Elemente- Methode implementiert.