Filtern
Dokumenttyp
- Zeitschriftenartikel (4) (entfernen)
Sprache
- Englisch (4)
Referierte Publikation
- ja (4)
Schlagworte
- Cast iron (2)
- Axial-torsional Loading (1)
- Axial-torsional loading (1)
- Cracks (1)
- Cyclic softening (1)
- Fatigue assessment (1)
- Gamma titanium aluminide (1)
- Gamma-Titanium Aluminide (1)
- High Cycle Fatigue (HCF) (1)
- Microscopy (1)
- Microstructure (1)
- TNB-V5 (1)
- Thermo-mechanical Fatigue (1)
- Thermomechanical Fatigue (TMF) (1)
- Thermomechanical fatigue (1)
- Thermomechanical fatigue (TMF) (1)
The uniaxial, torsional and axial-torsional thermomechanical fatigue (TMF) behavior of the near-γ TiAl-alloy TNB-V5 was investigated. TMF tests were performed at 400-800 °C with mechanical strain amplitudes ranging from 0.15% to 0.7%. The tests were conducted thermomechanically in-phase (IP) and out-of-phase (OP).
For the same lifetimes, uniaxial IP tests required the highest strain amplitudes, while OP test conditions were most damaging and needed the lowest strain amplitudes. The Mises equivalent mechanical strain amplitudes of pure torsional tests were found in between uniaxial in-phase and out-of-phase tests for the same lifetimes. The non-proportional multiaxial out-of-phase test showed a lower lifetime at the same equivalent mechanical strain amplitude compared to the other types of tests.
The microstructure has been characterized applying electron microscopy and microstructural parameters such as fraction of twinned grains, grain size, lamellar distance and dislocation density have been quantified.
A material family to replace the current superalloys in aeronautical gas turbine engines is
considered to be that of gamma Titanium Aluminide (γ-TiAl) alloys. Structural components in
aeronautical gas turbine engines typically experience large variations in temperatures and multiaxial
states of stress under non-isothermal conditions. The uniaxial, torsional and bi-axial thermomechanical
fatigue (TMF) behaviour of this γ-TiAl alloy have been examined at 400 800°C with
strain amplitudes from 0.15% to 0.7%. The tests were conducted at both in-phase (IP) and out-ofphase
(OP). The effects of TMF on the microstructure were also investigated. For the same
equivalent mechanical strain amplitude uniaxial IP tests showed significantly longer lifetimes than
pure torsional TMF tests. The non-proportional multiaxial OP test showed the lowest lifetimes at
the same equivalent mechanical strain amplitude compared to the other types of tests.
Experimental and analytical investigation of the TMF-HCF lifetime behavior of two cast iron alloys
(2017)
The combined loading Thermomechanical Fatigue (TMF) with High Cycle Fatigue (HCF) has been experimentally investigated for two cast iron alloys. Both alloys contain globular graphite nodules but the first one has a ferritic structure while the second one has an austenitic crystal structure. In particular, the influences of the HCF frequency, of the HCF loading amplitude and of the location of the superposed HCF cycles have been investigated. It was observed that the HCF frequency has a limited impact on the fatigue life. On the other side, the HCF-strain amplitude has a highly non-linear influence on the fatigue life. The experimental results can be understood in terms of a fracture mechanics based damage mechanism: Cracks quickly initiate due to the TMF loading and the growth of the cracks up to a few mm controls the fatigue life. If HCF-loading cycles are superposed, cyclic crack propagation dramatically accelerates after a threshold has been reached. This threshold is regarded as controlling the fatigue life reduction. The previous ideas have been expressed in a model that can be very simply applied to estimate the fatigue life reduction ratio due to the superposed HCF cycles. It only contains two adjustable parameters and can be combined with any TMF life assessment model.
TMF tests were carried out on EN-GJSA-XNiSiCr35-5-2 at constant minimum temperature (400 °C) and varying maximum temperatures (Tmax = 700 °C, 800 °C, 900 °C) with hold times of 180 s at Tmax and two phase angles (in-phase (IP), 180° out-of-phase (OP)). The results showed a comparable strength under OP- and IP-TMF loading. At Tmax = 700 °C and 900 °C, the lifetime in IP-tests was slightly longer than that of OP-tests, while it is vice versa at Tmax = 800 °C. The IP-tests at Tmax = 900 °C showed a similar lifetime as OP-tests at Tmax = 700 °C and 800 °C, which was unexpected for such a high testing temperature. All IP-tests at Tmax = 900 °C showed a continuous cyclic softening from the beginning on, which was different from all other testing conditions. Complementary metallographic investigations indicated that under this test condition, intergranular creep damage is present in the volume of the test pieces.