This contribution presents the results of structural and compressive strength investigations on cured andhigh-temperature treated silica-based one-part geopolymer-zeolite composites. The specimens weresynthesized from two different silica sources, sodium aluminate and water. The phase content as well asthe compressive strength of the cured composites varied depending on the starting mix-design and thesilica feedstock. Besides geopolymeric gel, A-type zeolites and hydrosodalites were the major reactionproducts. One of the silica feedstocks yielded significantly higher compressive strength (19 MPa), whilethe other one appears to cause less variation in phase content. Strength testing indicated an improvementon heating up to
200–400 °C (28 MPa) followed by a moderate decrease up to 700 °C. Above 700 °C the sys-tems underwent new phase formation and shrinkage (volume decrease) deformations. After exposureat 1000 °C the different mixes consisted of a mix of several stuffed silica phases, almost pure hexago-nal nepheline or amorphous phase. Depending on the mix-design, the onset temperature of the hightemperature phase transformations varied.
The production of Portland cement causes a substantial environmental impact, since the calcination of limestone results in high emissions of carbon dioxide. The use of supplementary cementitious materials such as calcined clays as partial replacement for Portland cement offers a solution to limit this environmental impact. This paper investigates four clays from deposits in central Germany with the aim of obtaining pozzolans for the production of Portland-pozzolana cement. The results obtained show that the calcined clays possess pozzolanic properties, which differ depending on calcination temperature and the relative amounts of Kaolinite and 2:1 clay minerals.