Poly(p-phenylenediamine) (PpPD)/carboxylic acid-functionalized multiwalled carbon nanotubes (c-MWCNTs) nanocomposites were prepared by chemical oxidative polymerization using potassium persulfate (K2S2O8) as an oxidant. Field-emission scanning electron microscopy (FE–SEM) and field-emission Transmission electron microscopy (FE–TEM) showed that a tubular layer of PpPD was coated on the surface of carbon nanotubes with a thickness of 10–20 nm. FT–IR analysis provided an evidence for the formation of nanocomposites. The thermal stability of nanocomposites was improved by addition of c-MWCNTs as confirmed by thermogravimetric analysis (TGA). XRD spectra showed that the crystalline nature of PpPD was not affected much by the addition of c-MWCNTs. As the content of c-MWCNTs was increased, the electrical conductivity of the nanocomposites increased due to the interaction between polymer and nanotubes that enhances electron delocalization.
The symmetry or structural stability of ABO3-type perovskite oxides depends largely on the size of ‘A’ and ‘B’ cations, which determines the material properties. The partial substitution of these cations may be used to tune these properties. The ionic sizes and valence states of the cations play an important role in improving the prop- erties of perovskite. In this study, the substitution of La3+ with Sr2+ with a larger ionic radius and Mn3+ with Fe3+ with a similar ionic radius favored both the crystal symmetry and the mixed ionic–electronic conductivity of the perovskite. Electrodes based on La0.7Sr0.3Mn0.5Fe0.5O3 (LSMFO55) exhibited a faradaic behavior with a specific capacity of 330 C g−1 (92 mAh g−1 ) at 12C rate, while this electrode maintained a capacity of 259 C g−1 at 240C (charge or discharge in 15 s). Additionally, exohedral carbon nano-onions (CNO) were introduced as a negative electrode to design an asymmetric hybrid supercapacitor (AHS) with a widened cell voltage. The use of CNO as a negative electrode in the AHS improved the rate capability drastically compared to the use of rGO. This device maintained a good energy density even at an extra-high charging rate (600C) owing to its outstanding rate capability. The high-rate performance of the LSMFO55//CNO AHS can be elucidated by successful fabrication with a mixed ionic–electronic conductive positive electrode and a CNO negative electrode. Tuning the electronic and ionic conductivities by cationic substitution and adopting an appropriate carbon-derived negative electrode (such as CNO) can provide a practical high-rate hybrid device using various perovskites.
The continual increase in energy demand and inconsistent supply have attracted attention towards sustainable energy storage/conversion devices, such as electrochemical capacitors with high energy densities and power densities. Perovskite oxides have received significant attention as anion-intercalation electrode materials for electrochemical capacitors. In this study, hollow nanospheres of nonstoichiometric cubic perovskite fluorides, KNi1-xCoxF3-delta (x = 0.2; delta = 0.33) (KNCF-0.2) have been synthesized using a localized Ostwald ripening. The electrochemical performance of the non-stoichiometric perovskite has been studied in an aqueous 3 M KOH electrolyte to categorically investigate the fluorine-vacancy-mediated charge storage capabilities. High capacities up to 198.55 mA h g-1 or 714.8 C g-1 (equivalent to 1435 F g-1) have been obtained through oxygen anion-intercalation mechanism (peroxide pathway, O-). The results have been validated using ICP (inductively coupled Plasma mass spectrometry) analysis and cyclic voltammetry. An asymmetric supercapacitor device has been fabricated by coupling KNCF-0.2 with activated carbon to deliver a high energy density of 40 W h kg-1 as well as excellent cycling stability of 98 % for 10,000 cycles. The special attributes of hollow-spherical, non-stoichiometric perovskite (KNCF-0.2) have exhibited immense promise for their usability as anion-intercalation type electrodes in supercapacitors.
The use of a biocompatible and thermoresponsive polymer, poly (2-hydroxyethyl methacrylate) (PHEMA) grafted onto the surface of graphene oxide (GO) as an adsorbent for the removal of a cationic dye (methylene blue [MB]) from an aqueous solution is examined in this work. GO–PHEMA forms a hydrogel in water thus overcoming the problem faced by carbon-based adsorbent materials during post-treatment (i.e., separation of adsorbent from the aqueous phase). The GO–PHEMA composite was synthesized using a green approach through dispersion polymerization in supercritical CO2. The successful preparation of this composite was confirmed by a series of characterization techniques. The adsorption behavior of the composite toward MB, such as the effect of the adsorbent dosage, pH, contact time, dye concentration, and recyclability was observed. In addition, the adsorption isotherm, kinetics and thermodynamics were investigated. According to the experimental data, the adsorption parameters were found to fit well into the Freundlich adsorption isotherm with a correlation coefficient of 0.975 and a maximum predicted adsorption capacity of 39.41 mg g−1 at 25 °C. The adsorption kinetics studies showed that the adsorption behavior followed a pseudo-second-order reaction. On the other hand, the thermodynamics studies showed that the adsorption of MB on GO–PHEMA composite followed spontaneous and endothermic adsorption process with an efficient adsorption temperature at 45 °C. The experimental results also showed that the GO–PHEMA composite could remove 99.8 % of the dye in 45 min. Therefore, GO–PHEMA composite is a favorable green adsorbent for environmental applications.
With the vast exploration of the applications of graphene, researchers are assessing different methods for fabricating graphene-based electrode material with high capacitance but low material and energy costs. In this study, reduced graphene oxide/nickel oxide (RGO/NiO) nanocomposites were prepared using a non-aqueous solvent-based method followed by calcination. Nickel acetate tetrahydrate and tert-butanol were used as the precursor and solvent, respectively. Ultrasmall nickel oxide nanoparticles, ca. 8.0 nm in size, were deposited on the surface of the graphene sheets simultaneously with the partial reduction of graphene oxide. The resulting RGO/NiO electrode exhibited a high capacitance of 689 F g⁻1 at a current density of 0.8 A g⁻1. After 1500 cycles, the specific retention and the coulombic efficiency yielded to 86.34% and 96.39%, respectively, which supports the viability of this composite as an alternative activated material with high electrochemical performance.
The solubility of carbon dioxide in three ionic liquids (ILs) under supercritical fluid condition was measured at pressures up to 32 MPa and at temperatures of 313.15, 323.15, and 333.15 K in a high-pressure view cell. The imidazolium-derivative ionic liquids 1-butyl-3-methylimidazolium hexafluorophosphate ([bmim][PF6]), 1-butyl-3-methylimidazolium tetrafluoroborate ([bmim][BF4]), and 1-octyl-3-methylimidazolium tetrafluoroborate ([omim][BF4]) were employed in this research. The effects of pressure, temperature, nature of anion and cation as well as the water content on the solubility of CO2 in the ILs were investigated experimentally. The solubility of CO2 in the IL was higher for the ILs with longer cationic alkyl group and for the ILs with lower anion polarity. The lower the water content or the lower the temperature as well as the higher the pressure, the higher was the solubility of CO2.
Nanocomposites of Ag-ZnFe2O4@reduced graphene oxide (rGO) were synthesized using a one-pot microwave-assisted self-assembly method. The morphology and structure of the Ag-ZnFe2O4@rGO nanocomposites were characterized. The nanocomposites formed with 15.2 wt% rGO showed excellent adsorption properties and high photocatalytic activity for the degradation of methylene blue (MB), rhodamine B (RhB), and methyl orange (MO). The synergistic interactions between Ag, ZnFe2O4, and rGO decreased the aggregation of the nanoparticles (NPs) and increased the surface area, resulting in better absorption in both UV and visible light. Such a structure was helpful for separating the photoexcited electron-hole pairs and accelerating electron transfer. Electrochemical impedance spectroscopy (EIS) revealed a smaller resistance in the solid-state interface layer and charge transfer on the composite surface than that of the bare ZnFe2O4 NPs and ZnFe2O4@rGO nanocomposite. The Ag-ZnFe2O4@rGO nanocomposite could be recovered easily by a magnet and reused five times with no significant decrease in photocatalytic activity. The as-prepared Ag-ZnFe2O4@rGO nanocomposite catalyst could be applied to the removal of hard-to-degrade waste materials owing to its high efficiency in both UV and visible light and its excellent reusability.
Metal oxide/graphene photocatalysts have been attracting considerable attention in solving environmental pollution problems because of the limitations of the semiconductor-based photocatalysts. In this study, highly efficient and inexpensive zinc oxide (ZnO) nanoparticles with three different morphologies, such as nanospheres, nanodisks, and nanorods, anchored on reduced graphene oxide (RGO) were synthesized in solvent mixtures with different ethanol to water ratios. Among the three morphologies, the nanospherical ZnO/RGO (sZG) Composite exhibited the highest methylene blue (MB) and rhodamine B removal efficiencies at 99% and 98%, respectively, after only 60 min under low-power (40 W) ultraviolet irradiation at a low catalyst loading of 0.1 g L−1. This nanocomposite also showed excellent photocatalytic stability under UV irradiation, retaining 96% Efficiency even after 15 cycles of MB degradation. Moreover, the sZG composite exhibited a high MB degradation Efficiency of approximately 99% after 100 min at a low catalyst loading of 0.2 g L−1 under solar light illumination. The
excellent photocatalytic performance and high stability of this low-cost nanospherical ZnO/RGO Composite exemplarily highlights the potential of sustainable next-generation photocatalysis for treating wastewater containing organic pollutants.
A hybrid nanocomposite of magnetic nanoparticles (Fe3O4) and poly(2-hydroxyethyl methacrylate)-blockpoly(methyl methacrylate) (PHEMA-b-PMMA) was synthesized successfully by the atom transfer radical polymerization (ATRP) in an ionic liquid (IL), 1-butyl-3-methylimidazolium hexafluorophosphate ([Bmim]PF6). Fe3O4 nanoparticles were first surface-modified with the initiator, 2-bromoisobutyryl bromide (BiBBr), in dimethylformamide (DMF) solvent, which produced the macro-initiator, Fe3O4-BiB, to initiate the polymerization reactions for the synthesis of the block polymer, PHEMA-b-PMMA. After immobilizing the Initiator on the surface of Fe3O4, the block polymer chains were grafted successfully onto the Fe3O4 surface, causing the Formation of a core-shell nanostructure. The incorporation of Fe3O4 in the nanocomposite was confirmed by attenuated total reflectance-Fourier transform infrared spectroscopy, X-ray diffraction, transmission electron microscopy, thermogravimetric analysis, and X-ray photoelectron spectroscopy. The thermal stability and magnetic properties increased with increasing amount of Fe3O4 in the nanocomposite.