Filtern
Dokumenttyp
- Zeitschriftenartikel (33)
- Posterpräsentation (9)
- Vortrag (8)
- Beitrag zu einem Tagungsband (3)
Schlagworte
- Additive manufacturing (13)
- Laser powder bed fusion (8)
- Residual stress (7)
- Additive Manufacturing (5)
- AlSi10Mg alloy (4)
- X-ray refraction (4)
- AlSi10Mg (3)
- Computed tomography (3)
- EBSD analysis (3)
- Electron backscatter diffraction (EBSD) (3)
- Fatigue crack growth (3)
- In situ heating (3)
- Laser Powder Bed Fusion (3)
- Neutron diffraction (3)
- Residual Stress (3)
- Residual stress analysis (3)
- Creep (2)
- Diffraction (2)
- Diffraction elastic constants (2)
- Digital image correlation (DIC) (2)
- Electron backscatter diffraction (2)
- Fatigue crack propagation (2)
- Heat treatment (2)
- IN718 (2)
- Inconel 718 (2)
- LPBF (2)
- Residual stress state (2)
- Residual stresses (2)
- Sintering (2)
- Synchrotron X-Ray Refraction (2)
- Synchrotron refraction radiography (2)
- Texture (2)
- Thermally induced porosity (2)
- A357-T6 cast aluminum alloy (1)
- A357-T6 casting (1)
- AGIL (1)
- AISI 316L (1)
- AM IN718 (1)
- AM IN718 alloy (1)
- Al-3.85%Mg alloy (1)
- Aluminium alloys (1)
- Aluminum alloy (1)
- Analyzer-based imaging (1)
- As-built LPBF IN718 alloy (1)
- Bench braking sequence (1)
- Bragg-edge neutron 2D imaging (BENI) (1)
- Braking load history (1)
- Bulk properties ageing (1)
- Cellular structures (1)
- Ceramics (1)
- Ceria (1)
- Components influence (1)
- Composite (1)
- Composites (1)
- Compression testing (1)
- Compressive test (1)
- Computed Tomography (1)
- Crack initiation period (1)
- Cracks (1)
- Crystal plasticity finite element modeling (CPFEM) (1)
- Crystallographic descriptor (1)
- Crystallographic texture control (1)
- Cyclic R-curve (1)
- DIC assisted compression (1)
- Damage characterization (1)
- Damage tolerance (1)
- Denoising filter (1)
- Diffraction methods (1)
- Diffraction peak width (1)
- Diffraction-elastic constants (1)
- Diffusion (1)
- Digital image correlation (1)
- Dislocation-climb-controlled creep (1)
- Dislocations (1)
- Distortion (1)
- Distortion upon baseplate removal (1)
- Effect of scanning strategies (1)
- Electron microscopy (1)
- Energy dispersive X Ray diffraction (1)
- Ernel average misorientation (KAM) (1)
- Evolution of bulk properties (1)
- Fatigue performance (1)
- Fractals (1)
- Fractographic observations (1)
- Friction braking (1)
- Geometric descriptor (1)
- Graphite induced hysteresis (1)
- Hystersis (1)
- IN718 PBF-LB/M (1)
- Imaging (1)
- In situ testing (1)
- In-situ (1)
- In-situ heat treatment (1)
- Interfaces (1)
- Interphase residual stress (1)
- Keramik (1)
- Kernel average misorientation (1)
- L-PBF (1)
- L-PBF IN718 material (1)
- Laboratory XµCT (1)
- Laboratory energy-dispersive X-ray diffraction (EDXRD) (1)
- Laminated metal composite (1)
- Laminated metallic composites (1)
- Laser Beam Melting (1)
- Laser Powder Bed Melting (1)
- Laser beam melting (1)
- Laser powder bed fusion (LPBF) (1)
- Laser-based additive manufacturing (1)
- Load history (1)
- Macroscopic stress (1)
- Mechanical behavior (1)
- Metal additive manufacturing (MAM) (1)
- Metal matrix composite (1)
- Metallic matrix pad (1)
- Microstructural evolution (1)
- Microstructure (1)
- Microstructure and texture (1)
- Monoclinic to tetragonal transformation (1)
- Near-surface X-ray diffraction (1)
- Neutron Diffraction (1)
- Neutron and X-ray diffraction (1)
- Neutrons diffraction (1)
- Nickel-based superalloys (1)
- Nonlinear stress-strain curve (1)
- Online Process Monitoring (1)
- PBFLB/M AlSi10Mg alloy (1)
- Phase transformation (1)
- Plasticity (1)
- Pore size (1)
- Porosity growth (1)
- Post processing heat treatment (1)
- Powder analysis (1)
- Powder metallurgy (1)
- Power law and power-law breakdown (1)
- Power-law breakdown (1)
- Propagation modes (1)
- Pure aluminium (1)
- Qquantification and segmentation (1)
- Re-entrant surface feature (1)
- Refractory (1)
- Refractory zirconia (1)
- Residual stress in AM (1)
- Residual stress measurements (1)
- Röntgen-Refraktion (1)
- SIF evaluation (1)
- Scan strategies (1)
- Scan strategy influence (1)
- Scanning electron microscopy (1)
- Scanning electron microscopy (SEM) (1)
- Selective laser melted materials (1)
- Semi-metallic brake-pad material (1)
- Semi-metallic friction material (1)
- Semi-metallic sintered material (1)
- Si network disintegration (1)
- Stainless Steel (1)
- Statistical image analysis (1)
- Statistically relevant volumes (1)
- Steady-state creep (1)
- Stiffness (1)
- Strain-free lattice references (1)
- Strain-free lattice spacing (1)
- Stress balance (1)
- Stress balance condition (1)
- Stress-relief heat-treatments (1)
- Surface roughness analysis (1)
- Synchrotron Energy Dispersive Diffraction (1)
- Synchrotron X-ray computed tomography (1)
- Synchrotron X-ray diffraction (1)
- Synchrotron X-ray diffraction (SXRD) (1)
- Synchrotron X-ray refraction (1)
- Synchrotron X-ray refraction radiography (1)
- Synchrotron computed tomography (1)
- Synchrotron refraction (1)
- Synchrotron tomography (1)
- Tensile testing (1)
- Thermally induced microcracking (1)
- Thermally induced porosity (TIP) (1)
- Thermography (1)
- Ti-6Al-4V (1)
- Tiatanium (1)
- Torsional fatigue (1)
- Torsional in situ fatigue testing (1)
- Toughening mechanism (1)
- Toughening mechanisms (1)
- Uniaxial compression tests (1)
- Verbundwerkstoffe (1)
- Wear resistance (1)
- X-Ray refraction (1)
- X-ray Diffraction (1)
- X-ray analysis (1)
- X-ray and Neutron Diffraction (1)
- X-ray and neutron diffraction (1)
- X-ray synchrotron tomography (1)
- Zirconia (1)
- pure aluminum (1)
- subgrain (1)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (53)
- 8.5 Röntgenbildgebung (53)
- 9 Komponentensicherheit (15)
- 9.4 Integrität von Schweißverbindungen (14)
- 5 Werkstofftechnik (5)
- 5.1 Mikrostruktur Design und Degradation (3)
- 5.2 Metallische Hochtemperaturwerkstoffe (2)
- 8.0 Abteilungsleitung und andere (2)
- 9.0 Abteilungsleitung und andere (2)
- 9.6 Additive Fertigung metallischer Komponenten (2)
- 5.0 Abteilungsleitung und andere (1)
- 9.3 Schweißtechnische Fertigungsverfahren (1)
Eingeladener Vortrag
- nein (8)
X-ray refraction is analogous to visible light deflection by matter; it occurs at boundaries between different media. The main difference between visible light and X-rays is that in the latter case deflection angles are very small, from a few seconds to a few minutes of arc (i.e., the refraction index n is near to 1). Trivially but importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks and quantify their densities in bulk (not too heavy) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, their detectability is simply limited by the wavelength of the radiation.
We thereby show the application of X-ray refraction 2D mapping (topography) and tomography to different sorts of problems in materials science and technology: 1) Sintering of SiC green bodies; 2) Porosity analysis in additively manufactured alloys; 3) Fiber de-bonding in metal and polymer matrix composites.
Such techniques, especially at the Synchrotron BESSY II, Berlin, Germany, can be used in-situ, i.e. when the specimen is subjected to temperatures or external loads. Applications of in-situ X-ray refraction radiography on aluminum alloys and composites are also shown.
The use of X-ray refraction analysis yields quantitative information, which can be directly input in kinetics, mechanical and damage models.
This study is shown as an example of the potential of synchrotron X-ray refraction technique to determine the evolution of damage in brittle (microcracked) materials. The strength of X-ray refraction resides in its high detectability of features (e.g., cracks, pores) within large volumes, enabling a macroscopic characterization of the microstructure. The case study is a Zirconia-based cast refractory, which is aimed to function at high temperatures (even in excess of 1700°C) in industrial furnaces to enable the production of special glasses. Therefore, this material must withstand severe in-service conditions (both thermomechanical and chemical). X-ray refraction technique is used to monitor the microcracking evolution of the material, which was previously subjected to thermal cycles (crossing the martensitic phase transformation around 1000°C) at two different stress levels.
The manufacturability of metallic alloys using laser-based additive manufacturing methods such as laser powder bed fusion has substantially improved within the last decade. However, local melting and solidification cause hierarchically structured and crystallographically textured microstructures possessing large residual stress. Such microstructures are not only the origin of mechanical anisotropy but also pose metrological challenges for the diffraction-based residual stress determination. Here we demonstrate the influence of the build orientation and the texture on the microstructure and consequently the mechanical anisotropy of as-built Inconel 718. For this purpose, we manufactured specimens with [001]/[011]-, [001]- and [011]/[111]-type textures along their loading direction. In addition to changes in the Young’s moduli, the differences in the crystallographic textures result in variations of the yield and ultimate tensile strengths. With this in mind, we studied the anisotropy on the micromechanical scale by subjecting the specimens to tensile loads along the different texture directions during in situ neutron diffraction experiments. In this context, the response of multiple lattice planes up to a tensile strain of 10% displayed differences in the load partitioning and the residual strain accumulation for the specimen with [011]/[111]-type texture. However, the relative behavior of the specimens possessing an [001]/[011]- and [001]-type texture remained qualitatively similar. The consequences on the metrology of residual stress determination methods are discussed.
The triaxial distribution of the residual stress in laser powder bed fused austenitic steel 316L was determined by X-ray and neutron diffraction. The residual stress analysis results were linked to the thermal history of the specimens, which were manufactured with varying inter-layer-times and scanning velocities. A clear link between the in-process temperature of the specimens and the residual stress was found, based on in-situ monitoring data.
The stress-induced tetragonal to monoclinic (t-m) zirconia phase transformation can provide a certain degree of plasticity to Ceria-stabilized (Ce-TZP) zirconia-based composites. Characterizing and monitoring this phase transition on a millimeter-size range, within the bulk and in-situ remains a challenge. In this work, the mechanical behavior of Ce-TZP based composite was studied in tension, combining microscopy and synchrotron Xray refraction techniques. In contrast with microscopy methods, which only provide surface information, X-ray refraction radiography (SXRR) allowed the visualization of all the transformation bands, over the entire length and thickness of tested specimens, opening up new avenues for in-situ stress-induced t-m transformation studies.
Toughening mechanisms and enhanced damage tolerant fatigue behaviour in laminated metal composites
(2022)
In the present study, fatigue crack growth (FCG) in a laminated metal composite (LMC) consisting of Al-based constituents with dissimilar strength was studied. Additionally, the FCG in both monolithic constituent materials was determined and a linear elastic rule of mixture (ROM) concept was calculated as a reference for the FCG of the laminated composite. Crack networks in the laminates were analyzed post-mortem by means of light microscopy and synchrotron X-Ray tomography (SXCT). Significantly reduced FCG rates for the LMC were found at elevated stress intensity ranges compared to both the monolithic constituents as well as the ROM concept. This is the result of the formation of a complex 3D crack network in the laminated architecture caused by the appearance of the two different toughening mechanisms a) crack deflection and b) crack bifurcation at the vicinity of the interfaces.
The mechanisms controlling the fatigue response of an A357-T6 cast aluminium alloy under cyclic torsional loading are investigated. Surface crack monitoring coupled with Electron BackScattering Diffraction (EBSD) analysis is used to study crack initiation. Determination of S-N curve combined with interrupted in situ fatigue testing using synchrotron tomography allows the study of the propagation behaviour. It is observed that fractographic morphologies depend on the stress level. At intermediate-low stress levels ( τmax < 100 MPa), the grain structure controls the crack initiation and propagation periods. Cracks are usually nucleated in mode II from slip planes close to the specimen axis or perpendicular to it. Mode II crack growth dominates the early stages of crack propagation as mode III inward crack growth is rapidly decelerated. This behaviour leads to the formation of characteristic shallow surface cracks. Once the crack is long enough for the mode II driving force to be overtaken by mode III, propagation branches into ~45 ◦mode I.
The stress–strain behavior of ceramics, such as aluminum titanate, has certain features that are unusual for brittle materials—in particular, a substantial nonlinearity under uniaxial tension, and load–unload hysteresis caused by the sharp increase of the incremental stiffness at the beginning of unloading. These features are observed experimentally and are attributed to microcracking. Here we compare different degrees of stress–strain nonlinearity of aluminum titanate materials and quantitatively model them. We use advanced mechanical testing to observe the mechanical response at room and high temperature; electron microscopy, and X-ray refraction radiography to observe the microstructural changes. Experiments show that two types of microcracks can be distinguished: (i) microcracks induced by cooling from the sintering temperature (due to heterogeneity and anisotropy of thermal expansion), with typical sizes of the order of grain size, and (ii) much larger microcracks generated by the mechanical loading. The two microcrack types produce different effects on the stress–strain curves. Such microcracks and the features of the stress–strain behavior depend on the density of the cooling-induced microcracks and on the distribution of grain sizes. They are modeled analytically and numerically.
The effect of two types of scanning strategies on the grain structure and build-up of Residual Stress (RS) has been investigated in an as-built IN718 alloy produced by Laser Powder Bed Fusion (LPBF). The RS state has been investigated by X-ray diffraction techniques. The microstructural characterization was performed principally by Electron Backscatter Diffraction (EBSD), where the application of a post-measurement refinement technique enables small misorientations (< 2°) to be resolved. Kernel average misorientation (KAM) distributions indicate that preferably oriented columnar grains contain higher levels of misorientation, when compared to elongated grains with lower texture. The KAM distributions combined with X-ray diffraction stress maps infer that the increased misorientation is induced via plastic deformation driven by the thermal stresses, acting to self-relieve stress. The possibility of obtaining lower RS states in the build direction as a consequence of the influence of the microstructure should be considered when envisaging scanning strategies aimed at the mitigation of RS.