Time dependence of y/y' Lattice Mismatch in Creep-deformed Single Crystal Superalloy SC16 at 1173 K
(2007)
High-resolution diffraction using synchrotron x-ray radiation was applied to study γ´ precipitates with an L12 superlattice crystal structure in the single crystal superalloy SC16 after creep deformation at 1223 K with a creep strain of ±0.5% for tensile and compressive loads, respectively. The measurements of full width at half maximum (FWHM) of 001 and 100 γ´ superlattice reflections were performed at various temperatures from ambient temperature to 1173 K in vacuum. The experimental results revealed that the FWHM of both reflections decrease with increasing temperature. It is well-known that changes in particle size and lattice distortion in materials could lead to a variation of FWHM. The observed behaviour is discussed in the light of both the above-mentioned aspects. The decrease in the peak width is mainly attributed to the temperature dependence of the internal strain state.
This work presents an X-ray absorption spectroscopy study on a single-phase state of the Al8Cr17Co17Cu8Fe17Ni33 compositionally complex alloy, focused on the local crystal structure around each alloying element. The comparison of 1st shell bond lengths, obtained by the analysis of extended X-ray absorption fine structure (EXAFS) measured at the K-edges of each alloying element, indicates that Al8Cr17Co17Cu8Fe17Ni33 crystallizes in a distorted arrangement of an fcc lattice. A modest bond length dependence of the alloying elements with increasing atomic number is observed, with minima and maxima at Cr/Co, and Al/Cu, respectively. 1st shell bond lengths spread over ~0.03 Å; consequently, such variations cannot result in lattice distortions greater than ~0.04 Å. EXAFS results clearly indicate short-range order in the alloy: pairing of Al with Ni and Cu is favored, correlating well with a g’ precipitate composition (Al-Ni-Cu rich) reported in previous work, while Al-Cr bonding is unfavored and no Al-Al pairs are observed. Electronic structure information was obtained through comparison between near-edge regions of alloying Elements and corresponding pure metals. Intensity comparison of K-edge features agree with a charge variation of p states in Al8Cr17Co17Cu8Fe17Ni33, where Ni and Cu act as p states electron acceptors, suggesting an orbital hybridization with Al, responsible for a shrinkage in Al metallic radius in the alloy by 0.17 Å.
We present transmission electron microscope (TEM) tomography investigations of ruthenium-based fuel cell catalyst materials as employed in direct methanol fuel cells (DMFC). The digital three-dimensional representation of the samples not only enables detailed studies on number, size, and shape but also on the local orientation of the ruthenium particles to their support and their freely accessible surface area. The shape analysis shows the ruthenium particles deviate significantly from spherical symmetry which increases their surface to volume ratio. The morphological studies help to understand the structure formation mechanisms during the fabrication as well as the high effectiveness of these catalysts in the oxygen reduction reaction at the cathode side of fuel cells.
This article reports a comprehensive investigation of the average and local structure of La5.6WO12-δ, which has excellent mixed proton, electron and oxide ion conduction suitable for device applications. Synchrotron X-ray and neutron powder diffraction show that a cubic fluorite supercell describes the average structure, with highly disordered lanthanum and oxide positions. On average, the tungsten sites are sixfold coordinated and a trace [3.7 (1.3)%] of anti-site disorder is detected. In addition to sharp Bragg reflections, strong diffuse neutron scattering is observed, which hints at short-range order. Plausible local configurations are considered and it is shown that the defect chemistry implies a simple 'chemical exchange' interaction that favours ordered WO6 octahedra. The local model is confirmed by synchrotron X-ray pair distribution function analysis and EXAFS experiments performed at the La K and W L-3 edges. It is shown that ordered domains of similar to 3.5 nm are found, implying that mixed conduction in La5.6WO12-δ is associated with a defective glassy-like anion sublattice. The origins of this ground state are proposed to lie in the nonbipartite nature of the face-centred cubic lattice and the pairwise interactions which link the orientation of neighbouring octahedral WO6 sites. This 'function through frustration' could provide a means of designing new mixed conductors.
Local structures of amorphous and quasicrystalline phases in Zr–Ti–Ni and Zr–Ti–Ni–Cu alloys have been studied by means of x-ray absorption spectroscopy. The amorphous phases show a high degree of icosahedral short-range order. In all investigated systems local order around Cu and Ni atoms was found to be nearly identical pointing to site substitution of Ni by Cu as the reason for an improved glass forming ability when Ni is partly substituted by Cu. The results strengthen an icosahedral cluster based approach for the structure of metallic glasses and indicate the importance of the medium-range order on glass formation.