Scanning force microscopy (SFM) has been used to assess the local mechanical properties of fibre-reinforced polymers. Using a sinusoidal displacement modulation (DM) and lock-in technique the method allows to characterize local viscoelastic properties with a high lateral resolution. The simultaneous measurement of the local electrical conductivity is proposed which facilitates the interpretation of the mechanical data. The investigation of cross-sections perpendicular to the axis of carbon fibres embedded in PPS delivers some information about the change in local stiffness within the interfacial region. As a first approach, assuming a single-exponential decrease in local stiffness along a radial line from fibre to polymer we find characteristic decay lengths which are distributed in a range between 20 and 80nm. Further, a modified DM-mode is proposed which is expected to provide a contrast enhancement of the signal which is related to local stiffness. This can be achieved by installing an additional feedback loop which keeps constant the amplitude of dynamic indentation (CDI-mode).
The physical properties as well as the thickness of the interphase between polymer and reinforcing phase are generally expected to show a strong influence on the macroscopic mechanical properties of composite materials. In this study the scanning force microscope (SFM) has been applied for detecting stiffness gradients near the interface between copper and epoxide. In displacement modulation mode the load exerted by the tip is modulated sinusoidally by vibrating the normal position of the cantilever or the sample. The corresponding amplitude of dynamic cantilever bending is related to local surface stiffness. Thus, using the SFM, the local mechanical properties of the surface under investigation can be probed. When scanning the tip across the reinforcement/polymer interface, the polymeric interphasial zone can be identified with the observed stiffness gradient. For a commercial epoxide based on diglycidyl ether of bisphenol A (DGEBA) cured with an amine-containing hardener, a stiffness gradient was detected that could be fitted by a Gaussian profile typical for diffusional processes. The width of the stiffness gradient was 280 nm. The observation is discussed in terms of interface-induced segregation processes between resin and hardener, as well as heat conduction mechanisms that can occur during the exothermic curing reaction. Both mechanisms are diffusional in nature and, via the local network structure, are expected to show some influence on the local stiffness of the cured epoxy. Copyright © 2000 John Wiley & Sons, Ltd.
Poly(methyl methacrylate) (PMMA) surfaces have been modified by dynamic plowing lithography. The resulting modified structures, presenting regions of different densities and stiffnesses, have been studied by forcedisplacement curves. The elasto-plastic response, the stiffness, and the adhesion of the modified samples have been characterized. Forcedisplacement curves are able to distinguish between unmodified PMMA and two different structures resulting from the lithography, i.e. compressed PMMA and low density PMMA. In particular, the low density regions are made up of cluster-like globular particles, whose elasto-plastic response and adhesion are measured and whose contribution to the total elasto-plastic response and to the adhesion has been studied in detail.
The fracture toughness in the fiber-matrix composite by means of the single fiber pull-out test can be achievable, if it is possible to measure the compliance of partial debonded fiber, which necessitates a stable crack propagation and the determination of the corresponding crack length. A combination of high stiff test equipment and a simultaneous monitoring of the photo-elastic pattern of the embedded fibers with the help of polarization microscope enables to measure crack length and determination of Gc [Hampe, A and Marotzke, C. (1997). The Energy Release Rate of the Fiber/Polymer Matrix Interface: Measurement and Theoretical Analysis, J. Reinf. Plast. and Compo., 16: 341-352.]. This method is well-known for glass fiber-amorphous polymer composite. In this investigation, we tried to implement the same technique to C-fiber with amorphous and semi-crystalline polymer composites. The energy release rate (ERR) of the fiber-matrix interface was evaluated for the carbon fiber-reinforced in polycarbonate (PC) by interfacial crack propagation arising in the single fiber pullout test. Further, the crack propagation at the fiber-matrix interface with different matrix morphology was discussed with the use of photo-elastic pattern observed with the aid of polarization microscope.
Die in zunehmenden Maße Mitte der 80er Jahre einsetzende Substitution von metallischen Materialien z. B. durch hochleistungsfähige polymere Werkstoffe und Verbundwerkstoffe wurde u. a. von der DGM zum Anlass genommen, ihre zukünftigen Aufgaben neu zu definieren und gleichzeitig mit der Gründung des Fachausschusses "Gefüge und Eigenschaften von Polymerwerkstoffen" dieser neuen Entwicklung in der Materialkunde auf dem Gebiet der Kunststoffe und ihrer Anwendungen Rechnung zu tragen.
The effect of transcrystallinity in carbon fiber reinforced poly(p-phenylene sulfide (PPS) composites on the apparent shear strength was investigated with the single fiber pull-out test. Transcrystalline zones around the reinforcing fibers do not seem to improve the adhesion level significantly. Neighbor fibers hinder the formation of the transcrystalline zone and a ductile fracture behavior can be observed. However, the apparent strength level is slightly higher for composites containing such reinforcing neighbor fibers compared with single fiber composite samples. During annealing a brittle interface can be formed in the multifiber composite yielding a higher level of the apparent shear strength.
It is highly desirable to improve attractive interactions between carbon fibers and unreactive thermoplastic matrices to the possible maximum. This could be achieved by a simple grafting process to create a covalently bonded interface or interlayer, which should result in cohesive interactions between the polymer-grafted fibers and the same matrix material, leading to a better adhesion strength in the obtained composite material. Here, we are describing the grafting of styrene onto unmodified and unsized carbon fibers via free-radical bulk polymerization in the presence of fibers. After grafting, the surface properties of the carbon fiber approach those of pure polystyrene which was proven by contact angle and zeta ({zeta}) potential measurements. As indicated by the water contact angle, the carbon fiber surface becomes more hydrophobic. Scanning electron microscopy (SEM) provides evidence of grafted polymer. This simple procedure results in a continuous polystyrene coating. The fiber diameter increases significantly after polymer grafting. The adhesion and fracture behavior between the original and polystyrene-grafted carbon fibers to a polystyrene (VESTYRON®) matrix was characterized using the single-fiber pull-out test. There is a considerable increase in the measurable adhesion, i.e., the interfacial shear strength IFSS, by almost 300% between the grafted fibers and polystyrene as compared to untreated original fibers. Two planes of interfacial failure could be distinguished; first in the fiber coating interface leading to lower interfacial shear strength and second in the PS-matrix-PS-coating interphase resulting in a higher interfacial shear strength. In addition to the improved adhesion, there are also clear differences in the pull-out behavior between the nongrafted and grafted fibers. After the initial debonding process corresponding to the maximal pull-out force is completed, the pull-out force is increasing again.