Current efforts for lightweight design result in a growing application of high-strength fine-grained structural steel in modern steel constructions, e.g. mobile cranes, with yield strength from 960 MPa. The design of welded structures and the welding process become more challenging with increasing material strength due to higher elastic ratios. The formation of high residual stresses, which are able to diminish lifetime, load capacity and component safety, has to be avoided. Recent numerical and experimental analyses have shown a strong influence of the heat control and the rigidity of the weld on the welding stresses. Global reaction stresses due to an external shrinkage restraint superimpose with local residual stresses in the weld seam. Modern inverter technologies allowed the development of numerous modified spray arc processes driven by the power source manufactures with almost equal characteristics. They provide several well-known technical and economic benefits, like the possibility of welding narrower seam configurations. As a result a smaller weld volume, total heat input and, therefore, reduced welding stresses are achievable. This research focuses on the welding loads due to modified weld seams. The global reaction forces in welded components due to an external shrinkage restraint were investigated in a special in-house developed testing facility. Additionally, the superposition of the local residual stresses, global stresses and bending moments were analysed with the help of X-ray diffraction. The intensity of the restraint, the weld seam configuration and the weld process (transitional arc and modified spray arc) were varied for a statistical evaluation of the resulting welding loads. It was observed that under restraint a smaller weld seam volume affects reduced reaction stresses.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a domi-nant role concerning so-called stress relief cracking (SRC) typically during post weld heat treat-ment (PWHT). Besides specific metallurgical factors (like secondary hardening due to re-precipitation), high tensile residual stresses are a considerable influence factor on SRC. For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-re-melted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases compa-rable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analysed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behaviour, welding and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.