Filtern
Dokumenttyp
- Zeitschriftenartikel (7)
- Vortrag (6)
- Beitrag zu einem Tagungsband (2)
- Buchkapitel (1)
Sprache
- Englisch (16)
Schlagworte
- Welding (4)
- Mechanical properties (3)
- Residual stresses (3)
- Restraint (3)
- Ultrasonic-assisted milling (3)
- Dissimilar metal weld (2)
- Electron backscattered diffraction (2)
- Friction stir welding (2)
- High Entropy Alloy (2)
- High-entropy alloy (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6)
Multiple principal element alloys (MPEA) encompass the well-known high entropy alloys (HEAs). MPEA/HEA represent a new class of materials consisting of at least three alloying elements, each containing 5 to 35 at.-%. This alloying concept thus differs fundamentally from conventional materials such as steel or nickel alloys. For this purpose, the alloying elements are specifically selected, and the microstructures are adjusted in a single-phase and, in some cases, multi-phase manner. In particular, conflicting goals, such as the trade-off between strength and ductility in conventional steels, are overcome. In the last 20 years, however, the focus has been on material synthesis. With the increase in available material quantities, the focus is now on pro-cessing issues such as joining and welding processes. The weldability of MPEA has received very little atten-tion so far. Experience with dissimilar metal welds (DMWs) is completely lacking but is essential for the appli-cation of these materials in combination with conventional materials. The present study presents, comprehen-sive experimental results on the weldability of MPEA-DMWs. For that purpose, a Co20Cr20Fe20Mn20Ni20 HEA in cold-rolled and heat-treated condition was joined by means of tungsten inert gas welding (TIG) with the austenitic Cr-Ni steel AISI 304. The DMWs resulted in interesting mechanical properties. They were obtained by instrumented tensile tests as well as the local deformation in the weld area by using digital image correlation (DIC) technique. A significant softening in the heat-affected zone (HAZ) of the MPEAs as well as a slightly reduced tensile strength with a significant decrease of the elongation at fracture were found. The experiments provided proof in principle of the weldability of the MPEAs for DMWs with conventional materials that ensure a corresponding capability for mechanical loading. This allows further considerations on the application of these innovative materials.
When welding super duplex stainless steels a non-admissible pore formation can occur even if recommended processing guidelines are followed strictly. To investigate this phenomenon and to determine the influencing factors different claddings were produced using gas metal arc welding and submerged arc welding. The welding consumables, the shielding gas and the welding flux were varied. As shielding gases several mixtures, based on argon and 30 % helium, with various amounts of nitrogen, nitric oxide, carbondioxid and oxygen were applied. As welding flux agglomerated fluoride basic fluxes and aluminate fluoride basic fluxes were used. Different batches of the similar solid filler wire G 25 9 4 N L were used to produce the claddings on the base material UNS32750. To determine the pore formation X-ray examinations and microsections were used, to analyze the chemical composition of the claddings melt extractions and spectrometric examinations were applied. Additionally, the microhardness and the ferrite number were detected. The studies have shown the shielding gas, the welding flux and the filler metal possess a great influence on the pore formation. Even small variations in the chemical composition of the welding consumables lead to totally different results. In addition, the ferrite number and the chemical composition of the claddings depend strongly on the used gases and filler metals.
Current efforts for lightweight design result in a growing application of high-strength fine-grained structural steel in modern steel constructions, e.g. mobile cranes, with yield strength from 960 MPa. The design of welded structures and the welding process become more challenging with increasing material strength due to higher elastic ratios. The formation of high residual stresses, which are able to diminish lifetime, load capacity and component safety, has to be avoided. Recent numerical and experimental analyses have shown a strong influence of the heat control and the rigidity of the weld on the welding stresses. Global reaction stresses due to an external shrinkage restraint superimpose with local residual stresses in the weld seam. Modern inverter technologies allowed the development of numerous modified spray arc processes driven by the power source manufactures with almost equal characteristics. They provide several well-known technical and economic benefits, like the possibility of welding narrower seam configurations. As a result a smaller weld volume, total heat input and, therefore, reduced welding stresses are achievable. This research focuses on the welding loads due to modified weld seams. The global reaction forces in welded components due to an external shrinkage restraint were investigated in a special in-house developed testing facility. Additionally, the superposition of the local residual stresses, global stresses and bending moments were analysed with the help of X-ray diffraction. The intensity of the restraint, the weld seam configuration and the weld process (transitional arc and modified spray arc) were varied for a statistical evaluation of the resulting welding loads. It was observed that under restraint a smaller weld seam volume affects reduced reaction stresses.
High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analysed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behaviour, welding and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.
Multiple principal element alloys (MPEA) represent a class of materials consisting of at least three alloying elements, each with 5 to 35 atomic %. The MPEAs encompass the so-called high-entropy (HEA) and medium-entropy alloys (MEAs) and are fundamentally different from conventional materials like the Fe-based steel. Within the last 20 years, highly innovative MPEA with individually adjustable properties for industrial applications were identified. However, the focus has been on pure material synthesis. With the increase in available material quantities, the focus is now on processing issues such as joining and welding. In that connection, the weldability of MPEAs has received very little attention so far and experience in dissimilar metal welds (DMWs) is lacking so far but. The present study summarizes comprehensive experimental results on the weldability of MPEA-DMWs and their resulting microstructure. For this purpose, two equiatomic MPEAs, CoCrFeMnNi (HEA) and CoCrNi (MEA) in cold-rolled and annealed conditions were joined by solid-state friction stir welding (FSW) to an austenitic stainless steel 316L. The DMWs showed very interesting microstructure features. In addition, the mechanical-technological properties were obtained by instrumented tensile tests, and the local straining was determined in-situ by digital image correlation (DIC). A significant influence of the FSW processing on the mechanical performance was identified,in terms of the formation of FSW-specific defects like whitebands or tunnel defects. The experiments proofed the general (but currently limited) FS weldability of the MPEAs to conventional austenitic steel grade AISI 304. This enables targeted further considerations of these highly innovative MPEAs.
High- and medium-entropy alloys (HEAs) are a quite new class of materials. They have a high potential for applications from low to high temperatures due to the excellent combination of their structural properties.
Concerning their application as components; processing properties, such as machinability, have hardly been investigated so far. Hence, machinability analyses with a focus on the influence of the milling process and its basic parameters (cutting speed, feed per cutting edge) on the resulting surface integrity of specimens from an equiatomic high- (CoCrFeMnNi) and a medium- (CoCrNi) entropy alloy have been carried out. A highly innovative milling process with ultrasonic assistance (USAM) was compared to conventional milling processes.
Recent studies have shown that USAM has a high potential to significantly reduce the mechanical load on the tool and workpiece surface during milling. In this study, the basic machining and ultrasonic parameters were systematically varied. After machining, the surface integrity of the alloys was analyzed in terms of topography, defects, subsurface damage, and residual stresses. It was observed that USAM reduces the cutting forces and increases the surface integrity in terms of lower tensile residual stresses and defect density near the surfaces for the CoCrFeMnNi alloy. It was shown that the cutting forces and the metallurgical influence in the sub surface region are reduced by increasing the cutting speed and reducing the feed rate per cutting edge. With the CoCrNi alloy, the tool revealed severe wear. As a result, for this alloy no influence of the parameters on the machinability could be determined.
Multi-element systems with defined entropy (HEA - High Entropy Alloy or MEA - Medium Entropy Alloy) are rather new material concepts that are becoming increasingly important in materials research and development. Some HEA systems show significantly improved properties or combinations of properties, e.g., the overcome of the trade-off between high strength and ductility. Thus, the synthesis, the resulting microstructures, and properties of HEA have been primarily investigated so far. In addition, processing is crucial to achieve a transfer of potential HEA/MEA materials to real applications, e.g. highly stressed components. Since fusion welding is the most important joining process for metals, it is of vital importance to investigate the weldability of these materials. However, this has rarely been the subject of research up to date. For that reason, in this work the weldability depending on the surface preparation of a CoCrFeMnNi-HEA and a CoCrNi-MEA for TIG welding is investigated. The fusion welding of longer plates is described here for the first time for the CoCrNi alloy. The welds of both materials showed distinct formation of cracks in the heat affected zone (HAZ). Optical and scanning electron microscopy analysis clearly confirmed an intergranular fracture topography. But based on the results, the crack mechanism cannot be conclusively clarified as either a liquid metal embrittlement (LME) or hot cracking like liquid film separation occurred.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a domi-nant role concerning so-called stress relief cracking (SRC) typically during post weld heat treat-ment (PWHT). Besides specific metallurgical factors (like secondary hardening due to re-precipitation), high tensile residual stresses are a considerable influence factor on SRC. For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-re-melted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases compa-rable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
Multiple principal element alloys encompass the well-known high entropy alloys (HEA). The alloy system represents a new class of materials consisting of at least three alloying elements, each containing 5 to 35 at.%. Thus, this alloying concept differs fundamentally from conventional materials such as steel or nickel alloys. For this purpose, the alloying elements are specifically selected, the microstructures are adjusted in a single-phase and, in some cases, multi-phase manner. In particular, conflicting goals, such as the trade-off between strength and ductility in conventional steels, are overcome. However, in the last 20 years, the focus has been on material synthesis. With the increase in available material quantities, the focus is now on processing issues such as joining and welding processes. The weldability of HEAs has received very little attention so far. The experience with dissimilar metal welds is completely lacking but is essential for the application of these materials in combination with conventional materials. The present study presents comprehensive experimental results on the weldability of an equimolar CoCrFeMnNi-HEA in cold-rolled and heat-treated condition, which was joined by tungsten inert gas welding to an austenitic steel AISI 304. The mechanical properties of the dissimilar metal welds were characterized by cross-weld tensile samples, whereas the local deformation in the weld of the different welding zones was measured by digital image correlation. In accordance with the respective initial HEA condition (cold-rolled vs. heat-treated), the local strain behavior was divergent and influenced the global mechanical properties of both DMW types. Nonetheless, the experiments provided proof in principle of the weldability for dissimilar joints of the CoCrFeMnNi-HEA welded to conventional materials like austenitic stainless steels ensuring a corresponding capability for mechanical loading. This allows further considerations on the application of these innovative materials.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system with a load capacity of 2 MN specifically developed for online monitoring of stress formation and cracking are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be quantified in-situ during welding and post weld heat treatment. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. Elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of mechanical stresses resulting from welding on stress relief cracking is demonstrated by the example of a creep resistant steel. Reheat cracks were monitored online during post weld heat treatment.