The hydrolytic degradation of technical poly(ethylene terephthalate) (PET) was investigated by means of different methods such as size-exclusion chromatography (SEC), viscometry, light-scattering, thin-layer chromatography, end-group titration, and matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS). The long-term degradation was simulated by exposing PET filament yarns to aqueous neutral conditions at 90°C for up to 18 weeks. By means of MALDI-MS and thin-layer chromatography, the formation of different oligomers was obtained during polymer degradation. As expected, an ester scission process was found generating acid terminated oligomers (H-[GT]m-OH) and T-[GT]m-OH and ethylene glycol terminated oligomers (H-[GT]m-G), where G is an ethylene glycol unit and T is a terephthalic acid unit. Additionally, the scission of the ester bonds during the chemical treatment led to a strong decrease in the number of cyclic oligomers ([GT]m). The occurrence of di-acid terminated species demonstrated a high degree of degradation.
A report is presented on the development of a test for determining the long-term oxidation resistance of polyolefin materials, which is accelerated not only by elevated temperatures but also by increased oxygen pressure and a stirred aqueous medium. The method permits durability tests to be carried out at markedly lower temperatures with reasonable testing durations and significantly reduced diffusion limited oxidation effects and allows for physical and chemical impacts of aqueous media. Oxidative durability can be assessed by autoclave immersion exposures at three different temperatures (60, 70 and 80 degrees C) and 50 bar oxygen pressure and at 80 degrees C and two different oxygen pressures (usually 10 and 20 bar). Accelerated test data are evaluated by modified Arrhenius equations with the application of a three-dimensional regression analysis. The application of the test method to various materials, including PP non-woven materials and geosynthetics is demonstrated. 10 refs.
Oxidative long time resistance is essential for many polyolefin based products, especially if repair or exchange is not possible as encountered in many building and geotechnical applications. Current regulations and recommendations for geosynthetics cover mainly the needs of a maximum lifetime of 25 years, though many applications require longer lifetimes up to 100 years and more. Reliable testing of the long time oxidation resistance is complicated by the complex interplay of physicochemical processes and reactions in combination with the need of relatively short testing durations, usually not exceeding 12 months. Thus for conventional atmospheric oven testing, the use of temperatures higher than 100 °C is inevitable, making conclusive Arrhenius extrapolations often questionable.
Practical assessments of oxidative durability consist of exposures under accelerated ageing conditions with subsequent characterization of exposed material samples with respect to their residual stabilization and/or their mechanical properties.
The autoclave test combines exposures at elevated temperatures with higher oxygen pressures and is performed with material samples immersed in a well defined aqueous medium representing critical environments in geosynthetic applications and including extraction of additives. Under these conditions meaningful results can be obtained within reasonable testing durations at only moderately elevated temperatures up to 80 °C.
Application of different physicochemical methods, such as tensile testing, OIT /HP-OIT and analysis of residual antioxidant content (ICOT), in order to determine the time dependent degradation behaviour, reveal valuable information about mechanisms and effectiveness of the used antioxidants. Corresponding results for exposures at different temperatures and oxygen pressures are the basis for a 3D-extrapolation in order to estimate the expected service life. Different empirical models are presented and discussed with respect to their practical impact.