The hydrolytic degradation of technical poly(ethylene terephthalate) (PET) was investigated by means of different methods such as size-exclusion chromatography (SEC), viscometry, light-scattering, thin-layer chromatography, end-group titration, and matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS). The long-term degradation was simulated by exposing PET filament yarns to aqueous neutral conditions at 90°C for up to 18 weeks. By means of MALDI-MS and thin-layer chromatography, the formation of different oligomers was obtained during polymer degradation. As expected, an ester scission process was found generating acid terminated oligomers (H-[GT]m-OH) and T-[GT]m-OH and ethylene glycol terminated oligomers (H-[GT]m-G), where G is an ethylene glycol unit and T is a terephthalic acid unit. Additionally, the scission of the ester bonds during the chemical treatment led to a strong decrease in the number of cyclic oligomers ([GT]m). The occurrence of di-acid terminated species demonstrated a high degree of degradation.
A report is presented on the development of a test for determining the long-term oxidation resistance of polyolefin materials, which is accelerated not only by elevated temperatures but also by increased oxygen pressure and a stirred aqueous medium. The method permits durability tests to be carried out at markedly lower temperatures with reasonable testing durations and significantly reduced diffusion limited oxidation effects and allows for physical and chemical impacts of aqueous media. Oxidative durability can be assessed by autoclave immersion exposures at three different temperatures (60, 70 and 80 degrees C) and 50 bar oxygen pressure and at 80 degrees C and two different oxygen pressures (usually 10 and 20 bar). Accelerated test data are evaluated by modified Arrhenius equations with the application of a three-dimensional regression analysis. The application of the test method to various materials, including PP non-woven materials and geosynthetics is demonstrated. 10 refs.