Long-term behaviour of geosynthetic drains - excavations on landfills after up to 12 years service
(2002)
To properly understand and assess the long-term behaviour of geosynthetic materials it is necessary to investigate the various types of possible degradation mechanims. This includes both chemical and mechanical behaviour, and sometimes even their interactions with one another. Clearly, chemical degradation of geosynthetics depends on the polymer type. For example, polyolefins are vulnerable to oxidation; polyesters are susceptible to hydrolysis; and plasticizers can leach from polyvinyl chloride. This paper describes the concept of these three types of degradation, but focuses on the oxidation of polyolefins since the majority of the geosynthetics is made from this type of polymer. The methods used to predict the lifetime of antioxidants and service life of the geosynthetic material will be illustrated. Furthermore, the influence of temperature, pressure, and ultraviolet light on the service life are also demonstrated. Finally, the current specifications targeting the longevity of different geosynthetics are presented.
Regarding mechanical degradation, the paper mainly focuses upon the creep deformation of geogrids and stress crack resistance (SCR) of polyethylene geomembranes and geopipe. The method to assess stress crack resistance is described, and the microscopic mechanisms that lead to such failure are explained. For creep evaluation, different acceleration tests are presented and their applicability with respect to the different types of polymers is illustrated. In addition, the long-term shear behaviour of geocomposites and geosynthetic clay liners is presented.
Service life of geosynthetics made of polyolefin materials is mainly limited by oxidative degradation. Durability of polyolefin products depend on formulation, morphology resulting from manufacturing, design and particularly on the antioxidants used. Although the fundamental oxidative reactions are known, the complex effect of geosynthetic characteristics and external influences mean that durability assessments require practical tests.
The assessment of oxidative durability involves exposure to accelerating conditions as well as the material characterisation with respect to the state of stabilisation and/or degradation (e.g. by tensile testing and/or oxidation induction time).
The autoclave test developed by BAM for durability assessments of polyolefin geosynthetics is based on the simultaneous application of moderately elevated temperatures (up to 80 degrees Celsius) and elevated oxygen pressures (up to 5.0 MPa) in combination with a surrounding aqueous medium. Thus this test method provides several advantages in comparison to conventional oven testing, especially with respect to test duration, impact of surrounding environment and the potential to differentiate and rank oxidative resistance between products of very different dimensions (surface/volume) and stabilisation.
In view of the increasing demand for durability assessments of geosynthetic products with lifetimes significantly exceeding 25 years, the contribution is focused on practical aspects concerning implementation and optimisation of test procedures, conditions and evaluation of results. Furthermore, advanced approaches based on multiple exposure conditions will also be included and corresponding calculations of expected service life in typical applications will be evaluated with respect to significance and repeatability. Thereby involved standards and recommendations - such as EN ISO 13438, Part C or EAG-EDT - are considered.