Filtern
Dokumenttyp
- Zeitschriftenartikel (13)
- Beitrag zu einem Sammelband (1)
- Beitrag zu einem Tagungsband (1)
- Vortrag (1)
- Forschungsbericht (1)
- Forschungsdatensatz (1)
Schlagworte
- Crosslinking (3)
- Incineration bottom ash (3)
- Polyurethane (3)
- Rostasche (3)
- Thermal degradation (3)
- Degradation (2)
- Ecotoxicity (2)
- Geosynthetics (2)
- Geotextiles (2)
- Microplastic (2)
Organisationseinheit der BAM
- 4 Material und Umwelt (13)
- 4.3 Schadstofftransfer und Umwelttechnologien (13)
- 6 Materialchemie (5)
- 6.3 Strukturanalytik (5)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.7 Organische Spuren- und Lebensmittelanalytik (2)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (2)
- 1.2 Biophotonik (1)
- 5 Werkstofftechnik (1)
- 5.6 Glas (1)
Eingeladener Vortrag
- nein (1)
Polyether and -ester urethanes (PU) were exposed to artificial weathering at 40 °C and artificial UV radiation in a weathering chamber. In 3 parallel exposures, humidity was varied between dry, humid, and wet conditions. Material alteration was investigated by various analytical techniques like size exclusion chromatography
(SEC), liquid chromatography-infrared spectroscopy (LC-FTIR), thermal-desorption gas chromatography-mass spectrometry (TD-GC-MS), fluorescence mapping and dynamic mechanical analysis (DMA). Our results show that depending on the weathering conditions, different degradation effects can be observed. By means of SEC an initial strong decrease of the molar masses and a broadening of the mass distributions was found. After a material dependent time span this was followed by a plateau where molar mass changes were less significant. A minor moisture-dependent degradation effect was only found for polyester PU. Fluorescence measurements on two materials revealed an increase in the luminescence intensity upon weathering process reaching a saturation level after about 500 h. The changes in the optical properties observed after different exposure conditions and times were very similar. The TD-GC-MS data showed the fate of the stabilizers and antioxidant in the course of weathering. LC-FTIR measurements revealed a change in peak intensities and the ratio of urethane and carbonyl bands.
Aschen und Schlacken aus der thermischen Abfallbehandlung stellen mit rund 25% Massenanteil die größte Reststofffraktion dar. In Deutschland fallen pro Jahr rund 6 Millionen Tonnen an. Während sich die Verwertung der metallischen Anteile problemlos gestaltet, werden an die mineralische Fraktion Anforderungen bezüglich der möglichen Freisetzung von Schwermetallen sowie Chlorid und Sulfat gestellt. In der Ersatzbaustoffverordnung sind für Aschen und Schlacken aus der Abfallverbrennung zwei Materialklassen mit unterschiedlich hohen Anforderungen an die Umweltverträglichkeit definiert. Im Rahmen eines Forschungsprojekts wurde untersucht, ob mit Abtrennung der Feinfraktion von 0–2mm die höhere Materialklasse HMVA-1 erreicht werden kann. Im Ergebnis wurde eine Verbesserung des Auslaugverhaltens erzielt, doch nicht in dem Maß, dass eine Qualität nach HMVA-1 erreicht wird. Rostaschen halten aber die Anforderungen zur Deponierung auf einer DK I-Deponie sowie die Anforderungen zur Verwertung gemäß HMVA-2 sicher ein.
The long-term leaching behavior of incineration bottom ash (IBA) was studied with large-scale samples from two German waste incinerators with grate technology. The observation period was up to 281 days. The aging processes proceeded faster in the outdoor storage of the samples. The dominant factor in the leaching behavior is the pH, which starts at values above 12 and decreases to values below 10 (outdoors, <11 indoors). Most heavy metals exhibit minimum solubility in this pH range. The solubility of Sb depends on the prevailing Ca concentration, due to the formation of low-soluble Ca antimonate. The very low sulfate concentrations observed in the leaching tests with fresh IBA could be explained by the presence of ettringite. In the course of the aging reaction, ettringite is transformed into gypsum. The results from batch tests were compared with those from column tests, showing reasonable agreement. Leaching dynamics can be better followed with column tests. All results confirm that the use of IBA is possible under German law.
The most massive design on the Baltic shore used geosynthetic materials, the landslide protection construction in Svetlogorsk (1300 m long, 90,000 m2 area, South-Eastern Baltic, Kaliningrad Oblast, Russian Federation) comprises the geotextile and the erosion control geomat coating the open-air cliff slopes. Due to changes in elastic properties during long-term use in the open air, as well as due to its huge size, this structure can become a non-negligible source of microplastic pollution in the Baltic Sea. Weather conditions affected the functioning of the structure, so it was assessed that geosynthetic materials used in this outdoor (open-air) operation in coastal protection structures degraded over time. Samples taken at points with different ambient conditions (groundwater outlet; arid places; exposure to the direct sun; grass cover; under landslide) were tested on crystallinity and strain at break. Tests showed a 39–85% loss of elasticity of the polymer filaments after 3 years of use under natural conditions. Specimens exposed to sunlight are less elastic and more prone to fail, but not as much as samples taken from shaded areas in the grass and under the landslide, which were the most brittle.
Size-exclusion chromatography (SEC) was used to monitor changes of the molecular masses of thermoplastic polyether – and polyester urethane (TPU) exposed to thermal, hydrolytic, and photo-oxidative (UV) Degradation conditions for several days. The thermal treatment was performed at elevated temperatures (100–200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks. Surprisingly, the influence of oxygen (air) was found to be less distinct. In contrast to that, UV treatment at 25 °C at less than 10% rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than for thermal treatments. The depth of penetration of the UV radiation was estimated using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that esterbased PU in general exhibits a significant higher stability compared to ether-based materials.
Degradation of polyurethanes in various environments – Effects on molecular mass and crosslinking
(2019)
The increasing application of polyurethanes (PU) in safety relevant sectors (fire protection, insulation, medicine technique) requires detailed knowledge of the stability and reliability of these materials. Different climate factors are supposed to induce diverse and overlapping degradation reactions. The knowledge of these degradation mechanisms is necessary for an estimation of the period of application depending on usage of the material. An essential property of a polymeric system is represented by the molecular weight. Since a change of the molecular weight is a measure for the chemical stability of a polymer, size-exclusion chromatography (SEC) was used to monitor changes of the molecular weight of thermoplastic polyether- and polyester urethane (TPU) exposed to thermal, hydrolytic and photo-oxidative (UV) degradation conditions for several days. Thermal treatments were performed at elevated temperatures (100 - 200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥ 175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤ 150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks, which was already known from FTIR spectroscopy[1]. In contrast to that, UV treatment at 25 °C at less than 10 % rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than during the thermal treatments. The depth of penetration of the UV radiation was determined using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤ 80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that ester-based PU in general exhibits a significant higher stability compared to ether-based materials.
With the aim of improving limits of detection (LOD) of trace elements in a matrix with adjacent fluorescence energies, a simple double dispersive X-ray fluorescence detection system (D2XRF) was constructed to operate at the beamlines BAMline and the mySpot @ BESSY II. This system is based on the combination of a crystal analyzer with an energy resolving single photon counting pnCCD. Without further collimators, the efficient suppression of the background by the pnCCD and the good energy resolution of the crystal results in improved LOD. In first order reflections, an energy resolution of 13 eV for Cu Kα was reached, and an energy range of 1 keV was covered in one shot.
This new system was applied to the detection of platinum (Pt) in gold leaves with a LOD of 0.9 mg/kg, which is the lowest attained by totally non-destructive methods nowadays. The presence of Pt in gilded objects from Abydos and Byzantine mosaics provides vital information, as it indicates the alluvial origin of the gold for these examples.
Im Rahmen des Projekts konnte gezeigt werden, dass Geokunststoffe bei ausreichender Stabilisierung Einsatzdauern von über 100 Jahren besitzen. Es werden keine Stoffe freigesetzt, die für Wasserorganismen schädlich sind. An den Ostseestränden im Gebiet Kaliningrad werden nennenswerte Mengen von Kunststoffresten gefunden, die zum Teil aus Küstenschutzbauwerken stammen. Ursache ist hier jedoch eine verfehlte Materialauswahl. Hauptsächlich stammen die Kunststoffreste am Strand jedoch aus unsachgemäße Abfallbehandlung.
Einstufung von Aschen und Schlacken aus der Abfallverbrennung im Hinblick auf die weitere Verwertung
(2024)
There are two mirror entries in the European Waste Catalogue for bottom ash and slag from waste incineration: 19 01 11* and 19 01 12. Entry 19 01 11* describes a waste material containing hazardous substances. It was shown that only the hazardous property HP14 (ecotoxic) is of relevance for the classification. If substances with the hazard statement code (HSC) H400, H410, H411, H412 and H413 are present in incineration bottom ash (IBA) above certain level the waste is classified as hazardous, otherwise it is non-hazardous (in this case 19 01 12). It was further shown that only Cu, Zn and Pb compounds have an impact on the classification using a summation rule: 100xΣ c(H410) + 10xΣ c(H411) + Σ c(H412). Limit value is 25 percent. It is obvious that H410 substances have the highest impact. Therefore, the knowledge of the elemental composition of IBA is not sufficient because the content of distinct chemical compounds (with the respective molecular weight) is needed. When the exact speciation is not known a worst-case approach has to be applied. A practical guideline for the estimation of HP14 was developed based on the definition of 4 substance groups: 1. Metals and alloys, 2. Water-soluble substances, 3. Oxides and carbonates and 4. Substances not soluble in weak acids. In substance group 1 only fine Zn powder has the HSC H410. Water-soluble substances are assumed to be H410 substances. Their concentrations are, however, regularly below the cut-off value of 0.1 %. The amount of substance group 3 is estimated by a selective extraction with maleic acid. According to the worst-case approach it is assumed that CuCO3xCu(OH)2 and ZnO represent the respective Cu and Zn species in IBA because these substances have the highest stochiometric factor. Even with this worst-case approach results from operators of IBA treatment plant showed that the limit value of 25 % is not exceeded.
The requirements for utilization of IBA in Germany are defined in the Secondary
Building Materials Decree (Ersatzbaustoffverordnung EBV) which was set into force in August 2023. Leaching methods (batch test or column test) with a liquid-to-solid ratio of 2 l/kg are applied. IBA fulfills the requirements for class HMVA-2. Actually, even a classification of IBA as hazardous (i.e 19 01 11*) would not affect utilization but handling and transport.
Die Einstufung von Hausmüllverbrennungsasche (IBA) als gefährlich oder nicht gefährlich nach der Gefahreneigenschaft HP14 (ökotoxisch) ist nach wie vor umstritten, da es noch keine keine allgemein anerkannten Methoden zur Bewertung gibt. Wenn die Berechnungsregeln angewendet werden sollen angewendet werden sollen, sind Kenntnisse über die chemische Zusammensetzung von IBA erforderlich. Informationen über über die chemische Zusammensetzung von IBA können mit einem Ansatz gewonnen werden, der auf der Gruppierung von Substanzen. Für IBA können vier Stoffgruppen definiert werden: 1. elementare und legierte Metalle, 2. leicht wasserlösliche Stoffe, 3. schwer lösliche Stoffe und 4. Stoffe mit starken chemischen Bindungen. Elementares und legiertes Cu und Zn sind in der IBA vorhanden und werden in der Regel als Nichteisenmetallfraktion zurückgewonnen, zumindest die größeren Partikel. Zn-Partikel, die kleiner als 1 mm sind, werden als H410 eingestuft, feine Partikel von Cu nur als H411. Die wasserlösliche Fraktion kann mit Standardauslaugungsmethoden quantifiziert werden Auslaugungsmethoden quantifiziert werden, z. B. bei einem Flüssigkeits-Feststoff-Verhältnis (L/S) von 2 oder 10 l/kg. Sowohl die Sulfate von Zn als auch von Cu gehören zu dieser Gruppe. In einer neueren Veröffentlichung wurde gezeigt, dass bei den oben genannten Metalle die ausgelaugte Menge weit unter dem Grenzwert von 1.000 mg/kg liegt, selbst wenn stöchiometrische Faktoren angewendet werden. Stoffgruppe 3 sind potenzielle H410-Stoffe. Dabei handelt es sich um Carbonate, Hydroxide und Oxide der betreffenden Elemente, die löslich sind in schwachen organischen Säuren wie Essigsäure löslich sind. Die Worst-Case-Stoffe der Gruppe 3, d. h. die Verbindungen mit den höchsten stöchiometrischen Faktoren, sind CuCO3xCu(OH)2 und ZnO. Stoffe mit starken chemischen Bindungen wie Silikate oder Sulfide sind nur löslich in starken Säuren (z.B. Königswasser) löslich und haben keinen Ökotoxizitäts-Gefahrencode. Das Mobilisierungsverhalten der relevanten Schwermetalle und damit der Gruppe der schwer schwerlöslichen Verbindungen kann mit der 4-stufigen sequentiellen Extraktion untersucht werden. Für die HP14 Einstufung könnte auch eine einstufige Extraktion ausreichend sein. Nur die Elemente Zn und Cu sind für die HP14-Einstufung der IBA von Bedeutung, da die Feststoffgehalte aller anderen Schwermetalle unterhalb des Feststoffgehalte aller anderen Schwermetalle unter der Cut-Off-Grenze von 0,1 % liegen, selbst wenn man sie in chemischen Verbindungen mit stöchiometrischen Faktoren. Im Ergebnis wurde gezeigt, dass IBA in der Regel als nicht gefährlich einzustufen ist.