Filtern
Dokumenttyp
- Zeitschriftenartikel (10)
- Beitrag zu einem Sammelband (1)
- Vortrag (1)
- Forschungsbericht (1)
- Forschungsdatensatz (1)
Schlagworte
- Crosslinking (3)
- Polyurethane (3)
- Thermal degradation (3)
- Degradation (2)
- Geosynthetics (2)
- Geotextiles (2)
- Microplastic (2)
- Molecular masses (2)
- UV degradation (2)
- AET (1)
Organisationseinheit der BAM
- 4 Material und Umwelt (9)
- 4.3 Schadstofftransfer und Umwelttechnologien (9)
- 6 Materialchemie (5)
- 6.3 Strukturanalytik (5)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.7 Organische Spuren- und Lebensmittelanalytik (2)
- 1.2 Biophotonik (1)
- 5 Werkstofftechnik (1)
- 5.6 Glas (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
- 7 Bauwerkssicherheit (1)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.5 Röntgenbildgebung (1)
Eingeladener Vortrag
- nein (1)
Degradation of polyurethanes in various environments – Effects on molecular mass and crosslinking
(2019)
The increasing application of polyurethanes (PU) in safety relevant sectors (fire protection, insulation, medicine technique) requires detailed knowledge of the stability and reliability of these materials. Different climate factors are supposed to induce diverse and overlapping degradation reactions. The knowledge of these degradation mechanisms is necessary for an estimation of the period of application depending on usage of the material. An essential property of a polymeric system is represented by the molecular weight. Since a change of the molecular weight is a measure for the chemical stability of a polymer, size-exclusion chromatography (SEC) was used to monitor changes of the molecular weight of thermoplastic polyether- and polyester urethane (TPU) exposed to thermal, hydrolytic and photo-oxidative (UV) degradation conditions for several days. Thermal treatments were performed at elevated temperatures (100 - 200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥ 175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤ 150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks, which was already known from FTIR spectroscopy[1]. In contrast to that, UV treatment at 25 °C at less than 10 % rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than during the thermal treatments. The depth of penetration of the UV radiation was determined using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤ 80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that ester-based PU in general exhibits a significant higher stability compared to ether-based materials.
With the aim of improving limits of detection (LOD) of trace elements in a matrix with adjacent fluorescence energies, a simple double dispersive X-ray fluorescence detection system (D2XRF) was constructed to operate at the beamlines BAMline and the mySpot @ BESSY II. This system is based on the combination of a crystal analyzer with an energy resolving single photon counting pnCCD. Without further collimators, the efficient suppression of the background by the pnCCD and the good energy resolution of the crystal results in improved LOD. In first order reflections, an energy resolution of 13 eV for Cu Kα was reached, and an energy range of 1 keV was covered in one shot.
This new system was applied to the detection of platinum (Pt) in gold leaves with a LOD of 0.9 mg/kg, which is the lowest attained by totally non-destructive methods nowadays. The presence of Pt in gilded objects from Abydos and Byzantine mosaics provides vital information, as it indicates the alluvial origin of the gold for these examples.
The most massive design on the Baltic shore used geosynthetic materials, the landslide protection construction in Svetlogorsk (1300 m long, 90,000 m2 area, South-Eastern Baltic, Kaliningrad Oblast, Russian Federation) comprises the geotextile and the erosion control geomat coating the open-air cliff slopes. Due to changes in elastic properties during long-term use in the open air, as well as due to its huge size, this structure can become a non-negligible source of microplastic pollution in the Baltic Sea. Weather conditions affected the functioning of the structure, so it was assessed that geosynthetic materials used in this outdoor (open-air) operation in coastal protection structures degraded over time. Samples taken at points with different ambient conditions (groundwater outlet; arid places; exposure to the direct sun; grass cover; under landslide) were tested on crystallinity and strain at break. Tests showed a 39–85% loss of elasticity of the polymer filaments after 3 years of use under natural conditions. Specimens exposed to sunlight are less elastic and more prone to fail, but not as much as samples taken from shaded areas in the grass and under the landslide, which were the most brittle.
Thermo-Desorption Gas Chromatography-Mass Spectrometry (TD-GC-MS) was used to investigate the thermal degradation of two different polyurethanes (PU). PU samples were heated at different heating rates and the desorbed products were collected in a cold injection system and thereafter submitted to GC-MS. Prospects and limitations of the detection and quantification of semi-volatile degradation products were investigated. A temperature dependent PU depolymerization was
found at temperatures above 200 °C proved by an increasing release of 1,4-butanediol and methylene diphenyl diisocyanate (MDI) representing the main building blocks of both polymers. Their release was monitored quantitatively based on external calibration with authentic compounds. Size Exclusion Chromatography (SEC) of the residues obtained after thermodesorption confirmed the initial competitive degradation mechanism indicating an equilibrium of crosslinking and depolymerization as previously suggested. Matrix-Assisted Laser Desorption Ionization (MALDI) mass spectrometry of SEC fractions of thermally degraded PUs provided additional hints on degradation mechanism.