A model based on movable cellular automata has been applied to study the sliding behaviour of tribofilms formed during automotive braking. Since it is not possible yet to determine the composition of real tribofilms quantitatively, final verification of modelling results is needed. This was done by preparing artificial third bodies with compositions and nanostructures matching the ones assumed for modelling. Pin-on-disc tests were performed while applying the artificial third bodies to the contact. The results revealed that not only the structure of the third body but also the amount of the applied normal pressure determines the COF obtained by modelling and that much better correlation between experimental and modelling results was obtained while assuming high normal pressures at asperity contacts.
A modified pin-on-disc test was applied to determine tribological properties of typical brake pad constituents. Ball-milling of these ingredients together with iron oxide and graphite provided model materials displaying the main features of real third bodies. Solid lubricants like graphite affected the friction and wear behaviour of Fe3O4 powders considerably whereas further addition of hard nanoparticles induced only minor effects. This was corroborated by comparison with modelling results. MoS2 played a dual role. Depending on special conditions, this ingredient either reduced or increased friction. The latter could be explained, after nanoscopic characterization, by oxidation and destruction of the wear-protecting tribofilm.
Molybdenum disulfide (MoS₂) is a well-known solid lubricant for tribosystems running in vacuum or dry gases. Problems arise due to its sensitivity to humidity, which is a drawback for its application under ambient conditions. However, by using a physical vapor deposition (PVD) process, deposition parameters can be optimized not only to gain a coatings structure with favorable frictional properties but also to minimize the sensitivity to attack by water molecules. Therefore, an improved tribological behavior even under moist conditions can be achieved. MoS₂coatings are also candidates for being applied at cryogenic temperatures. They already have proven their suitability, e.g., for sliding support elements between superconducting magnets of the nuclear fusion-experiment Wendelstein 7-X. However, these coatings were exclusively produced for this particular application and the utilization for more common tribosystems may be precluded due to cost considerations. In view of a wider range of applications, pure and Cr containing PVD-MoS₂ coatings with an optimized structure were tested under varying environments including hydrogen gas and cryogenic temperatures. Results of the most promising variant are presented in this paper.
The main part of a narrow support element (NSE) of the W7-X superconducting coil system is an aluminium bronze pad, PVD coated on its spherical surface with MoS2, which slides against the flat surface of the stainless steel coil housing, coated with MoS2 spray. The operational requirements of the NSEs are: vacuum of p < 10-6 mbar, temperature T ~4 K, maximum load P ~1500 kN, typical displacement ≤5 mm, smooth sliding and no stick-slip events. The paper describes test results obtained with a downscaled NSE at T = 4.2 and 77 K. During the test the NSEs were submerged in liquid helium and nitrogen, respectively. Whereas the LN2 test ran smoothly for up to ~15,000 cycles, the test in LHe showed stick-slip from the very first cycle. The stick-slip disappeared after ~50 cycles. Post mortem analysis of the tested parts revealed that in case of LHe the sprayed MoS2 film was removed during the first 30-100 cycles by blistering and flaking. The reason for the loss of adhesion at LHe temperature is not known, several possible causes are under discussion. Further experiments under vacuum and at T ~4 K are being prepared which are expected to help in clarifying the issue.
The solid lubricant molybdenum disulfide is a well known material for extreme conditions where conventional oil or grease lubrication is not feasible (vacuum, high pressures). However, under reactive environments e.g. high humidity or hydrogen MoS2 is prone to premature failure. By using a PVD process, deposition parameters can be optimized to gain coatings with a more textured structure orienting the basal planes parallel to the Substrate surface, A similar concept has been used by Koch et al. for coatings developed to withstand the extreme operational conditions of the WENDELSTEIN W7-X fusion experiment. Therefore, an improved tribological behavior even under adverse conditions can be achieved.
Adhesion measurements are presented which were carried out with an atomic force microscope between polymer balls attached to a cantilever and a silicon wafer under ultra high vacuum conditions. In using a silicon surface with a defined structure a correlation between adhesion force and contact area was found. This correlation could partly be explained by the Johnson-Kendall-Roberts model, if a change of the surface energy is assumed as a result of the structuring. For a constant geometric contact area an additional structuring leads to a decrease of the adhesion force.