A model based on movable cellular automata has been applied to study the sliding behaviour of tribofilms formed during automotive braking. Since it is not possible yet to determine the composition of real tribofilms quantitatively, final verification of modelling results is needed. This was done by preparing artificial third bodies with compositions and nanostructures matching the ones assumed for modelling. Pin-on-disc tests were performed while applying the artificial third bodies to the contact. The results revealed that not only the structure of the third body but also the amount of the applied normal pressure determines the COF obtained by modelling and that much better correlation between experimental and modelling results was obtained while assuming high normal pressures at asperity contacts.
Adhesion measurements are presented which were carried out with an atomic force microscope between polymer balls attached to a cantilever and a silicon wafer under ultra high vacuum conditions. In using a silicon surface with a defined structure a correlation between adhesion force and contact area was found. This correlation could partly be explained by the Johnson-Kendall-Roberts model, if a change of the surface energy is assumed as a result of the structuring. For a constant geometric contact area an additional structuring leads to a decrease of the adhesion force.
Spacers and supports belong to the critical elements in the structure of a nuclear fusion device, particularly, when they are installed in the vacuum or superconducting magnet system of the reactor. These supports have to sustain high loads while allowing a certain amount of tangential movement with low friction and without any stick-slip motion. Vacuum and cryogenic environments are extremely hostile for smooth sliding systems, because conventional liquid lubricants cannot be employed, and only a very limited number of materials for dry sliding systems under these conditions are available. In order to test the friction behaviour of support elements in the field coils of the fusion experiment WENDELSTEIN 7-X, a test rig was build which allows testing in liquid helium environment at 4.2 K, with a normal force up to 150 kN, and a sliding velocity of 0.1 mm/s in oscillating motion. First tests have shown that the apparatus is appropriate for simulating the sliding behaviour of support elements. As an example, a result of an earlier model test of an MoS2-coating is shown.
The main part of a narrow support element (NSE) of the W7-X superconducting coil system is an aluminium bronze pad, PVD coated on its spherical surface with MoS2, which slides against the flat surface of the stainless steel coil housing, coated with MoS2 spray. The operational requirements of the NSEs are: vacuum of p < 10-6 mbar, temperature T ~4 K, maximum load P ~1500 kN, typical displacement ≤5 mm, smooth sliding and no stick-slip events. The paper describes test results obtained with a downscaled NSE at T = 4.2 and 77 K. During the test the NSEs were submerged in liquid helium and nitrogen, respectively. Whereas the LN2 test ran smoothly for up to ~15,000 cycles, the test in LHe showed stick-slip from the very first cycle. The stick-slip disappeared after ~50 cycles. Post mortem analysis of the tested parts revealed that in case of LHe the sprayed MoS2 film was removed during the first 30-100 cycles by blistering and flaking. The reason for the loss of adhesion at LHe temperature is not known, several possible causes are under discussion. Further experiments under vacuum and at T ~4 K are being prepared which are expected to help in clarifying the issue.
MoS2 is a suitable solid lubricant for environments free of oxygen or water vapor (i.e. vacuum). Humid air degrades film properties due to oxidation accompanied by high wear and increasing coefficients of friction. The present study aims at the further development of sputtered pure MoS2 coatings, extending their applicability to varying environmental conditions by increasing the resistance against humidity. The systematic coating development process is supported by using an experimental Box–Behnken design with variations of the deposition parameters cathode voltage, target/substrate distance, temperature and argon gas pressure. In contrast to common one-factor-at-a-time (OFAT) studies, this approach enables a determination of interactions between deposition process parameters and tribological–mechanical MoS2 film properties. The tribological improvement focuses on a maximization of wear resistance in air and vacuum measured in ball-on-disk experiments. The evaluated mechanical properties are hardness, elastic modulus and residual stresses. These stresses were determined by the substrate curvature method. The study reveals that the residual stress state in the films and the hardness-to-modulus ratio are crucial for their tribological performance in humid air and vacuum environments. After a detailed determination of the relationships between deposition conditions and film properties, some selected microstructural analyses are presented which show that a substantially basal orientation of the lattice has positive effects on wear but also causes anisotropic film properties which result in fissile fracture of the coating if strong shock or point loads occur.
A modified pin-on-disc test was applied to determine tribological properties of typical brake pad constituents. Ball-milling of these ingredients together with iron oxide and graphite provided model materials displaying the main features of real third bodies. Solid lubricants like graphite affected the friction and wear behaviour of Fe3O4 powders considerably whereas further addition of hard nanoparticles induced only minor effects. This was corroborated by comparison with modelling results. MoS2 played a dual role. Depending on special conditions, this ingredient either reduced or increased friction. The latter could be explained, after nanoscopic characterization, by oxidation and destruction of the wear-protecting tribofilm.