Two types of cements were selected as the reference cement in the priority program 2005 of the German Research Foundation (DFG SPP 2005). A thorough characterization of CEM I 42.5 R has been made in a recent publication. In this paper, the characterization data of the other reference cement CEM III/A 42.5 N are presented from the aspects of chemical and mineralogical compositions as well as physical and chemical properties. The characterization data of the slag, which is the second main constituent of this specific cement besides the clinker, are presented independently. For all data received, the mean values and the corresponding errors were calculated. The data shall be used for the ongoing research within the priority program. Also, researchers from outside this priority program can benefit from these data if the same materials are used.
Organic admixtures are an indispensable component of modern concrete. Thus, their purposeful application is not only technically and economically viable but in addition an inevitable tool to make concrete more environmentally friendly. In this context, the use of polysaccharides has increasingly gained interest in the built environment as sustainable resource for performance enhancement. However, due to its origin, biopolymers possess a vast variety of molecular structures which can result in incompatibilities with other polymers present in concrete, such as superplasticizers. The present study highlights effects of the joint application of different types of starches and polycarboxylates with respect to their influence on cement hydration and structural build-up of cement pastes.
Today, chemical admixtures like superplasticisers and stabilising agents are extremely important for modern concrete technology. These agents have meanwhile become common practice in concrete technology, but the understanding within the entire system lags far behind their application. The macroscopic rheology of concrete in the presence of superplasticizers strongly depends upon effects on a much smaller scale such as the hydration of the cement, the adsorption of superplasticizers, and the pore solution chemistry.
Superplasticizers (SPs) have been employed in concrete technology for decades to improve the workability of concrete in its fresh state. The addition of SPs in cement-based systems affects the early properties. Although the interaction of the cement particles with various SPs has been extensively researched, there still exists limited research on the interaction of SPs with supplementary cementitious materials such as rice husk ash (RHA). This paper investigates the rheological properties and early hydration kinetics of RHA-blended systems with three types of SPs, a polycarboxylate ether (PCE) and two lignosulphonates (LS-acc and LS-ret). In rheological properties, the addition of SP causes an initial improvement of workability as the yield stress is significantly reduced. The pastes with PCE and LS-acc show a slight increase of yield stress over time whereas pastes with LS-ret tend to lower the yield stress slightly over time, further improving the workability. Without SP, pastes with RHA show a lower yield stress but an increase in plastic viscosity as cement is further replaced with RHA. The addition of the LS SPs is observed to lower the plastic viscosity but remains constant with further replacement of cement with RHA. This indicates that LS SPs further adsorbs on RHA particles and hydration products produced causing dispersion of the particles
within the system. In early hydration kinetics, pastes with PCE retard hydration and the degree of retardation is further increased with LS SPs. In the presence of RHA, the retardation of LS SP systems is significantly reduced. The pastes with PCE show more ettringite in the SEM micrographs, but is observed to be shorter needles. This indicates an initial good workability for PCE. However, C-S-H and CH were observed to be low in quantity, whereby the pastes with LS show more nucleation sites for C-S-H and CH. The ettringite needles in the LS systems were similar in quantity and more elongated in some cases but not abundant as in the PCE systems.
As soon as cement is mixed with water, the hydration reaction starts to set of. The progression of the hydration process is governed by the amount and the availability of water and its possibility to access the unhydrated cement grain surfaces. For a total hydration cement theoretically requires water amounting approximately 0.38 of its own mass. Nevertheless, due to the cement’s highly hygroscopic nature, already the moisture in the ambient air can cause first hydration reactions to set in upon the cement grain surfaces. Such pre-hydration processes have an effect on the cement's properties. Dpending on the specific conditions during the storage the significance of the impact on certain properties can vary.
If cement is consumed soon after production and is transported only short distances in a silo wagon to its final destination for immediate use without further stock transfer, the effects are rather negligible. However, if cement is delivered in bags, transported over long distances, shifted serval times and stored for longer time periods until it is finally consumend, these effects can be quite severe. Due to the actual logistical situation with comparably few cement plants, large delivery distances and partially less developed infrastructures, the latter scenario pictures the situation for the most cases in Africa quite well.
In order to verify the relevance of the pre-hydation for practical application, a series of tests was conducted at the German Federal Institute for Materials Research and Testing (BAM). The influence of the cement storage on gresh and hardened concrete properties was investigated for different concrete and mortar types. The investigations show that the impact of the storage conditions is more pronounced for specialized concretes with high sophisticated optimized mixture compositions containing admixtures. Nevertheless, the effects also occur for ordinary concrete and should not be ignored.
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
Tricalcium aluminate (C3A) is found with less than 10% wt. of the total composition; however, during hydration, C3A plays an important role in the early hydration of cement in the presence of gypsum as a set retarder.
The aim of this investigation is to assess the suitability of optical spectroscopy and a dye-based optical probe to monitor early hydration of C3A in the presence of gypsum and hemihydrate. Optical evaluation was performed using steady-state fluorescence and diffuses reflectance spectroscopy (UV-VisDR). Phase characterization during hydration was done with in-situ X-ray diffraction. UV-VisDR with a cyanine dye probe was used to monitor the formation of metastable phases and was employed together with fluorescence spectroscopy, to follow the Aggregation and disaggregation of the dye during hydration. In conclusion, for the first time, a cyanine dye was identified as a feasible and stable probe to monitor C3A hydration changes in the presence of calcium sulfate.
Nowadays, superplasticizers (SPs) are widely used to increase fluidity and reduce water content in concrete; thus, allowing better workability for final applications. The present study will focus on the hydration effect using comb shape polycarboxylates (PCEs), which are known to allow a very low water/cement ratio (w/c of 0.20) or less.Optical methods have been successfully used for the analysis and monitoring of the interactions between a broad variety of nanoscale and molecular systems like nanoparticles of various chemical composition and different types of organic ligands or biomolecules.This encouraged us to assess the potential of these methods, and particularly fluorescence, for the investigation of the interactions that occur at the interface between hydrate surfaces of cement particles and PCE at a very early stage of concrete formation and to differentiate between the impact of PCE’s molecular structures on such interactions.
Concrete technology was exposed to a rapid development during the last three decades. For the longest time in its history, concrete was considered as a three component System consisting of aggregates, which are bound by the hardened cement paste consisting of hydrated cement. Traditionally, the only way of adjusting the consistency of concrete was using well adjusted aggregates and grading curves and adding excess water to the concrete, accepting that the latter in return reduces strength and durability. During the last three decades, however, concrete has developed further from a three component System towards an (at least) five component system, since the use of mineral additions and Chemical admixtures has become state of the art. Both components are able to enhance the workability, the compactability, and the density of the microstructure with effects on strength, ductility and durability, while cement can be saved in parallel. Due to reasonable use of admixtures and additions, concrete can be designed to match mechanically high performance specifications. Traditionally, cement paste was considered the weakest component in concrete. Flowever, in modern concrete a good paste composition can yield highest performance, passing the role of the mechanical bottleneck towards the aggregates.