Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
Die Rheologie von fließfähigen zementären Systemen mit Fließmitteln wird durch eine Vielzahl parallel stattfindender Effekte beeinflusst. Zu diesen Effekten zählen Wechselwirkungen zwischen den Polymeren und Ionen in der Porenlösung, frühe Phasenbildung, zeitabhängige und kompetitive Adsorption zwischen anionischen Polymeren und Sulfationen, Bildung von Phasen in der Porenlösung sowie Morphologieänderungen an Partikeloberflächen. Die frühe Hydratation von Zement, die durch Lösungs- und Fällungsprozesse angetrieben wird, beeinflusst diese Effekte erheblich. Das permanente Ungleichgewicht der Porenlösung führt zu Veränderungen der Partikeloberflächen, welches widerum zur Folge hat, dass rheometrische Messungen dieser Zementleime anfällig für Streuungen sind. Um die Einflüsse aus der Zementhydratation zu minimieren, wurden die rheometrischen Untersuchungen mit Zement in Porenlösung durchgeführt. Die Experimente wurden mit verschiedenen Feststoffvolumenfraktionen durchgeführt und mit den Ergebnissen identischer Systeme mit Wasser anstelle von Porenlösung verglichen. Zusätzlich wurden die gleichen Systeme mit Zugabe von Polycarboxylatethern untersucht.
Die Ergebnisse zeigen, dass die Leime mit Wasser niedrigere Werte für Fließgrenze und plastische Viskosität aufweisen, als die Systeme mit Porenlösung. Während die Polymere eine Verminderung der Fließgrenze zur Folge hatte, war die Wirkung von Polymeren auf die plastische Viskosität vernachlässigbar. Zusätzlich wurde die frühe Hydratation unter Verwendung von Wärmeflusskalorimetrie, Rasterelektronenmikroskopie und Nadeleindringtiefe beobachtet.
Die meisten Einflüsse auf die Rheologie von Beton wirken auf sehr kleinen Skalenebenen. Einflussgrößen im Millimeter oder Zentimeterbereich sind im Wesentlichen auf den Sand und die Gesteinskörnung beschränkt. Letztere machen aber in den meisten Betonen 50 %-70 % des Gesamtvolumens aus, was bei Untersuchungen zur Steuerung der Verarbeitungseigenschaften von Beton häufig vernachlässigt wird. Während Betonzusatzmittel und Zusatzstoffe bei geeigneter Wahl die Rheologie sehr gezielt beeinflussen können, eignen sich Sand und Gesteinskörnung weniger gut zur Steuerung der Rheologie, aber sie tragen zur Rheologie des Gesamtsystems bei. Hierbei können Effekte aus Sand und Gesteinskörnung die Effekte von Zusatzmitteln und Zusatzstoffen überlagern und im ungünstigsten Falle sogar nahezu unwirksam machen. Deshalb sollten Ergebnisse zur Verarbeitbarkeit von Bindemittelsystemen nur mit großer Sorgfalt auf Beton übertragen werden. Es ist wichtig, den Einfluss des Sandes und der Gesteinskörnung besser zu verstehen, um diese so abzustimmen, dass sie Effekte aus Fließmitteln positiv ergänzen anstatt diesen entgegenzuwirken.
Durch eine gezielte Abstimmung lassen sich Kosten wirksam sparen.
Most factors acting on concrete rheology work at an extremely small-scale level. Influencing factors in the millimetre or centimetre area are essentially restricted to sand and aggregates. The latter, however, make up 50 to 70% of the total volume of most concretes – a fact often ignored in research on controlling concrete processing properties.
Whereas suitably chosen concrete admixtures and additives can influence rheology in a very targeted manner, sand and aggregates are less suitable for controlling rheology but nonetheless contribute to the rheology of the Overall system. The actions of sand and aggregate can impose themselves upon the actions of admixtures and additives
and, in unfavourable circumstances, even render them redundant. For this reason, any results concerning the processability of binding agent systems can only be transferred to concrete with great care. It is important to better understand the action of sand and aggregates in order to be able to harmonise them in such a way that they complement the action of superplasticisers positively, instead of
working against them. Savings on costs can also be made by this targeted fine-tuning.
The paper presents rheometric results and hydration curves for cementitious systems based on cement mixed with different aqueous phases at solid volume fraction of = 0.45. The varied aqueous phases were deionized water, limewater, the filter residue of a cement paste mixed at w/c = 2.0, and the filtrate of cement paste at solid volume fraction of 0.45. Each cementitious system provided different amounts and sizes of particles formed in the aqueous phase. The pastes were observed with and without polycarboxylate ether based superplasticizer. It was observed that the presence of particles causes higher PCE saturation dosages to achieve a minimum value, but the minimum value is only affected in the case of large particles. In all cases with and without PCE, the presence of small particles causes increased plastic viscosity. In addition, with decreased number and size of hydrates in the aqueous phase the hydration was retarded, which was specifically pronounced in the presence of PCE
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.