In the last years flowable concrete has become increasingly important in applications such as, for systems with highly reinforced concrete with a complicated formwork, or sprayed concrete and 3D-printing of concrete. For all these applications it is necessary to have tailored rheological properties. Rheology can be described by values of yield stress and plastic viscosity, which can be determined for example by evaluation of rheometer measurements. But for different materials various rheometers with different geometries and stirrers are being used. To see the effects from paste in concrete, it is necessary to investigate mixes of paste, mortar and concrete, stepwise. But currently there exists no device, which is calibrated for these different systems at once. Due to this fact, conventional tests such as V-funnel efflux-time and flow diameter were determined, as well as rheometer data in different cell sizes and geometries.
In this study the assessment of rheological effects in the binder on the rheology of mortar and concrete was investigated by using combination of two rheometers.
With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes.
The African cement, concrete and construction business is growing at rapid pace. The cement sales are expected to grow rapidly until 2050. The number of newly built cement plants increases dramatically and in addition more cements are being imported from outside the continent, e.g. from Turkey, Pakistan, Indonesia, and China, driven by overcapacities in the countries of origin. This causes a high number of potentials and challenges at the same time. Newly built cement plants can operate directly at best technological state of the art and thus incorporate more sustainable technologies as well as produce new and more sustainable products such as cements blended with sustainable supplementary cementitious materials such as calcined clays, and industrial or agricultural by products. At the same time the new variety of binding agent as well as the international imports, which are driven by price considerations, make the cement market prone to quality scatter. This puts pressure on the quality control regulations and institutions to ensure safety of construction, healthy application, and environmental safety for the population. The paper presents possible solutions to build up the rapidly increasing African cement production more sustainably than in the rest of the world as well as the related challenges and obstacles that need to be overcome. Based on experiences with a series of pan-African cement testing laboratory proficiency schemes conclusions are made on technical, regulative and political level.
In order to observe the effect of the aggregate phases between 2 mm and 16 mm without overlap with rheological effects induced by the cement hy-dration and without interactions with a threshold fine sand particle size that affects both, paste and aggregates, rheological experiments were conducted on a limestone filler based paste mixed with aggregates up to 16 mm. Vari-ous aggregate fractions were blended and mixed with the replacement paste in different volumetric ratios.
The dry aggregates’ flow coefficients were determined and compared to yield stress and plastic viscosity values at different aggregate volume fractions. The results indicated that the flow coefficient is not a suitable parameter to predict the performance of the aggregates in the paste. It was shown that the yield stress of pastes is largely determined by the blend of different aggregate fractions, while the plastic viscosity to large extend depends upon the coars-est aggregate fraction.
Based on the results, ideal aggregate composition ranges for minimised yield stress are presented. For the plastic viscosity no such grading curves to achieve minimum values could be found, but high viscosity curves are identified.
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
Repair is an indispensable part of the maintenance of structures over their lifetimes. Structural grouting is a widely used remediation technique for concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. A structural grout system should be injectable in narrow spaces and hence include ingredients with finer particles. Ultrafine cements are ideal for these type of demanding grouts due to their superior properties compared to that of the less expensive, but coarser ordinary Portland cement (OPC). Supplementary cementitious materials (SCMs) are often used to replace OPC clinker based binder in order to modify certain properties and to reduce costs. The most commonly used SCMs are fly ash (FA), and ground granulated blast furnace slag (GGBS). For various special applications microsilica (MS), and metakaolin (MK) are also used. Identifying the optimum replacement contents of OPC by SCMs are a challenge during the design of such grouts. The aim of this experimental study is to investigate the effect of the selected SCMs (FA, MS and MK) on the slump flow, time of efflux, viscosity, shrinkage, and compressive and flexural strength of ultrafine cement based grouts with constant water-binder ratio and superplasticizer content. The test program was formulated using Box-Behnken design principles. Maximum percentages of replacement with ultrafine cement was 6% by volume of cement for MS and 16% for FA, and MK. The results suggest that most investigated grouts have the potential to be used for structural applications. The appropriate quadratic models are then formulated through statistical tools and presented as response surfaces. The trends indicate that fly ash improves the rheological properties, whereas microsilica and metakaolin positively affect shrinkage and mechanical properties to some extent. Based on the influence of SCMs and priorities among the properties, Decision Matrix Analysis (DMA) is carried out to select the most suitable ones among the SCMs. The analysis suggests that microsilica and fly ash are more suitable as SCMs than metakaolin without affecting the properties.
Die Rheologie von fließfähigen zementären Systemen mit Fließmitteln wird durch eine Vielzahl parallel stattfindender Effekte beeinflusst. Zu diesen Effekten zählen Wechselwirkungen zwischen den Polymeren und Ionen in der Porenlösung, frühe Phasenbildung, zeitabhängige und kompetitive Adsorption zwischen anionischen Polymeren und Sulfationen, Bildung von Phasen in der Porenlösung sowie Morphologieänderungen an Partikeloberflächen. Die frühe Hydratation von Zement, die durch Lösungs- und Fällungsprozesse angetrieben wird, beeinflusst diese Effekte erheblich. Das permanente Ungleichgewicht der Porenlösung führt zu Veränderungen der Partikeloberflächen, welches widerum zur Folge hat, dass rheometrische Messungen dieser Zementleime anfällig für Streuungen sind. Um die Einflüsse aus der Zementhydratation zu minimieren, wurden die rheometrischen Untersuchungen mit Zement in Porenlösung durchgeführt. Die Experimente wurden mit verschiedenen Feststoffvolumenfraktionen durchgeführt und mit den Ergebnissen identischer Systeme mit Wasser anstelle von Porenlösung verglichen. Zusätzlich wurden die gleichen Systeme mit Zugabe von Polycarboxylatethern untersucht.
Die Ergebnisse zeigen, dass die Leime mit Wasser niedrigere Werte für Fließgrenze und plastische Viskosität aufweisen, als die Systeme mit Porenlösung. Während die Polymere eine Verminderung der Fließgrenze zur Folge hatte, war die Wirkung von Polymeren auf die plastische Viskosität vernachlässigbar. Zusätzlich wurde die frühe Hydratation unter Verwendung von Wärmeflusskalorimetrie, Rasterelektronenmikroskopie und Nadeleindringtiefe beobachtet.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has an enormous influence on the early hydration of cement. The hydration is retarded and the timing of formation and the morphology of hydrates is affected. This short paper presents experimental results about the influence of delayed Addition time of PCE SPs on hydration of cement and tricalcium aluminate (C3A) pastes, investigated by isothermal heat flow calorimetry. For cement pastes the hydration is retarded with SP, whereby the high charge PCE has a stronger retarding effect than the low charge PCE. With delayed PCE addition the cement shows a less retarded setting than with simultaneous addition. The alteration caused by PCE is much more pronounced for C3A and gypsum mixes than for cement. If the SP is added simultaneous, the exothermic peak of C3A is retarded. However, with delayed addition of SP the hydration is shortened, the gypsum depletion is fastened and the exothermic peak occurs less retarded or even accelerated compared to simultaneous addition. It is obvious that for C3A pastes there is less retardation the later the Addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and hydration rates. The rate of reaction in the second stage is lower, discernible in decreased slopes and broader peaks. Besides this, a distinct ramp in the C3A heat flow curves within the first stage of C3A hydration occurs for all pastes with delayed addition of SP, which suggests an accelerated ettringite formation.
Die meisten Einflüsse auf die Rheologie von Beton wirken auf sehr kleinen Skalenebenen. Einflussgrößen im Millimeter oder Zentimeterbereich sind im Wesentlichen auf den Sand und die Gesteinskörnung beschränkt. Letztere machen aber in den meisten Betonen 50 %-70 % des Gesamtvolumens aus, was bei Untersuchungen zur Steuerung der Verarbeitungseigenschaften von Beton häufig vernachlässigt wird. Während Betonzusatzmittel und Zusatzstoffe bei geeigneter Wahl die Rheologie sehr gezielt beeinflussen können, eignen sich Sand und Gesteinskörnung weniger gut zur Steuerung der Rheologie, aber sie tragen zur Rheologie des Gesamtsystems bei. Hierbei können Effekte aus Sand und Gesteinskörnung die Effekte von Zusatzmitteln und Zusatzstoffen überlagern und im ungünstigsten Falle sogar nahezu unwirksam machen. Deshalb sollten Ergebnisse zur Verarbeitbarkeit von Bindemittelsystemen nur mit großer Sorgfalt auf Beton übertragen werden. Es ist wichtig, den Einfluss des Sandes und der Gesteinskörnung besser zu verstehen, um diese so abzustimmen, dass sie Effekte aus Fließmitteln positiv ergänzen anstatt diesen entgegenzuwirken.
Durch eine gezielte Abstimmung lassen sich Kosten wirksam sparen.
Most factors acting on concrete rheology work at an extremely small-scale level. Influencing factors in the millimetre or centimetre area are essentially restricted to sand and aggregates. The latter, however, make up 50 to 70% of the total volume of most concretes – a fact often ignored in research on controlling concrete processing properties.
Whereas suitably chosen concrete admixtures and additives can influence rheology in a very targeted manner, sand and aggregates are less suitable for controlling rheology but nonetheless contribute to the rheology of the Overall system. The actions of sand and aggregate can impose themselves upon the actions of admixtures and additives
and, in unfavourable circumstances, even render them redundant. For this reason, any results concerning the processability of binding agent systems can only be transferred to concrete with great care. It is important to better understand the action of sand and aggregates in order to be able to harmonise them in such a way that they complement the action of superplasticisers positively, instead of
working against them. Savings on costs can also be made by this targeted fine-tuning.
Während für die Bauwirtschaft in den meisten Ländern der nördlichen Halbkugel die Instandhaltung bestehender Strukturen und Infrastruktur im Vordergrund steht, geht es in vielen Ländern der Südhalbkugel in der Hauptsache um die Schaffung von Bauwerken und Infrastruktur zur Verwirklichung angemessener Lebensbedingungen, was wiederum das schnelle Wirtschaftswachstum weiter befeuert.
Beton ist als Massenbaustoff, trotz landläufig anderer Bewertung, aufgrund seines im Vergleich zu anderen Baustoffen günstigen CO2-Footprints und der globalen Verfügbarkeit hierbei aktuell ohne Alternative. Allerdings ist Beton nach Wasser das am zweithäufigsten genutzte Produkt auf Erden [1] und die globale Nachfrage und Produktion steigt dramatisch. Dies hat Konsequenzen für das globale Klima, denn gerade die als Bindemittel eingesetzten Portlandzemente verursachen bei ihrer Herstellung selbst unter modernsten Produktionsbedingungen große Mengen an CO2.
Deshalb müssen für zukünftige nachhaltigere Technologien neuartige Betone entwickelt werden, die bei gleicher oder verbesserter Leistungsfähigkeit, einen geringeren Bedarf an Portlandzement aufweisen.
Um den CO2-Ausstoß, der mit der Betonherstellung verbunden ist zu minimieren, müssen Anteile an Portlandzement im Bindemittel reduziert und durch nachhaltigere Ersatzstoffe ausgetauscht werden. Darüber hinaus muss das eingesetzte Bindemittel im Beton so effizient wie möglich ausgenutzt werden. Das heißt, ein Bauteil oder Bauwerk sollte gerade so viel Bindemittel enthalten, wie für die Tragfähigkeit und Dauerhaftigkeit erforderlich ist. Hierfür erscheint der Einsatz von leistungsfähigen bauchemischen Produkten unumgänglich. Diese können zum einen die veränderten Verarbeitungseigenschaften, die Zementersatzstoffe mit sich bringen, ausgleichen und gleichzeitig helfen, den Gesamtwassergehalt zu minimieren, so dass das Bindemittel seine maximale Leistungsfähigkeit erzielt. Fließmittel sind aktuell die wichtigsten Zusatzmittel für Beton. Sie reduzieren den Wasserbedarf und ermöglichen, Zement im Beton effizienter auszunutzen. Darüber hinaus sind Stabilisierer wichtig zur Erhöhung der Robustheit, insbesondere im Hinblick auf die bautechnischen Herausforderungen der Zukunft – vom Pumpen über weite Distanzen, dem Spritzen, dem Betonieren bei extremen Klimabedingungen bis hin zum 3D-Druck.
The paper presents rheometric results and hydration curves for cementitious systems based on cement mixed with different aqueous phases at solid volume fraction of = 0.45. The varied aqueous phases were deionized water, limewater, the filter residue of a cement paste mixed at w/c = 2.0, and the filtrate of cement paste at solid volume fraction of 0.45. Each cementitious system provided different amounts and sizes of particles formed in the aqueous phase. The pastes were observed with and without polycarboxylate ether based superplasticizer. It was observed that the presence of particles causes higher PCE saturation dosages to achieve a minimum value, but the minimum value is only affected in the case of large particles. In all cases with and without PCE, the presence of small particles causes increased plastic viscosity. In addition, with decreased number and size of hydrates in the aqueous phase the hydration was retarded, which was specifically pronounced in the presence of PCE
Structural design and application have always been linked to the compressive strength of concrete as the main relevant criterion. This was justifiable in the past, where concrete consisted of water, ordinary Portland cement and aggregates, but this concept is no longer relevant for modern and more sustainable cement and concrete.
Despite these new developments, existing standards, guidelines and academic curricula have not been much updated and are still used worldwide. There is a need to change this situation by proper education of the users.
This overview describes the challenges that arise at a user Level from the higher complexity of modern concrete, and defines needs and requirements for enhanced applicability of sustainable concrete concepts.
Furthermore, recommendations are given on how better concrete practice can be communicated to all the involved parties, from civil and design engineers to constructors and site-appliers on the construction site.
While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio‐based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil‐based.
The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfet ta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly.
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has an enormous influence on the early hydration of cement. The hydration is retarded and the timing of formation and the morphology of hydrates is affected. This short paper presents experimental results about the influence of delayed addition time of PCE SPs on hydration of cement and alite pastes, investigated by isothermal heat flow calorimetry. For cement as well as for alite pastes the hydration is retarded with SP, whereby the high charge PCE has a stronger retarding effect than the low charge PCE. The retardation caused by PCE is much more pronounced for alite than for cement mixes. If PCE is added later to the mix, the induction period is shortened and the hydration is accelerated compared to simultaneous addition. This applies for cement and alite pastes. With delayed PCE addition the alite shows a clearly less retarded setting and main hydration than after simultaneous addition. It is obvious that for alite pastes there is less retardation the later the addition of SP.
Grouting is a universal repair and strengthening technique, which is constantly used for structural remediation of concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. Having an extremely small particle size of only few microns, ultrafine cements are ideal for grouting applications due to their superior permeability and compressive strength properties of the hardened cement paste compared to that of the less-expensive, but coarser ordinary Portland cements. Supplementary cementitious materials (SCMs) are often used to replace ultrafine cement in order to modify certain properties and to reduce costs. The aim of this experimental study is to investigate the effect of three supplementary materials: microsilica (MS), fly ash (FA), and metakaolin (MK) on the workability, and mechanical properties of an ultrafine cement based grout with a constant water-binder ratio and constant superplasticizer content. Maximum percentages of replacement with ultrafine cement were 6% by volume of cement for MS and 16% for FA, and MK. In general, results suggest that the workability is improved by addition of FA, whereas is reduced, when modified with MS and MK. The compressive strength of grout after cement replacement remains comparable to that of pure cement grout. However, there is a tendency of the MS to positively affect the compressive strength opposite to FA, whereas flexural strength is positively affected by FA. Based on the results, it is evident that grouts with Hägerman cone flow more than 500 mm and compressive strength of more than 90 MPa after 28 days can be produced.