Interactions between waste paper sludge ashes and superplasticizers based on polycarboxylates
(2016)
In many industrial nations, about two third of the paper demand is covered by recovered paper. A major process step within the treatment of waste paper is the de-inking. It is a floating process yielding paper sludge as a waste product. About 50 % of this residue is used as a fuel. In several cases it is burnt at temperature of about 850 °C and thereafter the accrued ashes are collected in the flue gas filter. During the combustion, kaolinite and calcium oxide generate gehlenite and larnite. Calcite is the main component of waste paper sludge ash (PA).The chemical and mineralogical composition of PA suggests using it as a supplementary cementitious material.
In modern construction materials technology, workability aspects gain importance, since for most modern materials the rheology and compaction ability are relevant for the operation at a hardened state. It was observed that PA significantly increases the water demand of powder systems, which can cause serious problems during the casting of mineral binder systems containing PA. It is therefore obvious that binder systems containing PA might demand for the use of superplasticizers. Superplasticizers are polymers with anionic backbone that cause electrostatic and steric repulsion effects upon adsorption on surfaces of particles and hydration phases.
In this paper interactions between superplasticizers and waste paper sludge ashes are discussed and analysed. Based on observations of changes in the zeta potential and the dispersion of the particle system, the influence of the charge density of superplasticizers is observed and time dependent effects are demonstrated.
Viscosity modifying agents: Key components of advanced cement-based materials with adapted rheology
(2022)
Viscosity modifying agents (VMAs) are essential ingredients for the production of flowable cement-based materials. This paper presents an overview of commonly used VMAs and attempts to shed some light on the underlying physics at the origin of their mechanisms of action. The main molecular parameters of VMA controlling the rheological properties of the cement pore solution are highlighted. As the mechanisms of action of VMAs in cement-based materials are closely related to their affinity with the surface of cement particles, the adsorption of the main VMA types is discussed. The effect of VMAs on flow properties and stability of cement-based materials is presented for VMAs added without any superplasticizer, and then in systems incorporating both VMAs and superplasticizers. Finally, the effect of VMAs in enhancing concrete properties to secure adequate performance of different construction applications, and perspectives for future developments of novel cement-based materials made with VMAs are showcased.
Chemical admixtures allow to the create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials. However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition. Among these admixtures, polysaccharides are most commonly used.
The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG.
The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone.
Chemical admixtures allow to create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials.
However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition.
Among these admixtures, polysaccharides are most commonly used. The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG. The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone.
Special applications like pumping, spraying or printing of concrete require the precise adjustment of very specific rheological properties at different time steps during the casting process. Superplasticizers such as polycarboxylate ethers (PCE) can be used to obtain the required flowability, which, possibly in combination with additional rheology modifying admixtures, generate the required specified consistency. However, after the application, the concrete should change the rheological properties immediately in order to avoid deformations at rest. Therefore, the use of accelerators can be effective. Accelerators influence the hydration of cementitious materials, and thus the rheological properties over the course of time and the setting.
In this paper, the influence of different accelerators on the rheology and early hydration of cement paste as well as the interaction of accelerator and PCE are presented. Methods like rheometry, needle penetration tests and practical Tests like spread flow were applied. The used accelerators showed accelerating behavior on the cement pastes without and in the presence of PCE. At the same time an influence on the rheology could be observed. This effect was less in the mixes with PCE, especially at the highest water/cement ratio (w/c).
In the last years flowable concrete has become increasingly important in applications such as, for systems with highly reinforced concrete with a complicated formwork, or sprayed concrete and 3D-printing of concrete. For all these applications it is necessary to have tailored rheological properties. Rheology can be described by values of yield stress and plastic viscosity, which can be determined for example by evaluation of rheometer measurements. But for different materials various rheometers with different geometries and stirrers are being used. To see the effects from paste in concrete, it is necessary to investigate mixes of paste, mortar and concrete, stepwise. But currently there exists no device, which is calibrated for these different systems at once. Due to this fact, conventional tests such as V-funnel efflux-time and flow diameter were determined, as well as rheometer data in different cell sizes and geometries.
In this study the assessment of rheological effects in the binder on the rheology of mortar and concrete was investigated by using combination of two rheometers.
Today, chemical admixtures like superplasticisers and stabilising agents are extremely important for modern concrete technology. These agents have meanwhile become common practice in concrete technology, but the understanding within the entire system lags far behind their application. The macroscopic rheology of concrete in the presence of superplasticizers strongly depends upon effects on a much smaller scale such as the hydration of the cement, the adsorption of superplasticizers, and the pore solution chemistry.
There is a wide range of research worldwide on supplementary cementitious materials (SCMs) such as fly ash and slag for substituting pure cement. Such materials are suitable to be considered in a cementitious system with ordinary Portland cement (OPC) due to their high pozzolanic properties. In addition, majority of the SCMs are said to significantly improve concrete properties especially in terms of increased strength and durability. Unfortunately, the production of such SCMs is not entirely eco-friendly and also limited to certain parts of the world, hence one has to look at alternative options.
The issue of availability of resources is a strong concept that is ever-increasing, and the use of more eco-friendly SCMs in a cementitious system is furthermore attractive. Hence this paper addresses the use of eco-friendly SCMs in concrete such as rice husk ash (RHA). Despite the fact that extensive research has been done on this material, its application in a cementitious system to obtain sufficient concrete properties is still rather limited. In a country like Tanzania, high strength concrete construction is applicable in special construction cases but certainly not a high priority. Majority of construction is still undertaken using normal strength concrete. In a ternary cementitious system consisting of OPC, RHA and other readily available resources such as limestone filler (LSF), normal strength concrete can still be produced having good performance and suitable for regular on-site construction. This paper explains a possible application of obtaining sufficient concrete properties from the available resources.
Over the course of the last decades, concrete construction has significantly changed from mass application towards sophisticated more innovative, future oriented, and performance based materials technology. Today concrete no longer consists of cement, water, and aggregates, but can be enhanced significantly by using supplementary additions and chemical admixtures. Advancements in admixtures eventually facilitated the development of new concrete types such as self-compacting concrete (SCC) and high performance concrete (HPC) by uncoupling the workability from the water-cement ratio (w/c).
While for traditional concrete types the major mixture parameter for the workability and strength were the w/c and the grading of the aggregates, for SCC and HPC the performance parameters are more complicated and the performance depends highly on the powder components. This makes the system more sophisticated and in parallel more prone to scatter during the production. The complexity and difficulty to predict the effects of changes in the process and mixture makes it very difficult to identify the right potentials for savings.
Concrete of today has only little in common with the traditional concrete used a few decades ago. It has become a high performance material, which can be adjusted for high performance applications and according to ultimate user specifications. The reason for the rapid evolvement was the increasing awareness about how the rheology of concrete can be improved without negatively affecting the mechanical properties of concrete by chemical admixtures.