Control chart systems are used in quality management systems to keep production processes stable. In concrete production they are often applied for the control of the compressive strength. The most efficient control chart systems are cumulated sums (cusum), which help to observe deviations from a targeted value. Unlike alternative observation chart systems that focus on process data evaluation, cusum observations react very rapidly on systematic process changes in processes. Therefore, the cusum method is particularly suitable if immediate counteractions have to be taken, like in the case of fresh concrete properties of self-compacting concrete (SCC), which can have severe influences on the durability and mechanical strength of concrete. The rheology of SCC can be affected by an enormous variety of influencing factors, from raw material properties to handling or environmental temperature. The present study shows that regardless of the material based influencing parameter for a rheology change, a steady slump flow can be achieved only by adding supplementary superplasticizer in case of loss of flow and adding stabilising agent (ST) in case of increased flow if the respective V-mask indicates a systematic change. A reference SCC was artificially manipulated in order to achieve realistic experimental data for flowability and flowability changes due to changes in the raw material properties. The results point out that productions with applied cusum methods were capable of keeping the target slump flow deviation within approximately 1% only, while productions without applied cusum method deviated up to 14% and more from the target.
After a brief introduction into past and modern concrete, the relevance of sustainable concrete technologies is emphasised from a global perspective. In order to minimise the environmental impact of cement and concrete in the world, solutions for alternative binder materials as well as rheology and performance modifying additives are presented based on local bio-based resources.
However, the perception of bio-based constituents is typically rather negative in construction materials and its application is often limited to low-end construction. In order to show that this is not inevitable, the lecture ends with a number of case studies for the use of bio-based materials for high performance concrete applications.
Polymers that help tailoring rheological properties during the casting process have become inevitable constituents for all kinds of high-performance concrete technologies. Due to lacking industries, these typically crude-oil based admixtures are not readily available in many parts of the world, which limits the implementation of more sustainable high-performance construction technologies in these regions. Alternative polymers, which often demand for less processing, can be derived from local plant-based resources. The paper provides experimental data of flow tests of cement pastes with polysaccharides from Triumfetta pendrata A. Rich, acacia gum and cassava without and in the presence of polycarboxylate ether superplasticizer. The flow tests are amended by observations of the zeta potentials and the hydrodynamic diameters in the presence of and without calcium ions in the dispersion medium. The results show that in the presence of and without calcium ions all polysaccharides provide negative zeta potentials, yet, they affect flowability and thixotropy in different ways. Cassava starch, acacia gum, and the gum of Triumfetta pendrata A. Rich qualified well for robustness improvement, strong stiffening, and additive manufacturing, respectively. The reason for the different effects can be found in their average sizes and size distribution. Due to the promising results, a flow chart for local value chains is derived on the example of yet unused cassava wastes, which can be converted in parallel.
Concrete technology was exposed to a rapid development during the last three decades. For the longest time in its history, concrete was considered as a three component System consisting of aggregates, which are bound by the hardened cement paste consisting of hydrated cement. Traditionally, the only way of adjusting the consistency of concrete was using well adjusted aggregates and grading curves and adding excess water to the concrete, accepting that the latter in return reduces strength and durability. During the last three decades, however, concrete has developed further from a three component System towards an (at least) five component system, since the use of mineral additions and Chemical admixtures has become state of the art. Both components are able to enhance the workability, the compactability, and the density of the microstructure with effects on strength, ductility and durability, while cement can be saved in parallel. Due to reasonable use of admixtures and additions, concrete can be designed to match mechanically high performance specifications. Traditionally, cement paste was considered the weakest component in concrete. Flowever, in modern concrete a good paste composition can yield highest performance, passing the role of the mechanical bottleneck towards the aggregates.
Clearing the way
(2012)
With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes.
In order to observe the effect of the aggregate phases between 2 mm and 16 mm without overlap with rheological effects induced by the cement hy-dration and without interactions with a threshold fine sand particle size that affects both, paste and aggregates, rheological experiments were conducted on a limestone filler based paste mixed with aggregates up to 16 mm. Vari-ous aggregate fractions were blended and mixed with the replacement paste in different volumetric ratios.
The dry aggregates’ flow coefficients were determined and compared to yield stress and plastic viscosity values at different aggregate volume fractions. The results indicated that the flow coefficient is not a suitable parameter to predict the performance of the aggregates in the paste. It was shown that the yield stress of pastes is largely determined by the blend of different aggregate fractions, while the plastic viscosity to large extend depends upon the coars-est aggregate fraction.
Based on the results, ideal aggregate composition ranges for minimised yield stress are presented. For the plastic viscosity no such grading curves to achieve minimum values could be found, but high viscosity curves are identified.
Structural design and application have always been linked to the compressive strength of concrete as the main relevant criterion. This was justifiable in the past, where concrete consisted of water, ordinary Portland cement and aggregates, but this concept is no longer relevant for modern and more sustainable cement and concrete.
Despite these new developments, existing standards, guidelines and academic curricula have not been much updated and are still used worldwide. There is a need to change this situation by proper education of the users.
This overview describes the challenges that arise at a user Level from the higher complexity of modern concrete, and defines needs and requirements for enhanced applicability of sustainable concrete concepts.
Furthermore, recommendations are given on how better concrete practice can be communicated to all the involved parties, from civil and design engineers to constructors and site-appliers on the construction site.