Filtern
Erscheinungsjahr
- 2017 (19) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (7)
- Vortrag (7)
- Zeitschriftenartikel (4)
- Forschungsbericht (1)
Sprache
- Englisch (19)
Schlagworte
- Cement (14)
- Rheology (9)
- Concrete (8)
- Sustainability (5)
- Polysaccharides (4)
- Admixtures (3)
- Africa (3)
- Bio-based materials (3)
- Starch (3)
- Superplasticizer (3)
Eingeladener Vortrag
- nein (7)
Rising temperatures worldwide pose an increasing challenge for safe and healthy living conditions. Particularly inner cities have been affected by these environmental changes because of the materials used to build houses, streets and infrastructure. The most common building material is concrete. It shows a specific heat capacity, while the heat conductivity for Standard concrete is low. Thus, the use of concrete generates a high capacity of heat storage. In addition, extensive soil sealing also contributes to the temperature rise of inner city areas compared to
their surroundings. To mitigate this so-called urban heat island effect, a self-cooling concrete paver was developed. This paver is able to store water. The evaporation of the water at elevated temperatures provides a cooling effect. This paper focuses on determination of this new paver’s capability to cool the surface and the surrounding. The new paver’s cooling Qualities were analysed in a series of laboratory tests. To prove the results outside of laboratory conditions, two fields (12 m × 8 m) with self-cooling and reference pavers were installed in Spain.
This paper presents and discusses the results of the tests. Correlation between reduced surface temperature of the self-cooling concrete pavers and the air temperature is examined.
Chemical admixtures allow to the create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials. However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition. Among these admixtures, polysaccharides are most commonly used.
The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG.
The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone.
Chemical admixtures allow to create a variety of fresh and hardened state properties in cementitious materials. In the case of self-compacting concrete, plasticizers or superplasticizers are introduced with the aim to decrease the yield stress and the viscosity of the materials.
However, in order to prevent segregation and bleeding, and to improve the water retention of cement-based system, stabilizing agents or viscosity agents are often introduced in addition.
Among these admixtures, polysaccharides are most commonly used. The aim of this study is to provide an understanding of competitive or synergetic effects induced by the combination of hydroxypropyl guar stabilizing agents (HPG) and superplasticizers on cement pastes. Two polycarboxylate superplasticizers (PCE) exhibiting different charge densities and one HPG were studied. It was found that the combination of HPG with PCE superplasticizer strongly affects the rheological behavior of cement pastes. Despite the presence of HPG, the viscosity of the pastes strongly decreased with increasing dosage of PCE until it became close to the viscosity of a cement paste with PCE only. However, the use of HPG in combination with PCE allows maintaining a significant yield stress in the cement paste compared to PCE alone. The increase in the charge density of the PCE seemed to amplify the drop of the viscosity and to reduce the gain on the yield stress induced by HPG. The results also highlight a delay in the setting-time of the cement paste by adding HPG and PCE. The delay induced by HPG is significantly lower than that generated by PCEs. However, the combination of the both kind of admixtures leads to a slightly shorter setting-time compared to the PCE alone.
The paper showed that the STA behave completely different in pastes with LSF and cement, respectively, as well as with or without PCE. While STA can affect plastic viscosity and yield stress in LSF and cement pastes, the addition of PCE causes that the STA have mainly an impact on plastic viscosity, except DGUM and ST-low. The performance of STA in LSF and cementitious systems can vary greatly due to different ionic strengths of the liquid phase. The charges due to modification of the starches have an intense influence on the rheological properties in pastes. The combined use of PCE and STA can lead to a significant increase of the plastic viscosity without a strong effect to the yield stress.
For the evaluation of the effectivity of STA the ionic strength of the liquid phase and the solid volume fraction of the binder have to be taken into account. Further influences can arise from grain size and aggregate content as well as the temperature, which were not discussed in this paper.
Superplasticizers (SPs) have been employed in concrete technology for decades to improve the workability of concrete in its fresh state. The addition of SPs in cement-based systems affects the early properties. Although the interaction of the cement particles with various SPs has been extensively researched, there still exists limited research on the interaction of SPs with supplementary cementitious materials such as rice husk ash (RHA). This paper investigates the rheological properties and early hydration kinetics of RHA-blended systems with three types of SPs, a polycarboxylate ether (PCE) and two lignosulphonates (LS-acc and LS-ret). In rheological properties, the addition of SP causes an initial improvement of workability as the yield stress is significantly reduced. The pastes with PCE and LS-acc show a slight increase of yield stress over time whereas pastes with LS-ret tend to lower the yield stress slightly over time, further improving the workability. Without SP, pastes with RHA show a lower yield stress but an increase in plastic viscosity as cement is further replaced with RHA. The addition of the LS SPs is observed to lower the plastic viscosity but remains constant with further replacement of cement with RHA. This indicates that LS SPs further adsorbs on RHA particles and hydration products produced causing dispersion of the particles
within the system. In early hydration kinetics, pastes with PCE retard hydration and the degree of retardation is further increased with LS SPs. In the presence of RHA, the retardation of LS SP systems is significantly reduced. The pastes with PCE show more ettringite in the SEM micrographs, but is observed to be shorter needles. This indicates an initial good workability for PCE. However, C-S-H and CH were observed to be low in quantity, whereby the pastes with LS show more nucleation sites for C-S-H and CH. The ettringite needles in the LS systems were similar in quantity and more elongated in some cases but not abundant as in the PCE systems.
Rice husk as (RHA) is an eco-friendly material, which can be used as a supplementary cementitious material (SCM) in cement and concrete. Due to the high water demand for the material, superplasticizers (SPs) are essential to improve the performance. However, the interaction between the SPs and RHA systems is limited. This paper investigates the interaction of the binders with three SPs, i.e. two polycarboxylate ethers (PCEs) and one lignosulphonate (LS). The investigations are performed on blended systems of mortar containing various percentages of RHA and limestone powder (LSP). LSP is used in this research to improve the workability of the mortar. The results from the zeta potential (ZP) shows that the SPs are extremely dependent on the pH of the suspension. At higher pH values such as in a cementitious system, the ZP becomes less negative indicating that the ions in the suspension interact with the carboxyl groups in the backbone of the polymers thus reducing the surface charges of the SP. The mini-slump flow shows that the workability of the blended mortar systems is significantly improved with the addition of SPs. LS systems with increasing RHA is observed to have similar workability as the control mix over time. The compressive strength test results show increased strength for all mortar specimens with added RHA and LSP at later ages.
Potentials for sustainable cement and concrete technologies - Comparison between Africa and Europe
(2017)
Cement and concrete technologies in Africa provide vast potentials for sustainable future technologies as well as enormous challenges. The main focus of the symposium is to address existing challenges, possible solutions, and future potentials with all participants. This symposium also aims at offering a platform for networking with relevant players in science and industry.
With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes.
The African cement, concrete and construction business are growing at rapid pace. The cement sales are expected to grow tremendously until 2050. The number of newly built cement plants increases dramatically and in addition more cements are being imported from outside the continent, e.g. from Turkey, Pakistan, Indonesia, and China, driven by overcapacities in the countries of origin. This causes a high number of potentials and challenges at the same time. New cement plants can operate directly at best technological state of the art and thus incorporate more sustainable technologies as well as produce new and more sustainable products such as cements blended with sustainable supplementary cementitious materials such as calcined clays, and industrial or agricultural by products. At the same time the new variety of binding agent as well as the international imports, which are driven by price considerations, make the cement market prone to quality scatter. This puts pressure on the quality control regulations and institutions to ensure safety of construction, healthy application, and environmental safety for the population.
The paper presents possible solutions to build up the rapidly increasing African cement production more sustainably than in the rest of the world as well as the related challenges and obstacles that need to be overcome. Based on experiences with a series of pan-African cement testing laboratory proficiency schemes conclusions are made on technical, regulative and political level.
After a brief introduction into past and modern concrete, the relevance of sustainable concrete technologies is emphasised from a global perspective. In order to minimise the environmental impact of cement and concrete in the world, solutions for alternative binder materials as well as rheology and performance modifying additives are presented based on local bio-based resources.
However, the perception of bio-based constituents is typically rather negative in construction materials and its application is often limited to low-end construction. In order to show that this is not inevitable, the lecture ends with a number of case studies for the use of bio-based materials for high performance concrete applications.