Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (83) (entfernen)
Referierte Publikation
- nein (83) (entfernen)
Schlagworte
- Rheology (23)
- Cement (21)
- Concrete (14)
- Superplasticizer (7)
- Admixtures (6)
- Africa (6)
- Polycarboxylate ether (6)
- Rheologie (6)
- Self-compacting concrete (6)
- Sustainability (6)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (20)
- 7.4 Baustofftechnologie (17)
- 6 Materialchemie (5)
- 6.6 Physik und chemische Analytik der Polymere (5)
- 7.0 Abteilungsleitung und andere (3)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.2 Biophotonik (2)
- 8 Zerstörungsfreie Prüfung (2)
- 8.0 Abteilungsleitung und andere (2)
- 7.2 Ingenieurbau (1)
Influence of the hydroxypropylation of starch on its performance as viscosity modifying agent
(2022)
Synopsis: Starch is a commonly used viscosity modifying agent (VMA). The performance of starch as VMA depends on its origin (e.g. potato, corn, cassava, etc.) and corresponding molecular properties, such as molecular weight, ratio between amylose and amylopectin etc. Depending upon the application, the efficiency of starch can be enhanced by hydroxypropylation. The maximum degree of substitution (DoS) cannot be greater than 3.0, which is the number of hydroxy groups per glucose monomer in the polymer. In the current research three potato starches exhibiting the DoS of 0.4, 0.6 and 0.8 were utilised. The influence of the modified starch on the rheological properties and hydration of cement paste, as well as the viscosity of the pore solution were investigated. Our findings show that the starch with the highest DoS increases the dynamic yield stress the most, while the plastic viscosity is less dependent on the DoS. Additionally, starch with the highest DoS retards hydration to lower degree than other starches.
Synopsis: The paper presents the results of a study on the influence of agitation on the structural build-up of fresh cement pastes using a penetration test. It first presents results about the influence of the penetrating shape’s geometry on the influence on the cement paste specimen. Then, results are shown for the load-deflection curves depending upon time and agitation before testing. Based on the observation of the force required to penetrate the sample, conclusions on the structural build-up can be made. The observations were made over the course of time with samples that were left at rest and partly agitated before testing at different time steps. The setup allows to identify the contribution of the chemical reaction to the structural build-up process. The presence of superplasticizer obviously reduces the load that cement paste can withstand, while the loss of thixotropy is found notably lower than that of neat cement pates
Polysaccharides are important rheology modifying admixtures in the building material sector.
The use of starch is becoming increasingly important, due to many ecological and economic advantages. In the construction sector, starch ethers are being used as thickeners and as means to increase the yield stress. The starch ethers that are available on the market differ in
their behaviour, which can vary greatly depending upon the binder system and mortar composition, e.g. solid volume content, binder type, additional admixtures. In view of the limited knowledge about the influence of molecular modifications associated with cement based systems, some fundamental rheological functional mechanisms were analysed in this study. The differently modified starch ethers used were derived from potatoes. They varied in their charges and degrees of hydroxypropylation. The setting and the flow behaviour of all examined variations
of starch ethers were analysed in cement pastes. In order to illustrate the effects of the starch ethers that were used, the water-cement ratio (w/c) was held constant in all the mixtures [Schmidt 2012]. The results indicated significant differences in setting and flow behaviour.
This study focuses on concrete flow in presence of obstacles and develops a mathematical model and a computational approach for SCC flow through reinforced formworks. In order to decrease high computational times needed to simulate castings through reinforced elements, an innovative approach to model the reinforced sections as porous media is proposed here. In the previous work, this numerical model is proved able to simulate the free-surface flow of non-Newtonian fluids through the reinforcement networks. In the present study, the applicability of the model on the concrete flow will finally be proved. The large-scale form-filling experiments with SCC will be conducted and the experiments will be simulated using the proposed numerical model. The numerical model will then be validated through the comparison of the experimental results and the results of the numerical simulations.
The paper addresses numerical modelling of fresh self-compacting concrete. In the previous studies, a numerical tool for casting prediction is built based on the assumption that fresh concrete behaves as a yield-stress fluid and treating zones with rebars as porous media. The present contribution discusses the determination of material parameters, which are required as an input for numerical simulations of casting processes.
South Africa and recently Nigeria are the only net exporter of cement in Africa, yet cements are imported into the country mainly on the basis of price competitiveness. This poses potential for scatter in the properties of the cements in the South African market as pricing seems to be the only determining factor that affects Portland cements imported. A survey of cements of grade 42.5N in the South African cement market was carried out to identify major players in the industry. The identified cements, which included four locally produced and one imported cement were then analysed for both chemical composition and physical properties in line with the Eurocode EN 196. Tests carried out include loss on ignition, chloride content, sulphate content, specific surface (Blaine), standard consistence, initial setting time, final setting time, soundness and flexural and compressive strength at 2, 7 and 28 days. The testing program was initiated as part of on-going Africa-wide cement testing competency program in partnership with BAM and PTB in Germany. The performance of the identified cements from the different local manufacturers and the imported cement were analysed and are presented in this paper. These results reveal some similarities and differences in the properties. Particularly of interest is the marked difference in the 28 days compressive strength of the cements. This paper shows that there is need for further tests across the cement industry as some of the cements failed to meet certain requirement as set by EN 196. The paper also recommends the use of proficiency testing schemes in the cement industry of the country to ensure the cement laboratories are providing results of high quality and at the same time act as a check to make sure these laboratories are not failing to meet standard requirements.
Influence of the type of viscosity-modifying admixtures and metakaolin on the rheology of grouts
(2013)
The Viscosity-modifying admixtures (VMAs) contribute to the control of the rheology of grouts and are used to enhance plastic viscosity, cohesion, stability, and resistance to bleeding of cement-based systems. This paper reports the results of an investigation on the effect of type of VMAs, namely two types of diutan gums and a welan gum and metakaolin (MTK), plus a superplasticiser, on the rheology behaviour of cement grouts. All mixes were made with polycarboxylic superplasticiser at 0.6% and 0.9%. The dosages of VMAs were 0.05%, and 0.10%, with a fixed water-to-binder ratio of 0.40. The investigated fresh properties of the grouts included the mini-slump flow, plate cohesion, and rheology parameters: namely yield value and plastic viscosity. The rheological parameters were obtained using a vane viscometer. Control grouts (with and without superplasticiser and VMA) were also tested and compared to mixes containing VMAs. The results indicated that the incorporation of MTK reduced the fluidity and increased the plate cohesion and yield stress, and plastic viscosity due to the higher surface area of MTK. The diutan gum grouts improved the grout fresh properties and rheology compared to the welan gum grouts.
Grouting is a universal repair and strengthening technique, which is constantly used for structural remediation of concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. Having an extremely small particle size of only few microns, ultrafine cements are ideal for grouting applications due to their superior permeability and compressive strength properties of the hardened cement paste compared to that of the less-expensive, but coarser ordinary Portland cements. Supplementary cementitious materials (SCMs) are often used to replace ultrafine cement in order to modify certain properties and to reduce costs. The aim of this experimental study is to investigate the effect of three supplementary materials: microsilica (MS), fly ash (FA), and metakaolin (MK) on the workability, and mechanical properties of an ultrafine cement based grout with a constant water-binder ratio and constant superplasticizer content. Maximum percentages of replacement with ultrafine cement were 6% by volume of cement for MS and 16% for FA, and MK. In general, results suggest that the workability is improved by addition of FA, whereas is reduced, when modified with MS and MK. The compressive strength of grout after cement replacement remains comparable to that of pure cement grout. However, there is a tendency of the MS to positively affect the compressive strength opposite to FA, whereas flexural strength is positively affected by FA. Based on the results, it is evident that grouts with Hägerman cone flow more than 500 mm and compressive strength of more than 90 MPa after 28 days can be produced.
Chemical admixtures like superplasticisers or stabilising agents are of ever increasing importance for modern concrete technology. They liberate the workability of concrete from its dependency on water content, and thus, open the gate towards innovative and future oriented concrete technologies such as self-compacting concrete.
Today, admixture addition has become common practice in concrete technology, but the understanding of their highly complex mode of operation is extremely difficult and demands for understanding of processes within the range between nanometres and centimetres.
Due to its complex time-dependent, multi-phase and multi-scale behaviour, flowable concrete systems are highly complicated and cannot be described comprehensively by simple models. It is therefore extremely challenging to identify the relevant parameters that predominantly control flow phenomena on different size scales, since these may occur on any scale between the nano scale (e.g. superplasticizer adsorption) and macro scale (e.g. grading of the aggregates). The present study discusses fundamental mechanisms at the interface between particle or hydrate surfaces and the fluid phase at a very early stage of concrete formation, and links these effects to macroscopic flow phenomena. Methods are discussed that appear promising interdisciplinary tools for enhancement of the understanding of the relevant interactions that are responsible for the macroscopic flow of flowable concrete.