Filtern
Dokumenttyp
- Zeitschriftenartikel (10)
Sprache
- Englisch (9)
- Mehrsprachig (1)
Referierte Publikation
- ja (10) (entfernen)
Schlagworte
- Magnesium (3)
- Additive manufacturing (2)
- Biodegradation (2)
- Corrosion (2)
- Plasma-chemical oxidation (2)
- SAXS (2)
- 3D-Printing (1)
- Adhesion (1)
- Adhesives (1)
- Adsorption (1)
Organisationseinheit der BAM
- 6 Materialchemie (3)
- 5 Werkstofftechnik (2)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.5 Proteinanalytik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 6.7 Materialsynthese und Design (1)
- 7 Bauwerkssicherheit (1)
- 7.0 Abteilungsleitung und andere (1)
As bio-absorbable implant material the magnesium alloy Mg-1Ca is able to degrade in-vivo. The mechanical properties of this alloy are similar to those of human bone; both Mg and Ca are essential elements in human body. The main problem is the high corrosion rate of this alloy. Two coating systems based on plasma-chemical oxidation and an organic dip coating are applied onto MgCa1.0 magnesium alloy in order to slow down the corrosion rate. The corrosion behaviour of the coated alloys was investigated with electrochemical noise measurements. The influence of hydrogen evolution and increasing pH-value on the cytotoxicity was examined. The results of these investigations suggest that a combination of both coating systems leads to promising degradation properties.
The degradation behaviour of an Mg-1Ca alloy is investigated in vitro to figure out the possibilities of influencing the degradation behaviour of such an alloy by applying heat treatment as well as the use of a coating system based on plasma-chemical oxidation. It is shown that an optimised solution annealing (T4-heat treatment) can reduce the degradation rate while an additional ageing between 240 and 300 °C (T6-heat treatment) increases it. A coating generated by plasma-chemical oxidation reduces the degradation rate in the immersion test. Its effect is depending on the former heat treatment of the Mg-1Ca alloy as well as on the parameter during plasma-chemical oxidation.
Wollastonite (CaSiO 3 ) – diopside (CaMgSi 2 O 6 ) glass-ceramic scaffolds have been successfully fabricated using two different additive manufacturing techniques: powder-based 3D printing (3DP) and digital light processing (DLP), coupled with the sinter-crystallization of glass powders with two different compositions. The adopted manufacturing process depended on the balance between viscous flow sintering and crystallization of the glass particles, in turn in fluenced by the powder size and the sensitivity of CaO – MgO – SiO 2 glasses to surface nucleation. 3DP used coarser glass powders and was more appropriate for low temperature firing (800 – 900 °C), leading to samples with limited crystallization. On the contrary, DLP used finer glass powders, leading to highly crystallized glass-ceramic samples. Despite the differences in manufacturing technology and crystallization, all samples featured very good strength-to-density ratios, which bene fit theiruse for bone tissue engineering applications. The bioactivity of 3D-printed glass-ceramics after immersion in simulated body fluid and the similarities, in terms of ionic releases and hydroxyapatite formation with already validated bioactive glass-ceramics, were preliminarily assessed.
Ordered mesoporous silica materials such as COK-12, analogous to the well-known SBA-15, are characterized by high surface areas and unique features such as defined pore sizes in the meso-size range and high pore ordering.
The aim of this work was to prove the washing step and choice of calcination and aging temperature during the COK-12 synthesis as effective tools in tailoring, markedly improving the specific surface area, pore size, and pore volume. By controlling the aging temperature, the pore size was linearly adjusted between 5.7 and 8.1 nm, while preserving the hexagonal ordering of the pores. The synthesized COK-12 powders possess pore volumes and specific surface areas up to 1.23 cm3 g−1 and 860m2 g−1, respectively, which is markedly higher than what has previously been reported about COK-12. The presented results and the environmentally friendly character of the synthesis will make COK-12 more interesting for future adaption to the industrial processes, for example in catalysis, adsorption, or drug delivery.
The main problem limiting the application of magnesium alloys as biodegradable implant material is its high degradation rate. In order to slow down the corrosion rate an extrusion process and specific coating systems based on plasma-chemical oxidation (PCO) and organic dip coating with poly(ʟ-lactid-co-caprolacton) (PLLC) were applied on Mg–1Ca magnesium alloy. The additional PLLC coating is used to delay the start of substrate corrosion, while the purpose of the PCO coating is to decrease the substrate corrosion rate. The corrosion behaviour was investigated in synthetic body fluid (SBF) through measurement of the hydrogen evolution rate in long term tests and polarisation and electrochemical noise measurements in short term tests. The results showed significant differences between the cast and extruded alloys and a decrease of the corrosion rate due to corrosion product formation. The combination of both coating systems resulted in a significant delay of metal substrate corrosion and all coating systems showed good correlation between short and long term tests. The combination of the three investigation methods provides the possibility to gain more information about the degradation behaviour and break down of protective coatings.
We report on a new series of isoreticular frameworks based on zinc and 2-substituted imidazolate-4-amide-5-imidate (IFP-1–4, IFP=imidazolate framework Potsdam) that form one-dimensional, microporous hexagonal channels. Varying R in the 2-substitued linker (R=Me (IFP-1), Cl (IFP-2), Br (IFP-3), Et (IFP-4)) allowed the channel diameter (4.0–1.7 Å), the polarisability and functionality of the channel walls to be tuned. Frameworks IFP-2, IFP-3 and IFP-4 are isostructural to previously reported IFP-1. The structures of IFP-2 and IFP-3 were solved by X-ray crystallographic analyses. The structure of IFP-4 was determined by a combination of PXRD and structure modelling and was confirmed by IR spectroscopy and 1H MAS and 13C CP-MAS NMR spectroscopy. All IFPs showed high thermal stability (345–400°C); IFP-1 and IFP-4 were stable in boiling water for 7 d. A detailed porosity analysis was performed on the basis of adsorption measurements by using various gases. The potential of the materials to undergo specific interactions with CO2 was investigated by measuring the isosteric heats of adsorption. The capacity to adsorb CH4 (at 298 K), CO2 (at 298 K) and H2 (at 77 K) at high pressure were also investigated. In situ IR spectroscopy showed that CO2 is physisorbed on IFP-1–4 under dry conditions and that both CO2 and H2O are physisorbed on IFP-1 under moist conditions.
Phage display biopanning with Illumina next-generation sequencing (NGS) is applied to reveal insights into peptide-based adhesion domains for polypropylene (PP). One biopanning round followed by NGS selects robust PP-binding peptides that are not evident by Sanger sequencing. NGS provides a significant statistical base that enables motif analysis, statistics on positional residue depletion/enrichment, and data analysis to suppress false-positive sequences from amplification bias. The selected sequences are employed as water-based primers for PP-metal adhesion to condition PP surfaces and increase adhesive strength by 100% relative to nonprimed PP.
Mechanically stable structures with interconnected hierarchical porosity combine the benefits of both small
and large pores, such as high surface area, pore volume, and good mass transport capabilities. Hence, lightweight micro-/meso-/macroporous monoliths are prepared from ordered mesoporous silica COK-12 by means of spark plasma sintering (SPS, S-sintering) and compared to conventionally (C-) sintered monoliths. A multi-scale model is developed to fit the small angle X-ray scattering data and obtain information on the hexagonal lattice parameters, pore sizes from the macro to the micro range, as well as the dimensions of the silica population. For both sintering techniques, the overall mesoporosity, hexagonal pore ordering, and amorphous character are preserved. The monoliths' porosity (77–49%), mesopore size (6.2–5.2 nm), pore volume (0.50–0.22 g cm-3
), and specific surface area (451–180 m2 g-1) decrease with increasing processing temperature and pressure. While the difference in porosity is enhanced, the
structural parameters between the C-and S-sintered monoliths are largely converging at 900 C, except for the mesopore size and lattice parameter, whose dimensions are more extensively preserved in the
S-sintered monoliths, however, coming along with larger deviations from the theoretical lattice. Their higher mechanical properties (biaxial strength up to 49 MPa, 724 MPa HV 9.807 N) at comparable porosities and ability to withstand ultrasonic treatment and dead-end filtration up to 7 bar allow S-sintered monoliths to reach a high permeance (2634 L m-2 h-1 bar-1), permeability (1.25 x 10^-14 m2), and ability to reduce the chemical oxygen demand by 90% during filtration of a surfactant-stabilized oil in water emulsion, while indicating reasonable resistance towards fouling.
The round robin test investigated the reliability users can expect for AlSi10Mg additive manufactured specimens by laser powder bed fusion through examining powder quality, process parameter, microstructure defects, strength and fatigue. Besides for one outlier, expected static material properties could be found. Optical microstructure inspection was beneficial to determine true porosity and porosity types to explain the occurring scatter in properties. Fractographic analyses reveal that the fatigue crack propagation starts at the rough as-built surface for all specimens. Statistical analysis of the scatter in fatigue using statistical derived safety factors concludes that at a stress of 36.87 MPa the fatigue limit of 107 cycles could be reached for all specimen with a survival probability of 99.999 %.
Reclassification of bridges, i.e., a change in load rating, using reliability-based methods and a direct update with proof load information has been presented by many authors. However, bridge reclassification has hardly been studied from a decision analytic perspective, i.e., with quantification of the risks and benefits of different classification choices, and the expected benefit gain from proof loading. We derive, explain and exemplify a decision analytic approach for bridge reclassification along with models for (1) elastic and ultimate capacity and their adaptation with proof load information, (2) proof load information with classification outcomes accounting for target reliabilities and, (3) utilities including socio-economic benefits from reclassification. The approach and models are exemplified with a case study based on reclassification of bridges with a low existing classification. Decision rules, for practical use by a highway authority to find the optimal classification, are identified and documented based on: (1) the measurement of the capacity at elastic limit by proof loading, (2) the bridge reclassification benefits, and, (3) the required annual reliability level. From a Value of Information analysis, it is concluded that the proof load information is highly valuable for reclassification in cases of high socio-economic benefits and high reliability requirements.