- Flame retardant (5)
- Weathering (4)
- Durability (3)
- Aluminum hydroxide (ATH) (2)
- Cables (2)
- EVA (2)
- Ethylene-vinyl acetate (2)
- Fire resistance (2)
- Flame retardancy (2)
- Flammschutz (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (3)
Fire resistance testing of components made of carbon fibre reinforced polymers (CFRP) usually demands intermediate-scale or full-scale testing. A bench-scale test is presented as a practicable and efficient method to assess how different fire protective systems improve the structural integrity of CFRPs during fire. The direct flame of a fully developed fire was applied to one side of the CFRP specimen, which was simultaneously loaded with compressive force. Three different approaches (film, non-woven, and coatings) were applied: paper with a thickness in the range of μm consisting of cellulose nanofibre (CNF)/clay nanocomposite, nonwoven mats with thickness in the range of cm and intumescent coatings with a thickness in the range of mm. The uncoated specimen failed after just 17 s. Protection by these systems provides fire stability, as they multiply the time to failure by as much as up to 43 times. The reduced heating rates of the protected specimens demonstrate the reduced heat penetration, indicating the coatings’ excellent heat shielding properties. Bench-scale fire stability testing is shown to be suitable tool to identify, compare and assess different approaches to fire protection.
The durability of flame retardancy is a challenge for cables over long lifetimes. The degradation of flame retardance is investigated in two kinds of exposures, artificial weathering and humidity. In this basic study, typical mineral flame retardants in two polymers frequently used in cable jackets are investigated to get the fundamental picture. Aluminum hydroxide (ATH) and magnesium hydroxide (MDH) are compared in ethylene‐vinyl acetate (EVA), and further in EVA and linear low‐density polyethylene (LLDPE) cables containing the same ATH. The changes in chemical structure at the surface are studied through attenuated total reflectance Fourier transform infrared spectroscopy (ATR‐FTIR), the formation of cracks, and changes in color are investigated. The cone calorimeter and a bench scale fire testing cable module are utilized to evaluate the fire behavior of the cables. Although the flame retardancy deteriorated slightly, it survived harsh exposure conditions for 2000 h. Compared to EVA/MDH and LLDPE/ATH, the fire behavior of EVA/ATH is the least sensitive. Taken together, all of the results converge to estimate that there will be no problem with flame retardancy performance, for materials subjected to natural exposure for several years; the durability of fire retardancy is questionable for longer periods, and thus requires further investigation.
Biomass pre-treatments for bio-oil quality improvement are mainly based on thermal and chemical methods which are costly and hence reduce the sustainability of pyrolysis-based refineries. In this paper, anaerobic digestion (AD) and dark fermentation (DF) are proposed as alternative ‘green’ pre-treatments to improve this situation. For this purpose, three seaweeds namely Sargassum polycystum, (Phaephyta), Gracilaria tenuistipitata, (Rhodophyta) and Ulva reticulata, (Chlorophyta) with high ash and oxygen contents were pre-treated to improve their composition and structure prior to pyrolysis. The results reveal that both biological pre-treatments affected, positively, the composition and structure of the seaweed biomass with AD pre-treatment reducing N and S contents by 86% and 63%, respectively. DF was more efficient in terms of ash and moisture reduction with 25% and 70%, respectively. In addition, oxygen (O) reduction by 27% was observed after DF which was evidenced by FTIR spectroscopy indicating the reduction of most oxygen-containing functional groups in the biomass. On the other hand, the carbon (C) content increased in DF pre-treated seaweeds up to 42%, almost two times higher relative content than C in the raw seaweed. The changes in the composition of pre-treated seaweeds resulted in changes in their thermal degradation and the volatile profiles produced during pyrolysis. Interestingly, anhydrosugars and furans which account for some 70% (by area) in raw seaweeds markedly declined or become undetectable after DF pre-treatment and correspondingly more acetic acid and hydrocarbons were produced while after AD more aromatics with high toluene content (ca.17%) were generated. The results indicate that biooil with profiles more similar to petroleum-based composition i.e. rich in hydrocarbons and low in anhydrosugars, N and S can be generated by AD and DF pre-treatments and opens up the possibility of these approaches to effect cost reduction in the overall generation of bio-based fuels.
Three novel liquid ethyl (diethoxymethyl)phosphinate derivatives (EDPs) were synthesized and incorporated into flexible polyurethane foams (FPUFs). The flame retardancy of FPUFs were evaluated by limiting oxygen index (LOI), vertical burning and cone calorimetry tests, and the results indicated the structure-flame retardancy relationship of EDPs. Among these EDPs, P-(diethoxymethyl)-N-phenylphosphonamidate (EDPPA) exhibited the best flame retardant effect, methyl 3-((diethoxymethyl)(ethoxy)phosphoryl)propanoate (EDPMA) the second, and ethyl phenyl (di-ethoxymethyl)phosphonate (EDPPO) the worst. When the incorporation of EDPPA was 10 wt%, the FPUFs could self-extinguish and pass the vertical burning test. Meanwhile, the LOI value of FPUF-PA increased to 23.6% with 20 wt% loading of flame retardant. According to the investigation of volatiles during the thermal degradation of FPUFs and the morphologies of char residues after cone test, we inferred the pos- sible flame retardant mechanism. The results indicated that EDPs could release phosphorus-containing compounds in the gas phase, which would generate phosphorus-containing radicals and play the role of radical scavenger. In the condensed phase, EDPs can promote the formation of dense, intact and thermal stably char layer on the surface of FPUFs. Moreover, we found that the structure influence on flame retardancy was attributed to the atoms linked to the central phosphorus. Our results indicate that these EDPs are promising flame retardants in FPUFs that can be applied to improve the flame retardancy of FPUFs in various practical applications.