We present surface micro-modifications of bariumalumoborosilicate glasses with a high transformation temperature near 700 °C. Laser processing of the glass substrate was realized by using ultra-short laser pulses at 800 nm. The morphological conversion of the laser-treated surfaces was characterized by scanning force microscopy and nano-indentation. A hardness increase by at least a factor of six on the laser ablation crater edge relative to illuminated non- ablated areas shows that the material in the crater walls underwent drastic morphological and mechanical changes. In this heat- and shock-affected zone, the material became more elastic as a result of increased stress.
Laser ablation with femtosecond pulses (130 fs, wavelength 800 nm, repetition rate 2 Hz) was compared with nanosecond-pulse ablation (10 ns, wavelength 266 nm, repetition rate 2.5 Hz) of bariumalumoborosilicate glass in air using the direct focusing technique. Different ablation thresholds and heat-affected zones were observed. The lateral and vertical machining precision was evaluated. Single nanosecond laser pulses in the far UV resulted in a bubble or a circular hole in the centre of the illuminated spot, depending on the applied fluence. The ablation behaviour in the case of near-IR femtosecond pulses contrasted to this. Bubble formation was not detected. It needed repeated pulses at the same spot to modify the surface until material removal could be observed (incubation). Cavity dimensions of less than the beam diameter were achieved in this case.