Micro damage structures of fiber reinforced polymers (FRP) can be characterized nondestructively by X-ray refraction topography, which images inner surfaces. The damage accumulation after fatigue treatment of short glass fiber reinforced polybutylene terephthalate (PBT-GF) is correlated to the applied load and the number of cycles. Micro cracks and fiber/matrix debonding during fatigue can be detected separately due to their different direction of X-ray small angle scattering. The residual strength over the crack surface decreases by a linear decay as 30 %, 60 % and 90 % of the materials lifetime is passed.