Filtern
Dokumenttyp
- Vortrag (35)
- Posterpräsentation (16)
- Beitrag zu einem Tagungsband (13)
- Zeitschriftenartikel (10)
- Dissertation (1)
- Forschungsbericht (1)
Schlagworte
- KorroPad (35)
- Korrosion (32)
- Nichtrostender Stahl (31)
- EPR (22)
- Corrosion resistance (20)
- Wärmebehandlung (20)
- Heat treatment (19)
- Korrosionsbeständigkeit (16)
- Lochkorrosion (16)
- Stainless steel (14)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (35)
The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials).
Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Electrochemical tests, hardness measurements, and microstructure analysis are performed to study the influence of austenitizing, quenching, and tempering parameters on the corrosion resistance of the martensitic stainless steel grade X50CrMoV15 (1.4116). Different heat treatment states were studied using an adapted EPR-Test to evaluate the chromium distribution and depletion caused by the formation and dissolution of chromium rich carbides. The EPR results were correlated with pitting corrosion behavior, demonstrating the strong effect of heat treatment parameters on the susceptibility of martensitic stainless steels to corrosion phenomena.
Ageing at 600 °C (from 0.1 h up to 20 h) leads to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries of the lean duplex stainless steel (LDSS) X2CrNiN22-2. This leads to sensitisation due to chromium depletion and decreased pitting corrosion resistance proven by the results of various electrochemical methods (DL-EPR and determination of CPT, Epit). These results were compared with the KorroPad method, which uses an agar-based gel-electrolyte for the detection of stainless steel surfaces prone to pitting corrosion. However, the standard configuration of the KorroPad showed no differentiation for the various ageing conditions. Therefore, modified versions of the KorroPad with two, five and ten times higher NaCl and potassium ferrocyanide III (K3[Fe(CN)6]) concentrations were successfully used to visualise the behaviour detected by DL-EPR, Epit and CPT. Therefore, the KorroPad method can also detect a microstructure related reduction of pitting corrosion resistance, which can drastically reduce the experimental effort to generate sensitisation diagrams for stainless steels.
Durch eine breite Beteiligung von Schleifmittelherstellern, -anwendern und wissenschaftlichen Einrichtungen im projektbegleitenden Ausschuss (PA) konnte der vielschichtige Themenkomplex „Schleifen“ im Kontext zu den Projektzielen umfassend untersucht werden. Es wurden praxisrelevante Parameterfelder definiert, die eine erfolgreiche Aufklärung der Projektfragestellung ermöglichten.
Im Zuge der Untersuchungen wurde ein signifikanter Einfluss beim Einsatz von Granulatschleifbändern auf das Korrosionsverhalten geschliffener Oberflächen festgestellt. Damit zeigten geschliffene Oberflächen regelmäßig eine schlechtere Korrosionsbeständigkeit als Oberflächen, die mit sonst gleichen Parametern mit einlagig gestreuten Bändern bearbeitet wurden.
Die durch einige Untersuchungsergebnisse aus vorangegangenen AiF-Vorhaben ursprünglich verfolgte These, dass Unterschiede in der Korrosionsbeständigkeit auf die Kornart der Schleifmittel Korund bzw. SiC zurückzuführen ist, konnte nur bedingt bestätigt werden. Bei den systematischen Untersuchungen innerhalb dieses Projektes erwies sich der Einfluss der Kornart im Vergleich zum Einfluss des Schleifbandtyps (Granulat bzw. einlagig gestreutes Korn) als weniger relevant.
Durch weiterführende Untersuchungen konnten auf Oberflächen, die mit Granulatschleifbändern bearbeitet wurden, große Materialaufplattungen aus Eigenmaterial festgestellt werden. Das Eigenmaterial wird dabei im Schleifprozess zunächst abgetragen und aufgrund der Topografie des Schleifbandes zeitweise auf den Bändern festgehalten. Später lösen sich diese Materialanhäufungen vom Band ab und können prozessbedingt durch Wärme- und Krafteinwirkung auf den bearbeiteten Oberflächen aufgeplattet werden. Durch REM und KorroPad Untersuchungen ließen sich Bereiche mit solchen Eigenmaterialaufplattungen eindeutig als wesentliche Ausgangspunkte für Korrosionsprozesse identifizieren. Das aufgeplattete Material ist stark verformt, thermisch beeinflusst und bildet eine Spaltgeometrie zur Bauteiloberfläche aus. Diese Veränderungen führen zur Störung der Passivschichtausbildung in diesen Bereichen und verursachen damit eine erhöhte Korrosionsanfälligkeit der Oberflächen.
Durch gezielte Nachbearbeitungsprozesse ist es möglich, die Eigenmaterialaufplattungen von den Oberflächen zu entfernen. Im Rahmen des Vorhabens wurde dazu eine Nachbearbeitung mittels Schleifvlies geprüft, die zu einer Entfernung der Eigenmaterialaufplattungen und damit zu einer Wiederherstellung der erwarteten Korrosionsbeständigkeit führte. Wird der Endschliff von Oberflächen mit einlagig gestreutem Korn ausgeführt, sind ebenfalls keine korrosionsrelevanten Materialaufplattungen zu erwarten.
Die in einem vorhergehenden AiF Vorhaben IGF 17136 N/1 entwickelte Methode der KorroPad-Prüfung konnte auch hier erfolgreich für die Untersuchung der Auswirkung unterschiedlicher Prozessparameter auf die Korrosionsbeständigkeit der Oberflächen eingesetzt werden. Zudem erwies sich das EPR-SL-Verfahren als ein weiterer Ansatz, um die Passivschichtstabilität verschieden geschliffener Oberflächen vergleichend untersuchen zu können.
Mit den nun vorliegenden Erkenntnissen können kmU künftig durch Anpassungen und Optimierung von Schleifprozessen eine gute Korrosionsbeständigkeit der bearbeiteten Oberflächen sicherstellen. Die Optimierung der Prozessparameter und -schritte kann durch den Einsatz der KorroPad-Prüfung Inhouse erfolgen und somit die laufende Fertigung im Rahmen der Qualitätsprüfung überwacht und dokumentiert werden.