In the last years, new approaches for the evaluation of the corrosion resistance of martensitic stainless steels were developed, which allow nearly non-destructive as well as short-term corrosion testing. This work analyzes the sensitive influence of microstructure and surface treatment on the corrosion resistance. The effect of alloy composition and microstructure, which is always present in addition to the influence of various surface treatments will be evaluated and discussed. The corrosion behavior was investigated with conventional evaluation of the pitting potential, electrochemical potentiodynamic reactivation (EPR), electrochemical noise (EN), and the 'KorroPad' (KP) technique. EPR provided information about the passivation ability and the extent of chromium content reduction due to chromium carbide precipitation in the microstructure. The use of EN and KP aims to detect the influence of different surface treatment parameters on the corrosion resistance in a nearly non-destructive way. Furthermore the results shall demonstrate the functionality and convenience of the short-term corrosion test methods EN and KP in order to gain more acceptance within the scientific community. The results will allow the extraction of surface treatment effects on the corrosion behavior of the martensitic stainless steels 1.4116, 1.4034, and 1.4021.
Nickel‐free high‐nitrogen‐alloyed stainless steels like the P2000 (X13CrMnMoN18‐14‐3) were developed to enhance the strength and corrosion resistance of austenitic stainless steels like 304 and 316 while keeping the typical high ductility. The mechanical and corrosive properties of P2000 were investigated and compared with 304 and 316 to highlight the application opportunities of this new alloy. The microstructure of the solution‐annealed condition was characterised by electron backscatter diffraction and the mechanical properties were studied by uniaxial tensile tests, Charpy impact tests and hardness measurements. The passivation behaviour was analysed using the electrochemical potentiodynamic reactivation, whereas the pitting corrosion resistance was compared by pitting potentials and pitting temperatures. However, secondary thermal influences or suboptimal heat treatment can impair the corrosion resistance due to the precipitation of secondary phases and the resulting sensitisation. Thermodynamic calculations and artificial ageing treatment in the range of 500–900°C for up to 100 h were used to determine critical time–temperature parameters for sensitisation. The microstructure of the various aged states was evaluated by scanning electron microscopy and compared with the degrading corrosion resistance characterised by the KorroPad method.