In the last years, new approaches for the evaluation of the corrosion resistance of stainless steels were developed which allow short term corrosion testing with increased information content. This work analyses the extensive influence of heat treatment on microstructure and the resulting corrosion resistance of the martensitic stainless steels 1.4034 and 1.4021 with advanced methods. Different heat treatments at various austenitization temperatures up to 1100°C and the effect of different cooling rates were evaluated; the last has not yet been studied in literature at all. The resulting corrosion behaviour in relation to the different carbon content in the two used alloys and the applied heat treatment will be presented and discussed. The applied methods of investigation were conventional evaluation of the critical pitting corrosion potential (PP), modified electrochemical potentiodynamic reactivation (mEPR) and the "KorroPad" (KP) technique. The performance of modified EPR and its interpretation were optimized to provide additional information about the general passivation ability and the extent of chromium depletion as result of applied heat treatment. The aim using PP and KP was the correlation between the Parameters of the mEPR with the changes in the pitting corrosion resistance. Furthermore the results will demonstrate the functionality and usability of the short term corrosion test methods mEPR and KP in order to increase their acceptance within the scientific community. The results indicate a surprisingly large influence of both austenitization temperature and cooling rate on the corrosion resistance within all three used test methods, which can explain the different corrosion behaviour of martensitic stainless steels in earlier investigations.
Martensitic stainless steels are commonly used in cutlery fabrication requiring high hardness and sufficient corrosion resistance. The heat treatment process affects the mechanical and electrochemical behavior of martensitic stainless steels due to the precipitation of chromium carbides. Depending on the heat treatment the corrosion resistance of these steels can vary strongly, and improper heat treatment parameters can lead to a weak pitting corrosion resistance. The aim of this work is to identify heat treatment parameters influencing the corrosion resistance of martensitic stainless steels by using three different electrochemical testing methods. To this purpose, five different heat treatments were applied to the alloys 1.4116 and 1.4034. In addition to the determination of the critical pitting potentials and the modified double-loop electrochemical potentiodynamic reactivation tests (DL-EPR) a new KorroPad indicator test was used assessing the pitting corrosion behavior. The results showed that all methods used were in good agreement for verifying the influence of the various heat treatment parameters on the corrosion behavior and to identify the effect of heat treatment conditions on the pitting corrosion resistance.