Filtern
Dokumenttyp
Sprache
- Englisch (3)
Schlagworte
- Photogrammetry (3) (entfernen)
Organisationseinheit der BAM
Self-compacting concrete typically contains a higher content of powder materials than normal concrete. Furthermore it is assumed that the use of superplasticizers yields a more homogenous microstructure in the hardened paste. Both aspects generate a very dense microstructure, which can be assumed to cause material behaviour that differs from than normal concrete when it is exposed to elevated temperatures. However, the paste volumes in SCC can vary significantly based on the mixture composition. At a low paste volumes SCC can be very similar to normal concrete at hardened state while it can vary greatly at higher paste volumes. Since the high temperature behaviour of concrete is strongly affected by the different physical behaviour of the paste and the aggregates, it is likely that the high temperature behaviour is consequently strongly affected by the ratio of these mixture components. In the present study different SCC mixtures were observed with similar mechanical properties, but with significantly differing paste to aggregate ratios. Based on observations of the heat evolution at the fire exposed surface and at different depths inside the specimens as well as based on photogrammetric observations of the spalled dimensions, the results indicate that with increasing paste volumes the heat conductivity is reduced and as a result concrete with higher paste to aggregate ratios shows less spalling.
Spalling of concrete due to fire exposure can lead to severe damage of building components. It is a much discussed subject in structural engineering and not yet completely understood. Generally, it is assumed that thermohydraulic and thermomechanical processes induce tensile stresses in the concrete. Furthermore, the tensile strength of concrete is reduced due to increasing temperatures. The combination of an increasing tensile stress and a decreasing tensile strength result in the occurrence of explosive spalling. The spalling behaviour of concrete is influenced by many parameters, for instance the water cement ratio, porosity, permeability of concrete as well, the presence of steel reinforcement and polypropylene fibres, also the size and geometry of the fire exposed area. Within the current research project at Bundesanstalt für Materialforschung und prüfung (BAM), the susceptibility to spalling of six different concrete mixtures is analysed to quantify the size effect using small scale, intermediate scale and full scale tests. A special fire test setup was built to test specimens simultaneously to enable a better comparability. All specimens are tested without additional mechanical load and unrestraint to prevent external induced cracking at the fire exposed site. Thermocouples are used to measure in situ the temperature distribution as an indication on the thermal degradation of the concrete during the fire tests. Afterwards the maximum spalling depth and the damaged area of the specimen are illustrated by a photogrammetric measurement system. The contribution to the spalling workshop presents the results of four concrete mixtures tested in intermediate-scale and full-scale fire tests. The comparisons are based on the concrete temperature as well as the obtained photogrammetric data. The results show that the spalling depth and the spalling area are significantly affected by the size of the fire exposed area.
Within a current research project which is funded by the German Research Foundation (DFG) the influence of the size and the geometry of specimens on the spalling result in fire tests is going to be investigated at Bundesanstalt für Materialforschung und -prüfung (BAM). This paper describes some preliminary results and a newly developed test setup. The novel setup enables the efficient and precise quantification of spalling by using a special photogrammetric measurement system.