A set of compound refractive lenses (CRLs), mounted on a silicon wafer, was obtained from the Institut für Mikrostrukturtechnik Karlsruhe. The CRLs were characterized at the BAMline at the synchrotron BESSYII in Berlin. It could be demonstrated that beam diameters below 1 µm can be obtained. The beam size accepted by the lenses is (140 × 140) µm2, thus the intensity gain in the micrometer spot, including absorption, is about 15,000. It is possible to switch between different beam energies within a few minutes. First results of scans and the application of the lenses for MicroXANES (X-ray absorption near-edge structure) measurements are presented in this paper. Also, the possibility of MicroEXAFS (extended X-ray absorption fine structure) measurements is discussed.
The content of chromium in different oxidation states in chromium-treated wood was studied with XANES (X-ray absorption near-edge structure) measurements at the Cr K absorption edge. It could be shown that wood samples treated with Cr(VI) (pine and beech) did still contain a measurable content of Cr(VI) after four weeks conditioning. If such wood samples were heat exposed for 2 h with 135 °C prior conditioning, Cr(VI) was no longer detected by XANES, indicating a complete reduction to chromium (III).
The adsorption behavior of Platinum nanoparticles was studied for the as-received catalyst (under inert gas), under hydrogen and CO atmosphere using our newly designed in-situ cell. X-ray Absorption Spectroscopy (XAS) and Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) experiments were performed simultaneously with high data quality. Structural information and the type of adsorbate could be revealed via Extended X-ray Absorption Fine Structure (EXAFS) analysis, Δμ X-ray Absorption Near Edge Structure analysis (Δμ XANES) and in-situ DRIFTS. The as-received catalyst showed sub-surface oxygen and O(n-fold). Under CO atmosphere only CO(atop) was found. Reversible adsorbate induced changes of the Pt nanoparticle structure were derived from changes in the Pt-Pt coordination number and the corresponding bond distance. Under reducing conditions (H2, CO) a significant increase in both values occurred. Temperature dependent desorption of CO revealed a gradual shift from Pt-CO to Pt-O. Reoxidation was clearly assigned to strong metal support interaction from the SiO2 support.
Rigid rod-type metallo-supramolecular coordination polyelectrolytes with Fe(II) centres (Fe-MEPEs) are produced via the self-assembly of the ditopic ligand 1,4-bis(2,2':6',2''-terpyridine-4'-yl)benzene (tpy-ph-tpy) and Fe(II) acetate. Fe-MEPEs exhibit remarkable electrochromic properties; they change colour from blue to transparent when an electric potential is applied. This electrochemical process is generally reversible. The blue colour in the ground state is a result of a metal-to-ligand charge transfer at the Fe(II) centre ion in a quasi-octahedral geometry. When annealed at temperatures above 100 °C, the blue colour turns into green and the formerly reversible electrochromic properties are lost, even after cooling down to room temperature. The thermally induced changes in the Fe(II) coordination sphere are investigated in situ during annealing of a solid Fe-MEPE using X-ray absorption fine structure (XAFS) spectroscopy. The study reveals that the thermally induced transition is not accompanied by a redox process at the Fe(II) centre. From the detailed analysis of the XAFS spectra, the changes are attributed to structural changes in the coordination sphere of the Fe(II) site. In the low temperature state, the Fe(II) ion rests in a quasi-octahedral coordination environment surrounded by six nitrogen atoms of the pyridine rings. The axial Fe–N bond length is 1.94 Å, while the equatorial bond length amounts to 1.98 Å. In the high temperature state, the FeN6-site exhibits a distortion with the axial Fe–N bonds being shortened to 1.88 Å and the equatorial Fe–N bonds being elongated to 2.01 Å.
Agglomerated superparamagnetic iron
oxide nanoparticles can easily and in large scale be
precipitated from iron salt solutions. Although the
process is well known, it is ambiguously either assumed
that magnetite or maghemite is obtained. The first part
of our study clarifies this question using X-ray absorption
spectroscopy. For further processing of the nanoparticles,
i.e., for giving them a surface functionality or
incorporating them into composites, it is important to
break the agglomerates and individualize the particles
at first. This can effectively be done with nitric acid
treatment. The influence of this process on the particles
chemistry and structure was analyzed in great detail
using X-ray diffraction, X-ray absorption, and smallangle
X-ray scattering. In contrast to our expectation,
no oxidation from magnetite (Fe3O4) to maghemite (γ-
Fe2O3) was found; the formal valence of the particles in
any case is magnetite (Fe3O4). Instead, an increase in
the particles' surface disorder was discovered from
X-ray absorption analyses and high-resolution transmission
electron microscopy. The acid treatment
roughens and distorts the surface of the nanoparticles
which is connected with an increased spin disorder.
Although metallic nanoparticles play an important role in the area of nanotechnology, a coherent mechanistic explanation for the evolution of the particles during their chemical synthesis has not yet been provided in many cases. To gain a profound understanding of the growth mechanism of colloidal nanoparticles, new approaches using Small Angle X-Ray Scattering (SAXS) combined with X-ray absorption near-edge structure (XANES) are presented. This combination allows for insights into two prominent syntheses routes of gold nanoparticles (GNP): The 'slow' reaction using sodium citrate (30-90 min) as a reducing agent and the 'fast' reaction employing NaBH4 (within few seconds). In the first case data derived with the coupled XANES and SAXS suggests a four-step particle formation mechanism. For the second system a time resolution in the order of 100-200 ms was achieved by coupling a common laboratory SAXS instrument with a microstructured mixer, which allows data acquisition in a continuous-flow mode. The results indicate a coalescence driven growth process. Based on the capabilities to deduce the size, number and polydispersity of the particles, the results of both methods enable the development of mechanistic schemes explaining the different phases of particle formation and growth, thus providing a basis for improved control over the synthesis processes.
The adsorption behavior of Platinum nanoparticles was studied for the as-received catalyst (under inert gas), under hydrogen and CO atmosphere using our newly designed in-situ cell. X-ray Absorption Spectroscopy (XAS) and Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) experiments were performed simultaneously with high data quality. Structural information and the type of adsorbate could be revealed via Extended X-ray Absorption Fine Structure (EXAFS) analysis, Dl X-ray Absorption Near Edge Structure analysis (Dl XANES) and in-situ DRIFTS. The as-received catalyst showed sub-surface oxygen and O(n-fold). Under CO atmosphere only CO(atop) was found. Reversible adsorbate induced changes of the Pt nanoparticle structure were derived from changes in the PtAPt coordination number and the corresponding bond distance. Under reducing conditions (H2, CO) a significant increase in both values occurred. Temperature dependent desorption of CO revealed a gradual shift from PtACO to PtAO. Reoxidation was clearly assigned to strong metal support interaction from the SiO2 support.