Maintenance, repair and overhaul of components are of increasing interest for parts of high complexity and expensive manufacturing costs. In this paper a production process for laser metal deposition is presented, and used to repair a gas turbine burner of Inconel 718. Different parameters for defined track geometries were determined to attain a near net shape deposition with consistent build-up rate for changing wall thicknesses over the manufacturing process. Spot diameter, powder feed rate, welding velocity and laser power were changed as main parameters for a different track size. An optimal overlap rate for a constant layer height was used to calculate the best track size for a fitting layer width similar to the part dimension. Deviations in width and height over the whole build-up process were detected and customized build-up strategies for the 3D sequences were designed. The results show the possibility of a near net shape repair by using different track geometries with laser metal deposition.
High-power laser beam welding became new stimuli within the last 10 years due to the availability of a new generation of high brightness multi kilowatt solid state lasers. In the welding research new approaches have been developed to establish reliable and praxis oriented welding processes meeting the demands of modern industrial applications during this time. The paper focuses on some of the current scientific and technological aspects in this research field like hybrid laser arc welding, simulation techniques, utilization of electromagnetic fields or reduced pressure environment for laser beam welding processes, which contributed to the further development of this technology or will play a crucial role in its further industrial implementation.
The complex microstructure and the advanced mechanical properties of AHSS steel types lead to an increased susceptibility to weld cracking, especially during resistance spot welding under ‘rough’ manufacturing conditions.
Various activities have been conducted in recent years at the Federal Institute for Materials Research and Testing (BAM) and the Fraunhofer IPK on this matter. Understandings about the safe spot weldability and the process of crack-forming itself were gained, and solutions for handling this issue given.
The performed work includes investigations on the influence of initial gaps as well as restraint intensity. An experimental method for the determination of the general cracking susceptibility, i.e. a material ranking of AHSS in respective to current restraints was developed. Coupled mechanical and thermal simulations of the welding process show the present internal stress-strain-conditions and values responsible for the formation of cracks, deepening the understanding of the process.
By using this easy to perform and material-independent method for the determination of the cracking susceptibility in resistance spot welded joints, small and medium sized companies can profit by rapidly evaluating the joinability of their handled material combinations as well as OEMs.
Die in dieser Studie vorgestellte einfache Probengeometrie zeigt sich in Verbindung mit der
angewandten Versuchs- und Auswertemethodik geeignet, um den umwandlungsplastischen (TRIP)-Parameter K unter Verwendung des thermomechanischen Simulators Gleeble® 3500 experimentell zu bestimmen.
Der TRIP-Parameter K wurde für die Grundwerkstoffe S355J2+N und S960QL, sowie für den hochlegierten Zusatzwerkstoff CN13-4 -IG bestimmt.
Die numerische Einflussanalyse zeigt, dass bei der Berechnung von (Oberflächen-)Schweißeigen-spannungen die Vernachlässigung des TRIP-Effektes kaum einen Einfluss auf die Längseigenspannungen hat. Im Gegensatz da zu resultieren gegenüber dem Referenzfall signifikante Abweichungen der
Quereigenspannungen im und um den Schweißnahtbereich.
Die Verdopplung des TRIP-Parameters K gegenüber dem Referenzfall hat nur einen vernachlässigbaren Einfluss auf die Längs- sowie Quereigenspannungen auf der Oberfläche.
Für eine qualitative und quantitative numerische Nachbildung der experimentell bestimmten Längs- und Quereigenspannungen ist die Berücksichtigung der Größenordnung des material-abhängigen TRIP-Parameters K notwendig.
In dieser Studie wurde die Heißrissanfälligkeit beim Laserstrahlschweißen für die Werkstoffe 1.4376, 1.4301 und 1.4828 mit Hilfe des CTW Test quantifiziert. Bei den Versuchen konnten Erstarrungsrisse in den Proben generiert werden. Zusätzlich können mit der Bildkorrelations-Technik die lokalen Dehnungen und Dehnungsraten während des Heißrisstests gemessen wer den. In Verbindung mit einem externen Diodenlaser zum Beleuchten der zu messende Oberfläche und lnterferenzfiltern an den Kameras konnten die DIC Messungen ohne optische Störungen durchgeführt werden.
Die Ergebnisse zeigen, dass die Heißrissbildung bei einer externen Belastung von 3 % für die Stahlsorte 1.4376 zu erwarten ist. Für die Stahls orte 1.4301 beträgt dieser Grenzwert 2 % und 1,5 % für die Stahlgüte 1.4828. Außerdem ist zu beobachten, dass die Gesamtrisslänge mit zu nehmender äußerer Zugbeanspruchung steigt
Metal additive manufacturing is often based on laser beam processes like Laser Metal Fusion (LMF) or Laser Metal Deposition (LMD). The LMF process is in particular suitable for very complex geometries. However build rate, part volume and material flexibility are limited in LMF. In contrast, LMD achieves higher deposition rates, less restricted part sizes and the possibility to change the material composition during the build-up process. On the other hand, due to the lower spatial precision of the material deposition process, the complexity of geometries is limited. Therefore, combined manufacturing with both LMF and LMD has the potential to utilize the respective advantages of both technologies.
In this paper, combined additive manufacturing with LMF and LMD is described for Ti-6Al-4V and Inconel 718. First, lattice structures with different wall thickness and void sizes are built with LMF. The influence of LMD material deposition on these LMF-structures is examined regarding metallurgical impact and distortion. Cross-sections, x-ray computer tomography and 3D-scanning results are shown.
For the titanium alloy specimen, oxygen and Nitrogen content in the deposited material are analysed to evaluate the LMD shielding gas atmosphere. The results are used to develop guidelines for a LMD build-up strategy on LMF substrates. With these findings, a gas turbine burner is manufactured as reality test for the combined approach.
Der Einsatz von Hochleistungswerkstoffen verlangt nach einer hohen Endformnähe der zu fertigenden Bauteile, um den Aufwand und somit die Kosten für Materialeinsatz und Nachbearbeitung möglichst gering zu halten. Der additive Einsatz in Form des Laser-Pulver-Auftragschweißens bietet hierfür durch den gezielten Materialauftrag ein hohes Potential. Herausforderungen bestehen in Bereichen der Vorhersagbarkeit und der Reproduzierbarkeit des Materialauftrages, sowie der Fertigungszeit. Unterschiedliche Einflüsse bei der Schichterzeugung führen dabei zu Abweichungen von der Soll-Geometrie. Die vorliegenden Untersuchungen behandeln den Einfluss von Spurgeometrie, Spurüberlappung, Verfahrweg und Aufbaureihenfolge auf die entstehende Bauteilform. Die Teilung einer Lage in Rand- und Kernbereich ermöglicht einen konturangepassten Verfahrweg und eine Erhöhung der Endformnähe innerhalb einer Ebene. Die Verwendung unterschiedlicher Spurgrößen bei der Bauteilerzeugung verdeutlicht die Möglichkeiten einer hohen Auftragsrate bei gleichzeitig hoher Formgenauigkeit. Bereits kleine Unterschiede beim Materialauftrag zwischen Kern- und Randbereichen, Start- und Endpunkten sowie in Bereichen des Richtungswechsels führen aufgrund von Fehlerfortpflanzung nachmehreren Lagen zu Abweichungen in der Aufbaurichtung. Kompensierungen mittels angepasster Baustrategien werden aufgezeigt und diskutiert. Die Nickelbasislegierung Inconel 718, die Titanlegierung Ti-6Al-4V sowie der austenitische Stahl 316L sind Bestandteil der vorliegenden Untersuchungen. Die gewonnenen Erkenntnisse verdeutlichen das Potenzial einer angepassten Aufbaustrategie zur reproduzierbaren Erzeugung von Bauteilen am Beispiel unterschiedlicher Körpergeometrien.
Numerical Sensitivity Analysis of TRIP-Parameter K on Weld Residual Stresses and Weld Distortion
(2016)
A combined experimental numerical approach is applied for a sensitivity analysis of the transformation induced plasticity (TRIP)-parameter K on welding residual stresses and welding distortion for the welding of the low-alloyed high-strength S960QOL with the high-alloyed hig-strength filler material CN13-4-IG. A thermo-mechanical FE model of a real GMA welding process was experimentally validated against termperature field, X-Ray stress measurments and optical distortion measurement. Within the sensititvity analysis K was varied and the influence on the calculated welding residual stresses and welding distortion is evaluated by performing corresponding FEA. The correct order of K magnitude is necessary in order to reproduce the residual stresses qualitatively and quantitatively. For the sufficient reproducing of the welding distortion the transformation induced plasticity can be neglected.
Selecting a welding process for a given application is crucial with respect to the sustainability of part manufacturing. Unfortunately, since welding processes are evaluated by a number of criteria, preferences for one or the other process can be contradictory. However, the prevalent procedure of weight assignment for each criterion is subjective and does not provide information about the entire solution space. From the perspective of a decision maker it is important to be able to assess the entire set of possible weightings and answer the question which welding process is optimal for which set of weights. This issue is investigated by means of a weight space partitioning approach. Two welding processes are considered with respect to three criteria that reflect their economic and environmental performance. In order to find the most sustainable welding process the underlying weight space partition is evaluated.
Increasing performance and energy efficiency of Gas Metal Arc Welding by a high power tandem process
(2016)
Standard Gas Metal Arc Welding (Standard GMAW) and a high power Tandem GMAW (TGMAW) process are evaluated with respect to energy efficiency. Current, voltage and overall equipment power are measured and energy consumption is determined. The new key performance indicator Electrical Deposition Efficiency is introduced to reflect the energy efficiency of GMAW processes. Additionally, wallplug efficiency of the equipment is determined in order to identify the overall energy consumption. Results show that energy efficiency as well as economic process performance can be significantly increased by application of the TGMAW process. Furthermore findings indicate that wall-plug efficiency of the equipment is independent of power level and material transfer mode. A metal plate of 30 mm thick structural steel is joined by Standard GMAW and TGMAW to demonstrate the total energy savings for a real weld. Electricity consumption is reduced by more than 20 % using the high power TGMAW process.