Filtern
Erscheinungsjahr
- 2015 (36) (entfernen)
Dokumenttyp
Sprache
- Englisch (28)
- Deutsch (7)
- Mehrsprachig (1)
Schlagworte
- Laser beam welding (7)
- Solidification cracking (5)
- Hot cracking test (4)
- High power laser beam welding (3)
- Hot cracking (3)
- Keyhole (3)
- Local reduced pressure (3)
- Mobile vacuum (3)
- Duplex stainless steel (2)
- Electromagnetic weld pool support (2)
Eingeladener Vortrag
- nein (4)
Laser remote welding is a dynamic and flexible joining technology which enables various new approaches in welding sequence and weld position planning. However, the challenge is to find the optimal set-up within this large parameter space. In this article, numerical welding simulation is used to deal with this challenge. For a car door, different welding sequences and weld positions were numerically analyzed and compared with respect to its welding distortion behavior.
The safety of components or constructions is of great importance in the manufacturing and processing of metallic materials. Solidification cracking as well as the weldability of materials remain still for many years a highly contentious issues, particularly with regard to the causes of the hot crack formation. Many of studies have been conducted to determine the critical condition of occurrence of the solidification cracking. In this study different digital image correlation measuring techniques in conjunction with laser diodes as the illuminating source have been employed to measure the arising strain field during the laser welding process at the surface of the workpiece directed to the laser beam in the close vicinity of the weld pool. The Controlled Tensile Weldability test (CTW) was used to apply an external tensile load during the laser beam welding in order to generate the solidification cracks. The results showed that by means of those techniques it is possible to measure the strain field without any disturbances from the intense welding light or the smoke. Additionally, the strain and the strain rate as a critical factor determining solidification crack formation can be measured and analyzed.
Widerstandspunktschweißen ist insbesondere im Automobilbau eine der wichtigsten Fügetechniken. Bislang erfolgt die Qualitätssicherung überwiegend durch stichprobenartige zerstörende Prüfung. Eine zerstörungsfreie Prüftechnik würde neben der Reduzierung der Prüfkosten auch eine Optimierung des Punktschweißverfahrens bedeuten, da prinzipiell jeder Schweißpunkt geprüft werden könnte und somit auch eine Reduzierung der Anzahl der Schweißpunkte möglich ist.
Es wird ein Verfahren vorgestellt, bei dem die Punktschweißverbindung zwischen zwei Stahlblechen optisch auf einer Blechseite mittels Laser oder Blitzlicht erwärmt wird. Die aufgeschmolzene Zone, die sogenannte Schweißlinse, stellt dabei neben der mechanischen Verbindung auch eine Wärmebrücke zwischen den beiden verschweißten Blechen dar, die bei diesem Verfahren ausgenutzt wird. Durch den verbesserten thermischen Kontakt zwischen den verschweißten Blechen an der Schweißlinse kontrastiert diese deutlich mit dem umgebenden Blechmaterial, bei dem der Wärmeübertrag zwischen den Blechen vergleichsweise gering ist. Dieser Kontrast im thermischen Verhalten kann mittels zeitabhängiger Thermografie gemessen werden.
Durch das hier vorgestellte Verfahren kann mittels aktiver Thermografie sowohl in Transmissions- als auch in Reflexionsanordnung die Größe des thermischen Kontaktes zwischen den beiden Blechen ermittelt werden, welche ein Maß für die Größe der Schweißlinse und damit für die qualitative Güte der Schweißung darstellt. Ein Vorteil des entwickelten Verfahrens ist seine Anwendbarkeit auf Bleche ohne Oberflächenbehandlung.
Grain refinement is an important opportunity to improve mechanical properties of fusion welds and the weldability (susceptibility to solidification cracking) of the base metal. In this study, grain refinement was achieved in aluminium welds through additions of grain refiner to the weld metal. Increasing grain refiner additions led to a decrease of the weld metal mean grain size (down to −86 %). The grain refinement efficiency was the highest in commercial pure Al (Alloy 1050A, Al 99.5), followed by Alloy 6082 (Al Si1MgMn) and Alloy 5083 (Al Mg4.5Mn0.7). To investigate this clear influence of alloy content on grain size, the undercooling parameters P and Q were calculated. Temperature measurements revealed that solidification parameters such as solidification growth rate or cooling rate vary significantly along the solidification front, dependent upon torch speed and alloy. On the basis of this comparison, an analytical approach was used to model the columnar to equiaxed transition (CET). Moreover, wavelength dispersive X-ray spectroscopy (WDS) and transmission electron microscopy (TEM) analyses revealed particles rich in Ti and B that are probably TiB2 particles coated by Al3Ti nucleating Al grains during solidification. Also, Ti/B contents needed in commercial filler wires to allow optimum weld metal grain refinement were calculated dependent upon base alloy and welding process.
This work addresses the fatigue strength of friction-welded joints for the drive pinion in heavy-duty trucks. Three different friction welding (FW) variants were tested for the joint between the pinion and the bevel of the shaft: (1) conventional FW using series materials, (2) conventional FW from dissimilar materials for every part, and (3) dissimilar joints by applying joint-site structure of FW. Each joint variant was compared to the series production part using a 4-point bending test. Results showed that the higher strength material slightly improved the fatigue strength of the conventional friction-welded joints. Despite the light weight of the component joined structurally at the site, the joint revealed a lower endurance limit compared to other variants. However, there has been little discussion on the weld zone position. The applied equivalent stresses on the weld zone of the joint-site structure are less similar to the position for the conventional FW. Characterization of the failure explains the extraordinary behaviors in relation to S-N curves.
This paper presents an approach to reconstruct the three-dimensional transient temperature field for fusion welding processes as input data for computational weld mechanics. The methodology to solve this inverse heat conduction problem fast and automatically focuses on analytical temperature field models for volumetric heat sources and application of global optimisation. The important issue addressed here is the question which experimental data is needed to guarantee a unique reconstruction of the experimental temperature field. Different computational-experimental test cases are executed to determine the influence of various sets of discrete experimental data on the solvability of the optimisation problem. The application of energy distributions utilised for laser beam welding allows reconstructing the temperature field efficiently. Furthermore, the heat input into the workpiece determined by the simulation contributes to the evaluation of the thermal efficiency of the welding process.
This paper deals with the use of an adaptive control system for compensating the variation in the gap height of a fillet welded lap joint. Gap bridging requires the input of additional filler material and is related to an increased energy input. Hence, the aim was a compensation of the effect of an increased heat input, in order to maintain the weld pool and excessive penetration, which can prevent consequently root reinforcement and burn-through. The findings achieved in this work show possibilities for a real-time controlled adjustments of the welding parameters in automated metal active gas (MAG) welding for compensating a higher heat input, in particular by means of the torch offset relative to the top sheet at the fillet weld on a lap joint.
Solidification cracking phenomena taking place under Controlled Tensile Weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a three dimensional finite element model employing the contact elements technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure the resulting strain and displacement directed to the laser beam in the Close vicinity of the weld pool was measured at the surface of the workpiece using a Digital Image Correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good Agreement with those observed in experiments.
Understanding the influence of tool/pin shapes on the thermal and material flow behaviors in friction stir welding is of great significance for the optimal design of tool/pin based on a scientific principle. In this study, a numerical method based on computational fluid dynamics is employed to quantitatively analyze the thermo-physical phenomena in friction stir welding with two tools of different pin shapes (axisymmetrical conical tool and asymmetrical triflat tool). Through combining a steady state model with a transient state model, both the computation efficiency and accuracy are ensured. The boundary conditions of heat transfer and material flow are determined with considering a partial sticking/sliding contact condition at the toolworkpiece interface. The total heat generation, heat density and temperature distribution during the welding process with triflat tool are elucidated and compared with that of conical tool, and the material flow patterns and deformation regions of various pin orientations are illustrated in detail. It is found that the deformation zone caused by triflat tool is larger than that by conical tool, which is validated by the weld macrographs. The computed thermal cycles and peak temperature values at some locations are in good agreement with the experimentally measured ones.
Partial penetration welding with a fiber laser at a 9-kW laser power was carried out on 20-mm-thick plates at different positions and analyzed by both experimental and numerical methods. Experiments were carried out for four different angular positions at 1.5 m/min welding speed. All four cases showed a tail-like structure of molten pool on the top surface. The in-depth mechanisms of the energy input characteristics in fiber laser position welding for eight different positions were studied by numerical simulation using the volume-of-fluid (VOF) method. Experimental and numerical results were compared for four cases and showed fair agreement. Observation of flow pattern and bead shape revealed that gravity had little influence on bead shape and flow structure, but changed the pore structure considerably. Flow structure showed a periodic behavior which probably nullified the effect of gravity in position welding. Most of the laser rays reached the bottom of the keyhole without interruption and then multiple reflections started within the keyhole. The first five reflections inside the keyhole delivered around 70 % of the total energy.
The presented apparatus enables laser beam welding of thick materials under local reduced pressure conditions, thus improving the quality of welds and reducing the laser beam power necessary for complete penetration welding. The vacuum cap presented in this article uses a local reduced ambient pressure environment in a tight zone around the welding area and, in contrast to a conventional vacuum chamber, it is movable in the welding direction. The mobile installation is very compact and reaches pressure values of around 200 mbar. The reduced pressure in the vacuum cap is sufficient to generate 50 % higher penetration depth in comparison to welding under ambient pressure conditions. The low pressure around the keyhole reduces the vapour-plasma plume and therefore prevents a defocusing and scattering of the laser radiation. This allows to raise the amount of laser beam power entering the keyhole as well as the effective power density.
The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the camera size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Coupons from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth.
Maintenance, Repair and Overhaul (MRO) is acquiring increasing commercial and socio-economic significance. For products and goods with high investment costs and a long lifespan, especially in the sectors of energy and transportation, a considerable portion of commercial profits are generated by after-sales services. In the field of research and development, not enough attention has been paid so far to tasks and approaches involving MRO. The field thus has a limited scientific background, despite a high potential in the business sector for technological and scientific optimization. The challenges and chances of MRO for sustainable enterprises will be explained with reference to the Fraunhofer Innovation Cluster Maintenance, Repair and Overhaul in Energy and Transport. The developments and project results of the four fields of innovation »Cleaning«, »Repair and Overhaul«, »Condition Monitoring and Diagnosis«, as well as »MRO Planning and Digital Assistance« will be explained.
Welding is one of the most critical operations for the construction of reliable metal structures in everything from ships to reactor vessels. When welds fail, the entire structure often fails—so expectations on weld quality have never been higher. Any process that uses a localized heat source, such as welding, is likely to result in some distortion. The welding process of very thick metal components is not inherently stable and is barely controllable without external forces.
Life Cycle Assessment (LCA) is applied in evaluating environmental impacts of state-of-the-art welding technologies. Manual Metal Arc Welding (MMAW), Laser Arc-Hybrid Welding (LAHW) and two Gas Metal Arc Welding (GMAW) variants are used to join a plate of 20 mm thick structural steel. The LCA results indicate that for 1 m weld seam, MMAW causes the highest environmental impacts in global warming potential (GWP), eutrophication potential (EP), acidification potential (AP), and photochemical ozone creation potential (POCP) among the selected processes, and the LAHW variant performances the least. Filler material and electricity consumptions generally dominate the impacts and reach shares of up to 80% and 61% in the respective impact categories. However, electrode coating consumption in MMAW remarkably contributes impacts on AP and EP, for instance 52% of AP and 76% of EP. Strategies for improvement of the applied welding technologies are discussed.
Das Laser-MSG-Hybridschweißverfahren führt bei untersuchten hochfesten Pipelinestählen API X80 und X120 reproduzierbar zu Schweißverbindungen mit anforderungsgerechten Zähigkeitseigenschaften.
Eine metallurgische Beeinflussung der Schweißnahtzähigkeit ist durch eine gezielte Auswahl des Zusatzwerkstoffes möglich, wobei die maximale Eindringtiefe des Zusatzwerkstoffes in die Tiefe der Laserhybridnaht zu beachten ist.
Die maximal erzielbare Eindringtiefe des Zusatzwerkstoffes ist auf ca. 14 mm begrenzt. Die eingesetzte Art des MSG-Lichtbogens hatte keinen erkennbaren Einfluss auf die Aufmischung im Laseranteil der Laserhybridnaht.
Die besseren Ergebnisse der Kerbschlagzähigkeit konnten mit Metallpulverdrähten erreicht werden.
Mit den erzielten gemittelten Werten der Schlagarbeit: ca. 200 J bei -60°C für X80 und ca. 53 J bei -40°C für X120 werden Anforderungen der Norm API 5L und DIN EN 10208-2 für die beiden untersuchten Grundwerkstoffe erfüllt.
Das Laser-Pulver-Auftragschweißen als additives Fertigungsverfahren ermöglicht einen endformnahen Aufbau von Bauteilen. Ein Zielkonflikt besteht zwischen der Forderung nach hoher Aufbaurate und hoher Endformnähe, welcher von der Schweißraupengröße wesentlich beeinflusst wird. In dieser Veröffentlichung wird das Laser-Pulver-Auftragschweißen eingesetzt, um komplexe Formen additiv aufzubauen. Am Beispiel eines Tannenbaumprofiles werden unterschiedliche Einflussfaktoren dargestellt. Dazu gehören die Raupengeometrie, die Überlappung einzelner Raupen, die Verwendung unterschiedlicher Aufbaustrategien und die Teilung des Gesamtkörpers in Teilkörper. Der Zielkonflikt wird durch die Herstellung von Probekörpern mit unterschiedlichen Steigungswinkeln an den Seitenflächen verdeutlicht. Die Ergebnisse zeigen eine verbesserte Endformnähe in Bereichen flacher Steigung beim Einsatz kleiner Schweißraupen. Im Vergleich dazu erlauben die Schweißparameter der großen Raupen eine 5-fach höhere Aufbaurate. Bei einer Raupenüberlappung kleiner und großer Raupengeometrien innerhalb einer Lage treten Anbindungsfehler auf. Strategien zur Behebung dieses Fehlers durch Anpassung der Schweißreihenfolge werden in dieser Veröffentlichung aufgezeigt. Diese Erfahrungen werden genutzt, um einen Gesamtkörper aus Teilkörpern unterschiedlicher Raupengeometrien zu fertigen.
Laser-GMA-hybrid welding of longitudinally welded large-diameter pipes of grades API- X80/ X120
(2015)
Potentials of the hybrid laser arc welding processes were investigated regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120
Hybrid laser arc welding of the root pass:
Significant reduction in the weld cross section – savings of filler material
Lower heat input into the base material - improvement of mechanical properties of the weld joint
The arc type does not have any influence on the character of dilution in the laser part of the hybrid weld
14 mm deep root face was considered as optimum. No penetration of the filler material could be detected beyond this depth limit
Metal powder filler wires, micro alloyed with Ni and partly with Cr and Mo, guaranteed sufficient Charpy impact toughness at low temperature for the both investigated materials:
Hybrid laser arc welding is a very efficient process for the root pass in multi-pass welding and opens a large technical and economic potential for the manufacture of large pipes